Kawakami, A., Saito, S., & Hyodo, M. (2011). Fabrication of nano-antennas for superconducting Infrared detectors. IEEE Trans. Appl. Supercond., 21(3), 632–635.
Abstract: To improve the response performance of superconducting infrared detectors, we have developed a fabrication process for nano-antennas. A nano-antenna consists of a dipole antenna, and a superconducting thin film strip placed in the antenna's center. By measuring the transition temperature of the superconducting strips, we confirmed that their superconductivity maintained a good condition after the nano-antenna fabrication process. We also evaluated nano-antenna characteristics using Fourier transform infrared spectroscopy. The evaluated antenna length and width were respectively set at around 2400 nm and 400 nm, and the antennas were placed at intervals of several micrometers around the area of 1 mm2 . In an evaluation of spectral transmission characteristics, clear absorption caused by antenna effects was observed at around 1400 cm-1. High polarization dependencies were also observed.
|
|
|
Galeazzi, M. (2011). Fundamental noise processes in TES devices. IEEE Trans. Appl. Supercond., 21(3), 267–271.
Abstract: Microcalorimeters and bolometers are noise-limited devices, therefore, a proper understanding of all noise sources is essential to predict and interpret their performance. In this paper, I review the fundamental noise processes contributing to Transition Edge Sensor (TES) microcalorimeters and bolometers and their effect on device performance. In particular, I will start with a simple, monolithic device model, moving to a more complex one involving discrete components, to finally move to today's more realistic, comprehensive model. In addition to the basic noise contribution (equilibrium Johnson noise and phonon noise), TES are significantly affected by extra noise, which is commonly referred to as excess noise. Different fundamental processes have been proposed and investigated to explain the origin of this excess noise, in particular near equilibrium non-linear Johnson noise, flux-flow noise, and internal thermal fluctuation noise. Experimental evidence shows that all three processes are real and contribute, at different levels, to the TES noise, although different processes become important at different regimes. It is therefore time to discard the term “excess noise” and consider these terms part of the “fundamental noise processes” instead.
|
|
|
Lobanov, Y., Shcherbatenko, M., Finkel, M., Maslennikov, S., Semenov, A., Voronov, B. M., et al. (2015). NbN hot-electron-bolometer mixer for operation in the near-IR frequency range. IEEE Trans. Appl. Supercond., 25(3), 2300704 (1 to 4).
Abstract: Traditionally, hot-electron-bolometer (HEB) mixers are employed for THz and “super-THz” heterodyne detection. To explore the near-IR spectral range, we propose a fiber-coupled NbN film based HEB mixer. To enhance the incident-light absorption, a quasi-antenna consisting of a set of parallel stripes of gold is used. To study the antenna effect on the mixer performance, we have experimentally studied a set of devices with different size of the Au stripe and spacing between the neighboring stripes. With use of the well-known isotherm technique we have estimated the absorption efficiency of the mixer, and the maximum efficiency has been observed for devices with the smallest pitch of the alternating NbN and NbN-Au stripes. Also, a proper alignment of the incident Eâƒ<2014>-field with respect to the stripes allows us to improve the coupling further. Studying IV-characteristics of the mixer under differently-aligned Eâƒ<2014>-field of the incident radiation, we have noticed a difference in their shape. This observation suggests that a difference exists in the way the two waves with orthogonal polarizations parallel and perpendicular Eâƒ<2014>-field to the stripes heat the electrons in the HEB mixer. The latter results in a variation in the electron temperature distribution over the HEB device irradiated by the two waves.
|
|
|
Seliverstov, S., Maslennikov, S., Ryabchun, S., Finkel, M., Klapwijk, T. M., Kaurova, N., et al. (2015). Fast and sensitive terahertz direct detector based on superconducting antenna-coupled hot electron bolometer. IEEE Trans. Appl. Supercond., 25(3), 2300304.
Abstract: We characterize superconducting antenna-coupled hot-electron bolometers for direct detection of terahertz radiation operating at a temperature of 9.0 K. The estimated value of responsivity obtained from lumped-element theory is strongly different from the measured one. A numerical calculation of the detector responsivity is developed, using the Euler method, applied to the system of heat balance equations written in recurrent form. This distributed element model takes into account the effect of nonuniform heating of the detector along its length and provides results that are in better agreement with the experiment. At a signal frequency of 2.5 THz, the measured value of the optical detector noise equivalent power is 2.0 × 10-13 W · Hz-0.5. The value of the bolometer time constant is 35 ps. The corresponding energy resolution is about 3 aJ. This detector has a sensitivity similar to that of the state-of-the-art sub-millimeter detectors operating at accessible cryogenic temperatures, but with a response time several orders of magnitude shorter.
|
|
|
Hajenius, M., Barends, R., Gao, J. R., Klapwijk, T. M., Baselmans, J. J. A., Baryshev, A., et al. (2005). Local resistivity and the current-voltage characteristics of hot electron bolometer mixers. IEEE Trans. Appl. Supercond., 15(2), 495–498.
