Korneev, A., Lipatov, A., Okunev, O., Chulkova, G., Smirnov, K., Gol’tsman, G., et al. (2003). GHz counting rate NbN single-photon detector for IR diagnostics of VLSI CMOS circuits. Microelectronic Engineering, 69(2-4), 274–278.
Abstract: We present a new, simple to manufacture superconducting single-photon detector operational in the range from ultraviolet to mid-infrared radiation wavelengths. The detector combines GHz counting rate, high quantum efficiency and very low level of dark (false) counts. At 1.3–1.5 μm wavelength range our detector exhibits a quantum efficiency of 5–10%. The detector photoresponse voltage pulse duration was measured to be about 150 ps with jitter of 35 ps and both of them were limited mostly by our measurement equipment. In terms of quantum efficiency, dark counts level, speed of operation the detector surpasses all semiconductor counterparts and was successfully applied for CMOS integrated circuits diagnostics.
|
Zhang, J., Boiadjieva, N., Chulkova, G., Deslandes, H., Gol'tsman, G. N., Korneev, A., et al. (2003). Noninvasive CMOS circuit testing with NbN superconducting single-photon detectors. Electron. Lett., 39(14), 1086–1088.
Abstract: The 3.5 nm thick-film, meander-structured NbN superconducting single-photon detectors have been implemented in the CMOS circuit-testing system based on the detection of near-infrared photon emission from switching transistors and have significantly improved the performance of the system. Photon emissions from both p- and n-MOS transistors have been observed.
|
Sobolewski, R., Zhang, J., Slysz, W., Pearlman, A., Verevkin, A., Lipatov, A., et al. (2003). Ultrafast superconducting single-photon optical detectors. In J. Spigulis, J. Teteris, M. Ozolinsh, & A. Lusis (Eds.), Proc. SPIE (Vol. 5123, pp. 1–11). SPIE.
Abstract: We present a new class of single-photon devices for counting of both visible and infrared photons. Our superconducting single-photon detectors (SSPDs) are characterized by the intrinsic quantum efficiency (QE) reaching up to 100%, above 10 GHz counting rate, and negligible dark counts. The detection mechanism is based on the photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconducting stripe. The devices are fabricated from 3.5-nm-thick NbN films and operate at 4.2 K, well below the NbN superconducting transition temperature. Various continuous and pulsed laser sources in the wavelength range from 0.4 μm up to >3 μm were implemented in our experiments, enabling us to determine the detector QE in the photon-counting mode, response time, and jitter. For our best 3.5-nm-thick, 10×10 μm2-area devices, QE was found to reach almost 100% for any wavelength shorter than about 800 nm. For longer-wavelength (infrared) radiation, QE decreased exponentially with the photon wavelength increase. Time-resolved measurements of our SSPDs showed that the system-limited detector response pulse width was below 150 ps. The system jitter was measured to be 35 ps. In terms of the counting rate, jitter, and dark counts, the NbN SSPDs significantly outperform their semiconductor counterparts. Already identifeid and implemented applications of our devices range from noninvasive testing of semiconductor VLSI circuits to free-space quantum communications and quantum cryptography.
|
Zhang, J., Pearlman, A., Slysz, W., Verevkin, A., Sobolewski, R., Okunev, O., et al. (2003). Infrared picosecond superconducting single-photon detectors for CMOS circuit testing. In CLEO/QELS (Cmv4). Optical Society of America.
Abstract: Novel, NbN superconducting single-photon detectors have been developed for ultrafast, high quantum efficiency detection of single quanta of infrared radiation. Our devices have been successfully implemented in a commercial VLSI CMOS circuit testing system.
|
Verevkin, A. A., Zhang, J., Slysz, W., Sobolewski, R., Lipatov, A. P., Okunev, O., et al. (2002). Superconducting single-photon detectors for GHz-rate free-space quantum communications. In J. C. Ricklin, & D. G. Voelz (Eds.), Proc. SPIE (Vol. 4821, pp. 447–454). SPIE.
Abstract: We report our studies on the performance of new NbN ultrathin-film superconducting single-photon detectors (SSPDs). Our SSPDs exhibit experimentally measured quantum efficiencies from 5% at wavelength λ = 1550 nm up to 10% at λ = 405 nm, with exponential, activation-energy-type spectral sensitivity dependence in the 0.4-μm – 3-μm wavelength range. Using a variable optical delay setup, we have shown that our NbN SSPDs can resolve optical photons with a counting rate up to 10 GHz, presently limited by the read-out electronics. The measured device jitter was below 35 ps under optimum biasing conditions. The extremely high photon counting rate, together with relatively high (especially for λ > 1 μm) quantum efficiency, low jitter, and very low dark counts, make NbN SSPDs very promising for free-space communications and quantum cryptography.
|