Gerecht, E., Musante, C. F., Schuch, R., Lutz, C. R., Jr., Yngvesson, K. S., et al. (1995). Hot electron detection and mixing experiments in NbN at 119 micrometer wavelength. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 284–293).
Abstract: We have performed preliminary experiments with the goal of demonstrating a Hot Electron Bolometric (HEB) mixer for a 119 micrometer wavelength (2.5 THz). We have chosen a NbN device of size 700 x 350 micrometers. This device can easily be coupled to a laser LO source, which is advantageous for performing a prototype experiment. The relatively large size of the device means that the LO power required is in the mW range; this power can be easily obtained from a THz laser source. We have measured the amount of laser power actually absorbed in the device, and from this have estimated the best optical coupling loss to be about 10 di . We are developing methods for improving the optical coupling further. Preliminary measurements of the response of the device to a chopped black-body have not yet resulted in a measured receiver noise temperature. We expect to be able to complete this measurement in the near future.
|
|
|
|
Gol'tsman, G. N., Goghidze, I. G., Kouminov, P. B., Karasik, B. S., Semenov, A. D., & Gershenzon, E. M. (1994). Influence of grain boundary weak links on the nonequilibrium response of YBaCuO thin films to short laser pulses. J. Supercond., 7(4), 751–755.
Abstract: The transient voltage response in both epitaxial and granular YBaCuO thin films to 80 ps pulses of YAG∶Nd laser radiation of wavelength 0.63 and 1.54 μm was studied. In the normal and resistive states both types of films demonstrate two components: a nonequilibrium picosecond component and a bolometric nanosecond one. The normalized amplitudes are almost the same for all films. In the superconducting state we observed a kinetic inductive response and two-component shape after integration. The normalized amplitude of the response in granular films is up to five orders of magnitude larger than in epitaxial films. We interpret the nonequilibrium response in terms of a suppression of the order parameter by the excess of quasiparticles followed by the change of resistance in the normal and resistive states or kinetic inductance in the superconducting state. The sharp rise of inductive response in granular films is explained both by a diminishing of the cross section for current percolation through the disordered network of Josephson weak links and by a decrease of condensate density in neighboring regions.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B. S., et al. (1994). Nonequilibrium and bolometric photoresponse in patterned YBa2Cu3O7−δ thin films. J. Appl. Phys., 76(3), 1902–1909.
Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B., et al. (1994). A fast infrared detector based on patterned YBCO thin film. Supercond. Sci. Technol., 7(5), 321–323.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
|
|
|
Danerud, M., Winkler, D., Zorin, M., Trifonov, V., Karasik, B., Gershenzon, E. M., et al. (1993). Picosecond detection of infrared radiation with YBa2Cu3O7-δ thin films. In J. R. Birch, & T. J. Parker (Eds.), Proc. SPIE (Vol. 2104, pp. 183–184). Spie.
Abstract: Picosecond nonequilibrium and slow bolometric responses from a patterned high-Tc superconducting (HTS) film due toinfrared radiation were investigated using both modulation and pulse techniques. Measurements at A, = 0.85 [tm andA, = 10.6 lim have shown a similar behaviour of the response vs modulation frequency f. The responsivity of the HTS filmbased detector at f ..- 0.6-1 GHz is estimated to be 10-2 – 10-1 V/W.
|
|