Cherednichenko, S., Kroug, M., Khosropanah, P., Adam, A., Merkel, H., Kolberg, E., et al. (2002). A broadband terahertz heterodyne receiver with an NbN HEB mixer. In Harward University (Ed.), Proc. 13th Int. Symp. Space Terahertz Technol. (pp. 85–95). Cambridge, MA, USA.
Abstract: We present a broadband and low noise heterodyne receiver for 1.4-1.7 THz designed for the Hershel Space Observatory. A phonon- cooled NbN HEB mixer was integrated with a normal metal double- slot antenna and an elliptical silicon lens. DSB receiver noise temperature Tr was measured from 1 GHz through 8GHz intermediate frequency band with 50 MHz instantaneous bandwidth. At 4.2 K bath temperature and at 1.6 THz LO frequency Tr is 800 K with the receiver noise bandwidth of 5 GHz. While at 2 K bath temperature Tr was as low as 700 K. At 0.6 THz and 1.1 THz a spiral antenna integrated NbN HEB mixer showed the receiver noise temperature 500 K and 800 K, though no antireflection coating was used in this case. Tr of 1100 K was achieved at 2.5 THz while the receiver noise bandwidth was 4 GHz.
|
|
|
Meledin, D., Tong, C. Y. - E., Blundell, R., Kaurova, N., Smirnov, K., Voronov, B., et al. (2002). The sensitivity and IF bandwidth of waveguide NbN hot electron bolometer mixers on MgO buffer layers over crystalline quartz. In Harvard university (Ed.), Proc. 13th Int. Symp. Space Terahertz Technol. (pp. 65–72). Cambridge, MA, USA.
Abstract: We have developed and characterized waveguide phonon-cooled NbN Hot Electron Bolometer (FMB) mixers fabricated from a 3-4 nm thick NbN film deposited on a 200nm thick MgO buffer layer over crystalline quartz. Double side band receiver noise temperatures of 900-1050 K at 1.035 THz, and 1300-1400 K at 1.26 THz have been measured at an intermediate frequency of 1.5 GHz. The intermediate frequency bandwidth, measured at 0.8 THz LO frequency, is 3.2 GHz at the optimal bias point for low noise receiver operation.
|
|
|
Vahtomin, Y. B., Finkel, M. I., Antipov, S. V., Voronov, B. M., Smirnov, K. V., Kaurova, N. S., et al. (2002). Gain bandwidth of phonon-cooled HEB mixer made of NbN thin film with MgO buffer layer on Si. In Harvard university (Ed.), Proc. 13th Int. Symp. Space Terahertz Technol. (pp. 259–270). Cambridge, MA, USA.
Abstract: We present recently obtained values for gain bandwidth of NbN HEB mixers for different substrates and film thicknesses and for MgO buffer layer on Si at LO frequency of 0.85-1 THz. The maximal bandwidth, 5.2 GHz, was achieved for the device on MgO buffer layer on Si with a 2 nm thick NbN film. Functional devices based on NbN films of such thickness were fabricated for the first time due to an improvement of superconducting properties of NbN film deposited on MgO buffer layer on Si substrate.
|
|
|
Hübers, H. - W., Semenov, A. D., Richter, H., Schubert, J., Hadjiloucas, S., Bowen, J. W., et al. (2001). Antenna pattern of the quasi-optical hot-electron bolometric mixer at terahertz frequencies. In Proc. 12th Int. Symp. Space Terahertz Technol. (pp. 286–296). San Diego, CA, USA.
|
|
|
Cherednichenko, S., Kroug, M., Merkel, H., Kollberg, E., Loudkov, D., Smirnov, K., et al. (2001). Local oscillator power requirement and saturation effects in NbN HEB mixers. In C. Iit.u.t.e of T. Jet Propulsion Laboratory (Ed.), Proc. 12th Int. Symp. Space Terahertz Technol. (pp. 273–285). San Diego, CA, USA.