Abstract: Hot-electron bolometer devices, used successfully in low noise heterodyne mixing at frequencies up to 2.5 THz, have been analyzed. A distributed temperature numerical model of the NbN bridge, based on a local electron and a phonon temperature, is used to model pumped IV curves and understand the physical conditions during the mixing process. We argue that the mixing is predominantly due to the strongly temperature dependent local resistivity of the NbN. Experimentally we identify the origins of different transition temperatures in a real HEB device, suggesting the importance of the intrinsic resistive transition of the superconducting bridge in the modeling.
|
|
|
Korneev, A. A., Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Semenov, A. V., Vodolazov, D. Y., et al. (2015). Characterization of MoSi superconducting single-photon detectors in the magnetic field. IEEE Trans. Appl. Supercond., 25(3), 2200504 (1 to 4).
Abstract: We investigate the response mechanism of nanowire superconducting single-photon detectors (SSPDs) made of amorphous MoxSi1-x. We study the dependence of photon count and dark count rates on bias current in magnetic fields up to 113 mT at 1.7 K temperature. The observed behavior of photon counts is similar to the one recently observed in NbN SSPDs. Our results show that the detecting mechanism of relatively high-energy photons does not involve the vortex penetration from the edges of the film, and on the contrary, the detecting mechanism of low-energy photons probably involves the vortex penetration from the film edges.
|
|
|
Korneev, A., Korneeva, Y., Manova, N., Larionov, P., Divochiy, A., Semenov, A., et al. (2013). Recent nanowire superconducting single-photon detector optimization for practical applications. IEEE Trans. Appl. Supercond., 23(3), 2201204 (1 to 4).
Abstract: In this paper, we present our approaches to the development of fiber-coupled superconducting single photon detectors with enhanced photon absorption. For such devices we have measured detection efficiency in wavelength range from 500 to 2000 nm. The best fiber coupled devices exhibit detection efficiency of 44.5% at 1310 nm wavelength and 35.5% at 1550 nm at 10 dark counts per second.
|
|
|
Kitaygorsky, J., Zhang, J., Verevkin, A., Sergeev, A., Korneev, A., Matvienko, V., et al. (2005). Origin of dark counts in nanostructured NbN single-photon detectors. IEEE Trans. Appl. Supercond., 15(2), 545–548.
Abstract: We present our study of dark counts in ultrathin (3.5 to 10 nm thick), narrow (120 to 170 nm wide) NbN superconducting stripes of different lengths. In experiments, where the stripe was completely isolated from the outside world and kept at temperature below the critical temperature Tc, we detected subnanosecond electrical pulses associated with the spontaneous appearance of the temporal resistive state. The resistive state manifested itself as generation of phase-slip centers (PSCs) in our two-dimensional superconducting stripes. Our analysis shows that not far from Tc, PSCs have a thermally activated nature. At lowest temperatures, far below Tc, they are created by quantum fluctuations.
|
|
|
Zhang, J., Slysz, W., Verevkin, A., Okunev, O., Chulkova, G., Korneev, A., et al. (2003). Response time characterization of NbN superconducting single-photon detectors. IEEE Trans. Appl. Supercond., 13(2), 180–183.
Abstract: We report our time-resolved measurements of NbN-based superconducting single-photon detectors. The structures are meander-type, 10-nm thick, and 200-nm wide stripes and were operated at 4.2 K. We have shown that the NbN devices can count single-photon pulses with below 100-ps time resolution. The response signal pulse width was about 150 ps, and the system jitter was measured to be 35 ps.
|
|
|
Skalare, A., McGrath, W. R., Echternach, P. M., Leduc, H. G., Siddiqi, I., Verevkin, A., et al. (2001). Aluminum hot-electron bolometer mixers at submillimeter wavelengths. IEEE Trans. Appl. Supercond., 11(1), 641–644.
Abstract: Diffusion-cooled aluminum hot-electron bolometer (HEB) mixers are of interest for low-noise high resolution THz-frequency spectroscopy within astrophysics. Al HEB mixers offer operation with an order of magnitude less local oscillator power, higher intermediate frequency bandwidth and potentially lower noise than competing devices made from other materials. We report on mixer experiments at 618 GHz with devices fabricated from films with sheet resistances in the range from about 55 Ω down to about 9 Ω per square. Intermediate frequency bandwidths of up to 3 GHz were measured (1 μm long device), with absorbed local oscillator power levels of 0.5 to 6 nW and mixer conversion up to -21.5 dB. High input coupling efficiency implies that the electrons in the device are able to thermalize before escaping from the device. It was found that the long coherence length complicates mixer operations due to the proximity of the contact pads. Also, saturation at the IF frequency may be a concern for this type of device, and warrants further studies.
|
|
|
Gupta, D., & Kadin, A. M. (1999). Single-photon-counting hotspot detector with integrated RSFQ readout electronics. IEEE Trans. Appl. Supercond., 9(2), 4487–4490.
