Svechnikov, S. I., Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Smirnov, K. V., Seleznev, V. A., et al. (2006). Superconducting hot electron bolometer mixer for middle IR range. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 686–687).
Abstract: The developed directly lens coupled hot electron bolometer (HEB) mixer was based on 5 nm superconducting NbN deposited on GaAs substrate. The layout of the structure, including 30x20 mcm^2 active area coupled with a 50 Ohm coplanar line, was patterned by photolithography. The responsivity of the mixer was measured in a direct detection mode in the 25-64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 mum wavelength CW CO2 laser was utilized as a local oscillator.
|
|
|
Vachtomin, Y. B., Antipov, S. V., Maslennikov, S. N., Smirnov, K. V., Polyakov, S. L., Zhang, W., et al. (2006). Quasioptical hot electron bolometer mixers based on thin NBN films for terahertz region. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 688–689).
Abstract: Presented in this paper are the performances of HEB mixers based on 2-3.5 nm thick NbN films integrated with log-periodic spiral antenna. Double side-band receiver noise temperature values are 1300 K and 3100 K at 2.5 THz and at 3.8 THz, respectively. Mixer gain bandwidth is 5.2 GHz. Local oscillator power is 1-3 muW for mixers with different active area
|
|
|
Вахтомин, Ю. Б., Антипов, С. В., Масленников, С. Н., Смирнов, К. В., Поляков, С. Л., Чжан, В., et al. (2006). Квазиоптические смесители терагерцового диапазона на основе эффекта разогрева электронов в тонких пленках NbN. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 688–689).
Abstract: Представлены результаты измерения рактеристик смесителей на эффекте разогрева электронов в тонких сверхпроводниковых пленках NbN. Смесители были изготовлены на основе пленок NbN толщиной 2-3.5 нм осажденных на кремниевую подложку с буферным подсло- ем MgO. Смесительный элемент согласовывался с планар- ной логопериодической спиральной антенной. Лучшее зна- чение шумовой температуры приемника на основе NbN смесителя составило 1300 К и 3100 К на частотах гетеро- дина 2.5 TГц и 3.8 ТГц, соответственно. Максимальное зна- чение полосы преобразования, измеренной на частоте 900 |Ц, достигло значения 5.2 ГГц для смесителя изготовлен- ного из NbN пленки толщиной 2 нм. Оптимальная мощность Представлены результаты измерения ха- гетеродинного источника составила 1-3 мкВт для смесите- лей с различным объемом смесительного элемента.
|
|
|
Smirnov, K., Korneev, A., Minaeva, O., Divochij, A., Rubtsova, I., Antipov, A., et al. (2006). Superconducting single-photon detector for near- and middle IR wavelength range. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 684–685).
Abstract: Presented in this paper are the results of research of NbN-film superconducting single-photon detector. At 2 K temperature, quantum efficiency in the visible light (0.56 mum) reaches 30-40 %. With the wavelength increase quantum efficiency decreases and comes to 20% at 1.55 mum and 0.02% at 5.6 mum. Minimum dark counts rate is 2times10-4s-1. The jitter of detector is 35 ps. The detector was successfully implemented for integrated circuits non-invasive optical testing. It is also perspective for quantum cryptography systems
|
|
|
Chulkova, G., Milostnaya, I., Korneev, A., Minaeva, O., Rubtsova, I., Voronov, B., et al. (2005). Superconducting nanostructures for counting of single photons in the infrared range. In Proc. 2-nd CAOL (Vol. 2, pp. 100–103).
Abstract: We present our studies on ultrafast superconducting single-photon detectors (SSPDs) based on ultrathin NbN nanostructures. Our SSPDs are patterned by electron beam lithography from 4-nm thick NbN film into meander-shaped strips covering square area of 10/spl times/10 /spl mu/m/sup 2/. The advances in the fabrication technology allowed us to produce highly uniform 100-120-nm-wide strips with meander filling factor close to 0.6. The detectors exploit a combined detection mechanism, where upon a single-photon absorption, an avalanche of excited hot electrons and the biasing supercurrent, jointly produce a picosecond voltage transient response across the superconducting nanostrip. The SSPDs are typically operated at 4.2 K, but they have shown that their sensitivity in the infrared radiation range can be significantly improved by lowering the operating temperature from 4.2 K to 2 K. When operated at 2 K, the SSPD quantum efficiency (QE) for visible light photons reaches 30-40%, which is the saturation value limited by optical absorption of our 4-nm-thick NbN film. For 1.55 /spl mu/m photons, QE was /spl sim/20% and decreases exponentially with the increase of the optical wavelength, but even at the wavelength of 6 /spl mu/m the detector remains sensitive to single photons and exhibits QE of about 10/sup -2/%. The dark (false) count rate at 2 K is as low as 2 /spl times/ 10/sup -4/ s/sup -1/, what makes our detector essentially a background-limited sensor. The very low dark-count rate results in the noise equivalent power (NEP) as low as 10/sup -18/ WHz/sup -1/2/ for the mid-infrared range (6 /spl mu/m). Further improvement of the SSPD performance in the mid-infrared range can be obtained by substituting NbN for the other, lower-T/sub c/ superconductors with the narrow superconducting gap and low quasiparticle diffusivity. The use of such materials will shift the cutoff wavelength towards the values even longer than 6 /spl mu/m.
|
|