Rönnung, F., Cherednichenko, S., Winkler, D., & Gol'tsman, G. N. (1999). A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond. Sci. Technol., 12(11), 853–855.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
Lindgren, M., Zorin, M. A., Trifonov, V., Danerud, M., Winkler, D., Karasik, B. S., et al. (1994). Optical mixing in a patterned YBa2Cu3O7-δ thin film. Appl. Phys. Lett., 65(26), 3398–3400.
Abstract: Mixing of 1.56 µm infrared radiation from two lasers in a high quality YBa2Cu3O7-δ thin film, patterned to parallel strips, was demonstrated. A mixer bandwidth of 18 GHz, limited by the measurement system, was obtained. A model based on nonequilibrium electron heating gives a good fit to the data and predicts an intrinsic mixer bandwidth in excess of 100 GHz, operating in the whole infrared spectrum. Reduction of bolometric effects and ways to decrease the conversion loss of the mixer is discussed. The minimum conversion loss is expected to be ~10 dB.
|
Trifonov, V. A., Karasik, B. S., Zorin, M. A., Gol’tsman, G. N., Gershenzon, E. M., Lindgren, M., et al. (1996). 9.6 μm wavelength mixing in a patterned YBa2Cu3O7‐δ thin film. Appl. Phys. Lett., 68(10), 1418–1420.
Abstract: Hot‐electron bolometric (HEB) mixing of 9.6 μm infrared radiation from two lasers in high‐quality YBa2Cu3O7−δ (YBCO) patterned thin film has been demonstrated. A heterodyne measurement showed an intermediate frequency (IF) bandwidth of 18 GHz, limited by our measurement system. An intrinsic limit of 100 GHz is predicted. Between 0.1 and 1 GHz intermediate frequency, temperature fluctuations with an equivalent output noise temperature Tfl up to ∼150 K, contributed to the mixer noise while Johnson noise dominated above 1 GHz. The overall conversion loss at 77 K at low intermediate frequencies was measured to be ∼25 dB, of which 13 dB was due to the coupling loss. The HEB mixer is very promising for use in heterodyne receivers within the whole infrared range.
|
Cherednichenko, S., Rönnung, F., Gol'tsman, G., Kollberg, E., & Winkler, D. (2000). YBa2Cu3O7−δ hot-electron bolometer mixer. Phys. C: Supercond., 341-348, 2653–2654.
Abstract: We present an investigation of hot-electron bolometric mixer based on YBa2Cu3O7−δ (YBCO) superconducting thin film. Mixer conversion loss, absorbed local oscillator power and intermediate frequency bandwidth was measured at the local oscillator frequency 600 GHz. The fabrication technique for nanoscale YBCO hot-electron bolometer (HEB) mixer integrated into planar antenna structure is described.
|
Karasik, B. S., Lindgren, M., Zorin, M. A., Danerud, M., Winkler, D., Trifonov, V. V., et al. (1994). Picosecond detection and broadband mixing of near-infrared radiation by YBaCuO films. In M. Nahum, & J. - C. Villegier (Eds.), Proc. SPIE (Vol. 2159, pp. 68–76). Spie.
Abstract: Nonequilibrium picosecond and bolometric responses of YBCO films 500 angstroms thick patterned into 20 X 20 micrometers 2 size structure to 17 ps laser pulses and modulated radiation of GaAs and CO2 lasers have been studied. The modulation frequencies up to 10 GHz for GaAs laser and up to 1 GHz for CO2 were attained. The use of small radiation power (1 – 10 mW/cm2 for cw radiation and 10 – 100 nJ/cm2 for pulse radiation) in combination with high sensitive read-out system made possible to avoid any non-linear transient processes caused by an overheating of sample above a critical temperature or S-N switching enhanced by an intense radiation. Responses due to the change of kinetic inductance were believed to be negligible. The only signals observed were caused by a small change of the film resistance either in the resistive state created by a bias current or in the normal state. The data obtained by means of pulse and modulation techniques are in agreement. The responsivity about 1 V/W was measured at 1 GHz modulation frequency both for 0.85 micrometers and 10.6 micrometers wavelengths. The sensitivity of high-Tc fast wideband infrared detector is discussed.
|