Abstract: Absorption of an infrared photon in an ultrathin film (such as 10-nm NbN) creates a localized nonequilibrium hotspot on the submicron length scale and sub-ns time scale. If a strip /spl sim/1 /spl mu/m wide is biased in the middle of the superconducting transition, this hotspot will lead to a resistance pulse with amplitude proportional to the energy of the incident photon. This resistance pulse, in turn, can be converted to a current pulse and inductively coupled to a SQUID amplifier with a digitized output, operating at 4 K or above. A preliminary design analysis indicates that this data can be processed on-chip, using ultrafast RSFQ digital circuits, to obtain a sensitive infrared detector for wavelengths up to 10 /spl mu/m and beyond, with bandwidth of 1 GHz, that counts individual photons and measures their energy with 25 meV resolution. This proposed device combines the speed of a hot-electron bolometer with the single-photon-counting ability of a transition-edge microcalorimeter, to obtain an infrared detector with sensitivity, speed, and spectral selectivity that are unmatched by any alternative technology.
|
|
|
Larrey, V., Villegier, J. - C., Salez, M., Miletto-Granozio, F., & Karpov, A. (1999). Processing and characterization of high Jc NbN superconducting tunnel junctions for THz analog circuits and RSFQ. IEEE Trans. Appl. Supercond., 9(2), 3216–3219.
Abstract: A generic NbN Superconducting Tunnel Junctions (STJ) technology has been developed using conventional substrates (Si and SOI-SIMOX) for making THz spectrometers including SIS receivers and RSFQ logic gates. NbN/MgO/NbN junctions with area of 1 /spl mu/m/sup 2/, Jc of 10 kA/cm/sup 2/ and low sub-gap leakage current (Vm>25 mV) are currently obtained from room temperature sputtered multilayers followed by a post-annealing at 250/spl deg/C. Using a thin MgO buffer layer deposited underneath the NbN electrodes, ensures lower NbN surface resistance values (Rs=7 /spl mu//spl Omega/) at 10 GHz and 4 K. Epitaxial NbN [100] films on MgO [100] with high gap frequency (1.4 THz) have also been achieved under the same deposition conditions at room temperature. The NbN SIS has shown good I-V photon induced steps when LO pumped at 300 GHz. We have developed an 8 levels Al/NbN multilayer process for making 1.5 THz SIS mixers (including Al antennas) on Si membranes patterned in SOI-SIMOX. Using the planarization techniques developed at the Si-MOS CEA-LETI Facility, we have also demonstrated on the possibility of extending our NbN technology to high level RSFQ circuit integration with 0.5 /spl mu/m/sup 2/ junction area, made on large area substrates (up to 8 inches).
|
|
|
Trifonov, A., Tong, C. - Y. E., Grimes, P., Lobanov, Y., Kaurova, N., Blundell, R., et al. (2017). Development of A Silicon Membrane-based Multi-pixel Hot Electron Bolometer Receiver. In IEEE Trans. Appl. Supercond. (Vol. 27, 6).
Abstract: We report on the development of a multi-pixel
Hot Electron Bolometer (HEB) receiver fabricated using
silicon membrane technology. The receiver comprises a
2 × 2 array of four HEB mixers, fabricated on a single
chip. The HEB mixer chip is based on a superconducting
NbN thin film deposited on top of the silicon-on-insulator
(SOI) substrate. The thicknesses of the device layer and
handling layer of the SOI substrate are 20 μm and 300 μm
respectively. The thickness of the device layer is chosen
such that it corresponds to a quarter-wave in silicon at
1.35 THz. The HEB mixer is integrated with a bow-tie
antenna structure, in turn designed for coupling to a
circular waveguide,
|
|
|
Samsonova, A., Zolotov, P., Baeva, E., Lomakin, A., Titova, N., Kardakova, A., et al. (2021). Signatures of surface magnetic disorder in thin niobium films. IEEE Trans. Appl. Supercond., , 1.
Abstract: We present our studies on the evolution of the normal and superconducting properties with thickness of thin Nb films with a low level of non-magnetic disorder (kFl 150 for the thickest film in the set). The analysis of the superconducting behavior points to the presence of magnetic moments, hidden in the native oxide on the surface of Nb films. Using the Abrikosov-Gorkov theory, we obtain the density of surface magnetic moments of 1013 cm-2, which is in agreement with the previously reported data for Nb films.
|
|
|
Titova, N., Kardakova, A. I., Tovpeko, N., Ryabchun, S., Mandal, S., Morozov, D., et al. (2017). Slow electron–phonon cooling in superconducting diamond films. IEEE Trans. Appl. Supercond., 27(4), 1–4.
Abstract: We have measured the electron-phonon energy-relaxation time, τ eph , in superconducting boron-doped diamond films grown on silicon substrate by chemical vapor deposition. The observed electron-phonon cooling times vary from 160 ns at 2.70 K to 410 ns at 1.8 K following a T -2-dependence. The data are consistent with the values of τ eph previously reported for single-crystal boron-doped diamond films epitaxially grown on diamond substrate. Such a noticeable slow electron-phonon relaxation in boron-doped diamond, in combination with a high normal-state resistivity, confirms a potential of superconducting diamond for ultrasensitive superconducting bolometers.
|
|