Abstract: The local oscillator power required for NbN hot-electron bolometric mixers (P LO ) was investigated with respect to mixer size, critical temperature and ambient temperature. P LO can be decreased by a factor of 10 as the mixer size decreases from 4×0.4 µm 2 to 0.6×0.13 µm 2 . For the smallest volume mixer the optimal local oscillator power was found to be 15 nW. We found that for such mixer no signal compression was observed up to an input signal of 2 nW which corresponds to an equivalent input load of 20,000 K. For a constant mixer volume, reduction of T c can decrease optimal local oscillator power at least by a factor of 2 without a deterioration of the receiver noise temperature. Bath temperature was found to have minor effect on the receiver characteristics.
|
|
|
Kroug, M., Cherednichenko, S., Merkel, H., Kollberg, E., Voronov, B., Gol'tsman, G., et al. (2001). NbN hot electron bolometric mixers for terahertz receivers. IEEE Trans. Appl. Supercond., 11(1), 962–965.
Abstract: Sensitivity and gain bandwidth measurements of phonon-cooled NbN superconducting hot-electron bolometer mixers are presented. The best receiver noise temperatures are: 700 K at 1.6 THz and 1100 K at 2.5 THz. Parylene as an antireflection coating on silicon has been investigated and used in the optics of the receiver. The dependence of the mixer gain bandwidth (GBW) on the bias voltage has been measured. Starting from low bias voltages, close to operating conditions yielding the lowest noise temperature, the GBW increases towards higher bias voltages, up to three times the initial value. The highest measured GBW is 9 GHz within the same bias range the noise temperature increases by a factor of two.
|
|
|
Semenov, A. D., Hübers, H. –W., Schubert, J., Gol'tsman, G. N., Elantiev, A. I., Voronov, B. M., et al. (2000). Frequency dependent noise temperature of the lattice cooled hot-electron terahertz mixer. In Proc. 11th Int. Symp. Space Terahertz Technol. (pp. 39–48).
Abstract: We present the measurements and the theoretical model on the frequency dependent noise temperature of a lattice cooled hot electron bolometer (HEB) mixer in the terahertz frequency range. The experimentally observed increase of the noise temperature with frequency is a cumulative effect of the non-uniform distribution of the high frequency current in the bolometer and the charge imbalance, which occurs near the edges of the normal domain and contacts with normal metal. In addition, we present experimental results which show that the noise temperature of a HEB mixer can be reduced by about 30% due to a Parylene antireflection coating on the Silicon hyperhemispheric lens.
|
|
|
Tong, C. - Y. E., Kawamura, J., Todd, R. H., Papa, D. C., Blundell, R., Smith, M., et al. (2000). Successful operation of a 1 THz NbN hot-electron bolometer receiver. In Proc. 11th Int. Symp. Space Terahertz Technol. (pp. 49–59).
Abstract: A phonon-cooled NbN superconductive hot-electron bolometer receiver covering the frequency range 0.8-1.04 THz has successfully been used for astronomical observation at the Sub-Millimeter Telescope Observatory on Mount Graham, Arizona. This waveguide heterodyne receiver is a modified version of our fixed-tuned 800 GHz HEB receiver to allow for operation beyond 1 THz. The measured noise temperature of this receiver is about 1250 K at 0.81 THz, 560 K at 0.84 THz, and 1600 K at 1.035 THz. It has a 1 GHz wide IF bandwidth, centered at 1.8 GHz. This receiver has recently been used to detect the CO (9-8) molecular line emission at 1.037 THz in the Orion nebula. This is the first time a ground-based heterodyne receiver has been used to detect a celestial source above 1 THz.
|
|
|
Schubert, J., Semenov, A., Gol'tsman, G., Hübers, H. - W., Schwaab, G., Voronov, B., et al. (1999). Noise temperature of an NbN hot-electron bolometric mixer at frequencies from 0.7 THz to 5.2 THz. Supercond. Sci. Technol., 12(11), 748–750.
