Cherednichenko, S., Ronnung, F., Gol'tsman, G., Gershenzon, E., & Winkler, D. (1999). YBa2Cu3O7-δ hot-electron bolometer with submicron dimensions. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 181–189).
Abstract: Photoresponse of YBa2Cu3O7-δ hot-electron bolometers to modulated near-infrared radiation was studied at a modulation .frequenc y var y ing from 0.2 MHz to 2 GHz. Bolometers were _fabricated from a 50 12 M thick film and had in-plane areas of 10x10 , um 2 . 2x0.2 s um', 1x0.2 p.m', and 0.5x0.2 jim. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
|
Schubert, J., Semenov, A., Gol'tsman, G., Hübers, H. - W., Schwaab, G., Voronov, B., et al. (1999). Noise temperature and sensitivity of a NbN hot-electron mixer at frequencies from 0.7 THz to 5.2 THz. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 190–199).
Abstract: We report on noise temperature measurements of a NbN phonon-cooled hot-electron bolometric mixer at different bias regimes. The device was a 3 nm thick bridge with in-plane dimensions of 1.7 x 0.2 gm 2 integrated in a complementary logarithmic spiral antenna. Measurements were performed at frequencies ranging from 0.7 THz up to 5.2 THz. The measured DSB noise temperatures are 1500 K (0.7 THz), 2200 K (1.4 THz), 2600 K (1.6 THz), 2900 K (2.5 THz), 4000 K (3.1 THz) 5600 K (4.3 THz) and 8800 K (5.2 THz). Two bias regimes are possible in order to achieve low noise temperatures. But only one of them yields sensitivity fluctuations close to the theoretical limit.
|
|
|
|
Gerecht, E., Musante, C. F., Jian, H., Zhuang, Y., Yngvesson, K. S., Dickinson, J., et al. (1999). Improved characteristics of NbN HEB mixers integrated with log-periodic antennas. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 200–207).
|
|
|
|
Yagoubov, P., Kroug, M., Merkel, H., Kollberg, E., Hübers, H. - W., Schubert, J., et al. (1999). NbN hot electron bolometric mixers at frequencies between 0.7 and 3.1 THz. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 238–246).
Abstract: The performance of NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixers is investigated in the 0.7-3.1 THz frequency range. The devices are made from a 3.5-4 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The length of the bolometer microbridge is 0.1- 0.2 gm, the width is 1-2 gm. The best results of the DSB receiver noise temperature measured at 1.5 GHz intermediate frequency are: 800 K at 0.7 THz, 1100 K at 1.6 THz, 2000 K at 2.5 THz and 4200 K at 3.1 THz. The measurements were performed with a far infrared laser as the local oscillator (LO) source. The estimated LO power required is less than 500 nW at the receiver input. First results on the spiral antenna polarization measurements are reported.
|
|
|
|
Il'in, K. S., Gol'tsman, G. N., Voronov, B. M., & Sobolewski, R. (1999). Characterization of the electron energy relaxation process in NbN hot-electron devices. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 390–397).
Abstract: We report on transient measurements of electron energy relaxation in NbN films with 300-fs time resolution. Using an electro-optic sampling technique, we have studied the photoresponse of 3.5-nm-thick NbN films deposited on sapphire substrates and exposed to 100-fs-wide optical pulses. Our experimental data analysis was based on the two-temperature model and has shown that in our films at the superconducting transition 10.5 K the inelastic electron-phonon scattering time was about (111}+-__.2) ps. This response time indicated that the maximum intermediate-frequency band of a NbN hot-electron phonon-cooled mixer should reach (16+41-3) GHz if one eliminates the bolometric phonon-heating effect. We have suggested several ways to increase the effectiveness of phonon cooling to achieve the above intrinsic value of the NbN mixer bandwidth.
|
|
|
|
Schubert, J., Semenov, A., Hübers, H. - W., Gol'tsman, G., Schwaab, G., Voronov, B., et al. (1999). Broad-band terahertz NbN hot-electron bolometric mixer. In Inst. Phys. Conf. (Vol. 167, pp. 663–666).
|
|
|
|
Yagoubov, P., Kroug, M., Merkel, H., Kollberg, E., Schubert, J., Hubers, H. - W., et al. (1998). Performance of NbN phonon-cooled hot-electron bolometric mixer at Terahertz frequencies. In Proc. 6-th Int. Conf. Terahertz Electron. (pp. 149–152).
