Ryabchun, S. A., Tretyakov, I. V., Finkel, M. I., Maslennikov, S. N., Kaurova, N. S., Seleznev, V. A., et al. (2008). Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In Proc. 19th Int. Symp. Space Terahertz Technol. (pp. 62–67). Groningen, Netherlands.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
Datesman, A. M., Schultz, J. C., Lichtenberger, A. W., Golish, D., Walker, C. K., & Kooi, J. (2005). Fabrication and characterization of niobium diffusion-cooled hot-electron bolometers on silicon nitride membranes. IEEE Trans. Appl. Supercond., 15(2), 928–931.
|
Gol’tsman, G., Okunev, O., Chulkova, G., Lipatov, A., Dzardanov, A., Smirnov, K., et al. (2001). Fabrication and properties of an ultrafast NbN hot-electron single-photon detector. IEEE Trans. Appl. Supercond., 11(1), 574–577.
Abstract: A new type of ultra-high-speed single-photon counter for visible and near-infrared wavebands based on an ultrathin NbN hot-electron photodetector (HEP) has been developed. The detector consists of a very narrow superconducting stripe, biased close to its critical current. An incoming photon absorbed by the stripe produces a resistive hotspot and causes an increase in the film’s supercurrent density above the critical value, leading to temporary formation of a resistive barrier across the device and an easily measurable voltage pulse. Our NbN HEP is an ultrafast (estimated response time is 30 ps; registered time, due to apparatus limitations, is 150 ps), frequency unselective device with very large intrinsic gain and negligible dark counts. We have observed sequences of output pulses, interpreted as single-photon events for very weak laser beams with wavelengths ranging from 0.5 /spl mu/m to 2.1 /spl mu/m and the signal-to-noise ratio of about 30 dB.
|
Yang, J. K. W., Dauler, E., Ferri, A., Pearlman, A., Verevkin, A., Gol’tsman, G., et al. (2005). Fabrication development for nanowire GHz-counting-rate single-photon detectors. IEEE Trans. Appl. Supercond., 15(2), 626–630.
Abstract: We have developed a fabrication process for GHz-counting-rate, single-photon, high-detection-efficiency, NbN, nanowire detectors. We have demonstrated two processes for the device patterning, one based on the standard polymethylmethacrylate (PMMA) organic positive-tone electron-beam resist, and the other based on the newer hydrogen silsesquioxane (HSQ) negative-tone spin-on-glass resist. The HSQ-based process is simple and robust, providing high resolution and the prospect of high fill-factors. Initial testing results show superconductivity in the films, and suggest that the devices exhibit photosensitivity.
|
Kawakami, A., Saito, S., & Hyodo, M. (2011). Fabrication of nano-antennas for superconducting Infrared detectors. IEEE Trans. Appl. Supercond., 21(3), 632–635.
Abstract: To improve the response performance of superconducting infrared detectors, we have developed a fabrication process for nano-antennas. A nano-antenna consists of a dipole antenna, and a superconducting thin film strip placed in the antenna's center. By measuring the transition temperature of the superconducting strips, we confirmed that their superconductivity maintained a good condition after the nano-antenna fabrication process. We also evaluated nano-antenna characteristics using Fourier transform infrared spectroscopy. The evaluated antenna length and width were respectively set at around 2400 nm and 400 nm, and the antennas were placed at intervals of several micrometers around the area of 1 mm2 . In an evaluation of spectral transmission characteristics, clear absorption caused by antenna effects was observed at around 1400 cm-1. High polarization dependencies were also observed.
|