Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 23–28).
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
|
|
Yagubov, P., Gol'tsman, G., Voronov, B., Seidman, L., Siomash, V., Cherednichenko, S., et al. (1996). The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 290–302). Charlottesville, Virginia, USA.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|