Abstract: The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The results of the DSB noire temperature are: 1300 K at 650 GHz, 4700 K at 2.5 TBz and 10000 K at 3.12 THz. The RF bandwidth of the receiver is at least 2.5 THz. The amount of LO power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain is measured to be -9 dB, the total conversion gain -14 dB.
|
|
|
|
Svechnikov, S., Verevkin, A., Voronov, B., Menschikov, E., Gershenzon, E., & Gol'tsman, G. (1998). Quasioptical phonon-cooled NbN hot electron bolometer mixers at 0.5-1.1 THz. In Proc. 9th Int. Symp. Space Terahertz Technol. (pp. 45–51).
Abstract: The noise performance of a receiver incorporating spiral antenna coupled NbN phonon-cooled superconducting hot electron bolometric mixer is measured from 450 GHz to 1200 GHz. The mixer element is thin (thickness nm) NbN 1.5 pm wide and 0.2 i.um long film fabricated by lift-off e-beam lithography on high-resistive silicon substrate. The noise of the receiver temperature is 1000 K at 800-900 GHz, 1200 K at 950 GHz, and 1600 K at 1.08 THz. The required (absorbed) local-oscillator power is —20 nW.
|
|
|
|
Gousev, Y. P., Olsson, H. K., Gol'tsman, G. N., Voronov, B. M., & Gershenzon, E. M. (1998). NbN hot-electron mixer at radiation frequencies between 0.9 THz and 1.2 THz. In Proc. 9th Int. Symp. Space Terahertz Technol. (pp. 121–129).
Abstract: We report on noise temperature measurements for a NbN phonon-cooled hot-electron mixer at radiation frequencies between 0.9 THz and 1.2 THz. Radiation was coupled to the mixer, placed in a vacuum chamber of He cryostat, by means of a planar spiral antenna and a Si immersion lens. A backward-wave oscillator, tunable throughout the spectral range, delivered an output power of few 1.1W that was enough for optimum operation of the mixer. At 4.2 K ambient temperature and 1.025 THz radiation frequency, we obtained a receiver noise temperature of 1550 K despite of using a relatively noisy room-temperature amplifier at the intermediate frequency port. The noise temperature was fairly constant throughout the entire operation range and for intermediate frequencies from 1 GHz to 2 GHz.
|
|
|
|
Yazoubov, P., Kroug, M., Merkel, H., Kollberg, E., Gol'tsman, G., Lipatov, A., et al. (1998). Quasioptical NbN phonon-cooled hot electron bolometric mixers with low optimal local oscillator power. In Proc. 9th Int. Symp. Space Terahertz Technol. (pp. 131–140).
Abstract: In this paper, the noise perform.ance of NIN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixers is investigated in the 0.55-1.1 THz frequency range. The best results of the DSB noise temperature are: 500 K at 640 GHz, 600 K at 750 GHz, 850 K at 910 GHz and 1250 K at 1.1 THz. The water vapor in the signal path causes a significant contribution to the measured noise temperature around 1.1 THz. The required LO power is typically about 60 nW. The frequency response of the spiral antenna+lens system is measured using a Fourier Transform Spectrometer with the HEB operating in a detector mode.
|
|
|
|
Il'in, K. S., Cherednichenko, S. I., Gol'tsman, G. N., Currie, M., & Sobolewski, R. (1998). Comparative study of the bandwidth of phonon-cooled NbN hot-electron bolometers in submillimeter and optical wavelength ranges. In Proc. 9th Int. Symp. Space Terahertz Technol. (pp. 323–330).
Abstract: We report the results of the bandwidth measurements of NbN hot-electron bolometers, perfomied in the terahertz frequency domain at 140 GHz and 660 GHz and in time domain in the optical range at the wavelength of 395 nm.. Our studies were done on 3.5-nm-thick NbN films evaporated on sapphire substrates and patterned into ilin-size microbridges. In order to measure the gain bandwidth, we used two identical BWOs (140 or 660 GHz), one functioning as a local oscillator and the other as a signal source. The bandwidth we achieved was 3.5-4 GHz at 4.2 K with the optimal LO and DC biases. Time-domain measurements with a resolution below 300 fs were performed using an electro-optic sampling system, in the temperature range between 4.2 K to 9 K at various values of the bias current and optical power. The obtained response time of the NbN hot-electron bolometer to —100- fs-wide Ti:sapphire laser pulses was about 27 ps, what corresponds to the 5.9 GHz gain bandwidth.
|
|
|
|
Gousev, Y. P., Semenov, A. D., Goghidze, I. G., Pechen, E. V., Varlashkin, A. V., Gol'tsman, G. N., et al. (1997). Current dependent noise in a YBa2Cu3O7-δ hot-electron bolometer. IEEE Trans. Appl. Supercond., 7(2), 3556–3559.
