Hübers, H. - W., Semenov, A., Schubert, J., Gol'tsman, G., Voronov, B., & Gershenzon, E. (2000). Performance of the phonon-cooled hot-electron bolometric mixer between 0.7 THz and 5.2 THz. In Proc. 8-th Int. Conf. on Terahertz Electronics (pp. 117–119).
Abstract: We report on the phonon cooled NbN hot electron bolometer as mixer in the terahertz frequency range. Its hybrid antenna consists of a hyperhemispheric silicon lens and a logarithmic-spiral feed antenna. Noise temperatures have been measured between 0.7 THz and 5.2 THz. A quarter wavelength layer of Parylene works as antireflection coating for the silicon lens and reduces the noise temperature by about 30. It was found that the antenna pattern at 2.5 THz is determined by the feed antenna and not by the diameter of the lens.
|
Rosfjord, K. M., Yang, J. K. W., Dauler, E. A., Kerman, A. J., Vikas Anant, Voronov, B. M., et al. (2006). Nanowire Single-photon detector with an integrated optical cavity and anti-reflection coating. Opt. Express, 14(2), 527–534.
Abstract: We have fabricated and tested superconducting single-photon detectors and demonstrated detection efficiencies of 57% at 1550-nm wavelength and 67% at 1064 nm. In addition to the peak detection efficiency, a median detection efficiency of 47.7% was measured over 132 devices at 1550 nm. These measurements were made at 1.8K, with each device biased to 97.5% of its critical current. The high detection efficiencies resulted from the addition of an optical cavity and anti-reflection coating to a nanowire photodetector, creating an integrated nanoelectrophotonic device with enhanced performance relative to the original device. Here, the testing apparatus and the fabrication process are presented. The detection efficiency of devices before and after the addition of optical elements is also reported.
|
Meledin, D., Pavolotsky, A., Desmaris, V., Lapkin, I., Risacher, C., Perez, V., et al. (2009). A 1.3-THz balanced waveguide HEB mixer for the APEX telescope. IEEE Trans. Microw. Theory Techn., 57(1), 89–98.
Abstract: In this paper, we report about the development, fabrication, and characterization of a balanced waveguide hot electron bolometer (HEB) receiver for the Atacama Pathfinder EXperiment telescope covering the frequency band of 1.25–1.39 THz. The receiver uses a quadrature balanced scheme and two HEB mixers, fabricated from 4- to 5-nm-thick NbN film deposited on crystalline quartz substrate with an MgO buffer layer in between. We employed a novel micromachining method to produce all-metal waveguide parts at submicrometer accuracy (the main-mode waveguide dimensions are 90×180 μm). We present details on the mixer design and measurement results, including receiver noise performance, stability and “first-light†at the telescope site. The receiver yields a double-sideband noise temperature averaged over the RF band below 1200 K, and outstanding stability with a spectroscopic Allan time more than 200 s.
|
Lobanov, Y., Shcherbatenko, M., Shurakov, A., Rodin, A. V., Klimchuk, A., Nadezhdinsky, A. I., et al. (2014). Heterodyne detection at near-infrared wavelengths with a superconducting NbN hot-electron bolometer mixer. Opt. Lett., 39(6), 1429–1432.
Abstract: We report on the development of a highly sensitive optical receiver for heterodyne IR spectroscopy at the communication wavelength of 1.5 μm (200 THz) by use of a superconducting hot-electron bolometer. The results are important for the resolution of narrow spectral molecular lines in the near-IR range for the study of astronomical objects, as well as for quantum optical tomography and fiber-optic sensing. Receiver configuration as well as fiber-to-detector light coupling designs are discussed. Light absorption of the superconducting detectors was enhanced by nano-optical antennas, which were coupled to optical fibers. An intermediate frequency (IF) bandwidth of about 3 GHz was found in agreement with measurements at 300 GHz, and a noise figure of about 25 dB was obtained that was only 10 dB above the quantum limit.
|
Gol'tsman, G. N., Vachtomin, Y. B., Antipov, S. V., Finkel, M. I., Maslennikov, S. N., Smirnov, K. V., et al. (2005). NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In Proc. SPIE (Vol. 5727, pp. 95–106).
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|