Kerman, A. J., Dauler, E. A., Keicher, W. E., Yang, J. K. W., Berggren, K. K., Gol’tsman, G., et al. (2006). Kinetic-inductance-limited reset time of superconducting nanowire photon counters. Appl. Phys. Lett., 88(11), 111116 (1 to 3).
Abstract: We investigate the recovery of superconducting NbN-nanowire photon counters after detection of an optical pulse at a wavelength of 1550nm, and present a model that quantitatively accounts for our observations. The reset time is found to be limited by the large kinetic inductance of these nanowires, which forces a tradeoff between counting rate and either detection efficiency or active area. Devices of usable size and high detection efficiency are found to have reset times orders of magnitude longer than their intrinsic photoresponse time.
The authors acknowledge D. Oates and W. Oliver (MIT Lincoln Laboratory), S.W. Nam, A. Miller, and R. Hadfield (NIST) and R. Sobolewski, A. Pearlman, and A. Verevkin (University of Rochester) for helpful discussions and technical assistance. This work made use of MIT’s shared scanning-electron-beam-lithography facility in the Research Laboratory of Electronics. This work is sponsored by the United States Air Force under Air Force Contract No. FA8721-05-C-0002. Opinions, interpretations, recommendations and conclusions are those of the authors and are not necessarily endorsed by the United States Government.
|
Gershenzon, E. M., Gol'tsman, G. N., Multanovskii, V. V., & Ptitsina, N. G. (1983). Kinetics of electron and hole binding into excitons in germanium. Sov. Phys. JETP, 57(2), 369–376.
Abstract: The kinetics of binding of free carriers'into excitons under stationary and nonstationary conditions is studied by investigating the submillimeter photoconductivity of Ge in a wide range of temperatures and of excitation levels. It is shown that the absolute values and the temperature dependence of the binding cross section (o- T-'.' ) can be satisfactorily described by the cascade recombination theory. The value of o and its temperature dependence differ significantly from the cross sections, measured in the same manner, for capture by attracting small impurities. Under nonstationary conditions, just as in the case of recombination with shallow impurities, a signifi- cant role is played by the sticking of the carriers in highly excited states.
|
|
Gershenzon, E. M., Goltsman, G. N., Multanovskii, V. V., & Ptitsina, N. G. (1982). Kinetics of submillimeter impurity and exciton photoconduction in Ge. Optics and Spectroscopy, 52(4), 454–455.
|
Moshkova, M., Morozov, P., Divochiy, A., Vakhtomin, Y., & Smirnov, K. (2019). Large active area superconducting single photon detector. In J. Phys.: Conf. Ser. (Vol. 1410, 012139).
Abstract: We present development of large active area superconducting single-photon detectors well coupled with standard 50 μm-core multi-mode fiber. The sensitive area of the SSPD is patterned using the photon-number-resolving design and occupies an area of 40×40 μm2. Using this approach, we have obtained excellent specifications: system detection efficiency of 47% measured using a 900 nm laser and low dark count rate of 100 cps. The main advantages of the approach presented are a very short dead time of the detector of 22 ns and FWHM jitter value of about 130 ps.
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|