Abstract: We report on noise temperature measurements of an NbN phonon-cooled hot-electron bolometric mixer in the terahertz frequency range. The devices were 3 nm thick films with in-plane dimensions 1.7 × 0.2 µm2 and 0.9 × 0.2 µm2 integrated in a complementary logarithmic-spiral antenna. Measurements were performed at seven frequencies ranging from 0.7 THz to 5.2 THz. The measured DSB noise temperatures are 1500 K (0.7 THz), 2200 K (1.4 THz), 2600 K (1.6 THz), 2900 K (2.5 THz), 4000 K (3.1 THz), 5600 K (4.3 THz) and 8800 K (5.2 THz).
|
|
|
Yagoubov, P., Kroug, M., Merkel, H., Kollberg, E., Schubert, J., & Hübers, H. - W. (1999). NbN hot electron bolometric mixers at frequencies between 0.7 and 3.1 THz. Supercond. Sci. Technol., 12(11), 989–991.
Abstract: The performance of NbN-based phonon-cooled hot electron bolometric (HEB) quasioptical mixers is investigated in the 0.7-3.1 THz frequency range. The devices are made from a 3.5-4 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The length of the bolometer microbridge is 0.1-0.2 µm; the width is 1-2 µm. The best results of the DSB receiver noise temperature measured at 1.5 GHz intermediate frequency are: 800 K at 0.7 THz, 1100 K at 1.6 THz, 2000 K at 2.5 THz and 4200 K at 3.1 THz. The measurements were performed with a far infrared laser as the local oscillator (LO) source. The estimated LO power requirement is less than 500 nW at the receiver input. First results on spiral antenna polarization measurements are reported.
|
|
|
Kawamura, J. H., Tong, C. - Y. E., Blundell, R., Cosmo Papa, D., Hunter, T. R., Gol'tsman, G., et al. (1999). An 800 GHz NbN phonon-cooled hot-electron bolometer mixer receiver. IEEE Trans. Appl. Supercond., 9(2), 3753–3756.
Abstract: We describe a heterodyne receiver developed for astronomical applications to operate in the 350 /spl mu/m atmospheric window. The waveguide receiver employs a superconductive NbN phonon-cooled hot-electron bolometer mixer. The double sideband receiver noise temperature closely follows 1 kGHz/sup -1/ across 780-870 GHz, with the intermediate frequency centered at 1.4 GHz. The conversion loss is about 15 dB. The receiver was installed for operation at the University of Arizona/Max Planck Institute for Radio Astronomy Submillimeter Telescope facility. The instrument was successfully used to conduct test observations of a number of celestial sources in a number of astronomically important spectral lines.
|
|
|
Ekstörm, H., Kollberg, E., Yagoubov, P., Gol'tsman, G., Gershenzon, E., & Yngvesson, S. (1997). Gain and noise bandwidth of NbN hot-electron bolometric mixers. Appl. Phys. Lett., 70(24), 3296–3298.
Abstract: We have measured the noise performance and gain bandwidth of 35 Å thin NbN hot-electron mixers integrated with spiral antennas on silicon substrate lenses at 620 GHz. The best double-sideband receiver noise temperature is less than 1300 K with a 3 dB bandwidth of ≈5 GHz. The gain bandwidth is 3.2 GHz. The mixer output noise dominated by thermal fluctuations is 50 K, and the intrinsic conversion gain is about −12 dB. Without mismatch losses and excluding the loss from the beamsplitter, we expect to achieve a receiver noise temperature of less than 700 K.
|
|
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 23–28).
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
|
|
Yagubov, P., Gol'tsman, G., Voronov, B., Seidman, L., Siomash, V., Cherednichenko, S., et al. (1996). The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 290–302). Charlottesville, Virginia, USA.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|