Tretyakov, I. V., Ryabchun, S. A., Maslennikov, S. N., Finkel, M. I., Kaurova, N. S., Seleznev, V. A., et al. (2008). NbN HEB mixer: fabrication, noise temperature reduction and characterization. In Proc. Basic problems of superconductivity. Moscow-Zvenigorod.
Abstract: We demonstrate that in the terahertz region superconducting hot-electron mixers offer the lowest noise temperature, opening the possibility of using HTS's in the future to fabricate these devices. Specifically, a noise temperature of 950 K was measured for the receiver operating at 2.5 THz with a NbN HEB mixer, and a gain bandwidth of 6 GHz was measured at 300 GHz near Tc for the same mixer.
|
Ryabchun, S. A., Tretyakov, I. V., Pentin, I. V., Kaurova, N. S., Seleznev, V. A., Voronov, B. M., et al. (2009). Low-noise wide-band hot-electron bolometer mixer based on an NbN film. Radiophys. Quant. Electron., 52(8), 576–582.
Abstract: We develop and study a hot-electron bolometer mixer made of a two-layer NbN–Au film in situ deposited on a silicon substrate. The double-sideband noise temperature of the mixer is 750 K at a frequency of 2.5 THz. The conversion efficiency measurements show that at the superconducting transition temperature, the intermediate-frequency bandwidth amounts to about 6.5 GHz for a mixer 0.112 μm long. These record-breaking characteristics are attributed to the improved contacts between a sensitive element and a helical antenna and are reached due to using the in situ deposition of NbN and Au layers at certain stages of the process.
|
Tret’yakov, I. V., Ryabchun, S. A., Kaurova, N. S., Larionov, P. A., Lobastova, A. A., Voronov, B. M., et al. (2010). Optimum absorbed heterodyne power for superconducting NbN hot-electron bolometer mixer. Tech. Phys. Lett., 36(12), 1103–1105.
Abstract: Absorbed heterodyne power has been measured in a low-noise broadband hot-electron bolometer (HEB) mixer for the terahertz range, operating on the effect of electron heating in the resistive state of an ultrathin superconducting NbN film. It is established that the optimum absorbed heterodyne power for the HEB mixer operating at 2.5 THz is about 100 nW.
|
Manova, N. N., Korneeva, Y. P., Korneev, A. A., Slysz, W., Voronov, B. M., & Gol'tsman, G. N. (2011). Superconducting NbN single-photon detector integrated with quarter-wave resonator. Tech. Phys. Lett., 37(5), 469–471.
Abstract: The spectral dependence of the quantum efficiency of superconducting NbN single-photon detectors integrated with quarter-wave resonators based on Si3N4, SiO2, and SiO layers has been studied.
|
Seleznev, V. A., Tarkhov, M. A., Voronov, B. M., Milostnaya, I. I., Lyakhno, V. Y., Garbuz, A. S., et al. (2008). Deposition and characterization of few-nanometers-thick superconducting Mo-Re films. Supercond. Sci. Technol., 21(11), 115006 (1 to 6).
Abstract: We report on the fabrication and investigation of few-nanometers-thick superconducting molybdenum-rhenium (Mo-Re) films intended for use in nanowire single-photon superconducting detectors (SSPDs). Mo-Re films were deposited on sapphire substrates by DC magnetron sputtering of an Mo(60)-Re(40) alloy target in an atmosphere of argon. The films 2-10 nm thick had critical temperatures (Tc) from 5.6 to 9.7 K. HRTEM (high-resolution transmission electron microscopy) analysis showed that the films had a homogeneous structure. XPS (x-ray photoelectron spectroscopy) analysis showed the Mo to Re atom ratio to be 0.575/0.425, oxygen concentration to be 10%, and concentration of other elements to be 1%.
|