Abstract: We investigated the output noise of a YBa2Cu3O7-δ (YBCO) superconducting hot-electron bolometer (HEB) in a large frequency range (10 kHz to 8 GHz); the bolometer either consisted of a structured 50 nm thick YBCO film on LaAlO/sub 3/ or a 30 nm thick film on a MgO substrate. We found that flicker noise dominated at low frequencies (below 1 MHz), while at higher frequencies Johnson noise and a current dependent noise were the main noise sources.
|
|
|
|
Semenov, A. D., Gousev, Y. P., Renk, K. F., Voronov, B. M., Gol'tsman, G. N., Gershenzon, E. M., et al. (1997). Noise characteristics of a NbN hot-electron mixer at 2.5 THz. IEEE Trans. Appl. Supercond., 7(2), 3572–3575.
Abstract: The noise temperature of a NbN phonon cooled hot-electron mixer has been measured at a frequency of 2.5 THz for various operating conditions. We obtained for optimal operation a double sideband mixer noise temperature of /spl ap/14000 K and a system conversion loss of /spl ap/23 dB at intermediate frequencies up to 1 GHz. The dependences of the mixer noise temperature on the bias voltage, local oscillator power, and intermediate frequency were consistent with the phenomenological description based on the effective temperature approximation.
|
|
|
|
Svechnikov, S. I., Okunev, O. V., Yagoubov, P. A., Gol'tsman, G. N., Voronov, B. M., Cherednichenko, S. I., et al. (1997). 2.5 THz NbN hot electron mixer with integrated tapered slot antenna. IEEE Trans. Appl. Supercond., 7(2), 3548–3551.
Abstract: A Hot Electron Bolometer (HEB) mixer for 2.5 THz utilizing a NbN thin film device, integrated with a Broken Linearly Tapered Slot Antenna (BLTSA), has been fabricated and is presently being tested. The NbN HEB device and the antenna were fabricated on a SiO2membrane. A 0.5 micrometer thick SiO2layer was grown by rf magnetron reactive sputtering on a GaAs wafer. The HEB device (phonon-cooled type) was produced as several parallel strips, 1 micrometer wide, from an ultrathin NbN film 4-7 nm thick, that was deposited onto the SiO2layer by dc magnetron reactive sputtering. The BLTSA was photoetched in a multilayer Ti-Au metallization. In order to strengthen the membrane, the front-side of the wafer was coated with a 5 micrometer thick polyimide layer just before the membrane formation. The last operation was anisotropic etching of the GaAs in a mixture of HNO3and H2O2.
|
|
|
|
Svechnikov, S., Gol'tsman, G., Voronov, B., Yagoubov, P., Cherednichenko, S., Gershenzon, E., et al. (1997). Spiral antenna NbN hot-electron bolometer mixer at submm frequencies. IEEE Trans. Appl. Supercond., 7(2), 3395–3398.
Abstract: We have studied the phonon-cooled hot-electron bolometer (HEB) as a quasioptical mixer based on a spiral antenna designed for the 0.3-1 THz frequency band and fabricated on sapphire and high resistivity silicon substrates. HEB devices were produced from superconducting 3.5-5 nm thick NbN films with a critical temperature 10-12 K and a critical current density of approximately 10/sup 7/ A/cm/sup 2/ at 4.2 K. For these devices we reached a DSB receiver noise temperature below 1500 K, a total conversion loss of L/sub t/=16 dB in the 500-700 GHz frequency range, an IF bandwidth of 3-4 GHz and an optimal LO absorbed power of /spl sime/4 /spl mu/W. We experimentally analyzed various contributions to the conversion loss and obtained an RF coupling factor of about 5 dB, internal mixer loss of 10 dB and IF mismatch of 1 dB.
|
|