Korneev, A., Kouminov, P., Matvienko, V., Chulkova, G., Smirnov, K., Voronov, B., et al. (2004). Sensitivity and gigahertz counting performance of NbN superconducting single-photon detectors. Appl. Phys. Lett., 84(26), 5338–5340.
Abstract: We have measured the quantum efficiencysQEd, GHz counting rate, jitter, and noise-equivalentpowersNEPdof nanostructured NbN superconducting single-photon detectorssSSPDsdin thevisible to infrared radiation range. Our 3.5-nm-thick and 100- to 200-nm-wide meander-typedevices(total area 10310mm2), operating at 4.2 K, exhibit an experimental QE of up to 20% inthe visible range and,10% at 1.3 to 1.55mm wavelength and are potentially sensitive up tomidinfrareds,10mmdradiation. The SSPD counting rate was measured to be above 2 GHz withjitter,18 ps, independent of the wavelength. The devices’ NEP varies from,10−17W/Hz1/2for1.55mm photons to,10−20W/Hz1/2for visible radiation. Lowering the SSPD operatingtemperature to 2.3 K significantly enhanced its performance, by increasing the QE to,20% andlowering the NEP level to,3310−22W/Hz1/2, both measured at 1.26mm wavelength.
|
|
|
Gol'tsman, G. N., Kouminov, P., Goghidze, I., & Gershenzon, E. M. (1994). Nonequilibrium kinetic inductive response of YBaCuO thin films to low-power laser pulses. Phys. C: Supercond., 235-240, 1979–1980.
Abstract: Transient non-equilibrium kinetic inductive voltage response of YBaCuO thin films to 20 ps pulses of YAG:Nd laser radiation with 0.63 μm and 1.5 μm wavelength has been revealed. By increasing the sensitivity of 100 ps resolution time registration system and diminishing light intensity (fluence 0.1-1 μJ2/cm2) and transport current (density j≤105 A/cm2) we observed a perculiar bipolar signal form with nearly equal amplitudes of each sign. The integration of the kinetic inductive response over time gives the result which is qualitatively of the same form as the response in the resistive and normal states: nonequilibrium picosecond scale component followed by bolometric nanosecond. Nonequilibrium response is interpreted as suppression of order parameter by excess of quasiparticles followed by a change in resistance in the resistive state and kinetic inductance in superconductive state.
|
|
|
Goltsman, G., Korneev, A., Izbenko, V., Smirnov, K., Kouminov, P., Voronov, B., et al. (2004). Nano-structured superconducting single-photon detectors. Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment, 520(1-3), 527–529.
Abstract: NbN detectors, formed into meander-type, 10×10-μm2 area structures, based on ultrathin (down to 3.5-nm thickness) and nanometer-width (down to below 100 nm) NbN films are capable of efficiently detecting and counting single photons from the ultraviolet to near-infrared optical wavelength range. Our best devices exhibit QE >15% in the visible range and ∼10% in the 1.3–1.5-μm infrared telecommunication window. The noise equivalent power (NEP) ranges from ∼10−17 W/Hz1/2 at 1.5 μm radiation to ∼10−19 W/Hz1/2 at 0.56 μm, and the dark counts are over two orders of magnitude lower than in any semiconducting competitors. The intrinsic response time is estimated to be <30 ps. Such ultrafast detector response enables a very high, GHz-rate real-time counting of single photons. Already established applications of NbN photon counters are non-invasive testing and debugging of VLSI Si CMOS circuits and quantum communications.
|
|
|
Gol’tsman, G. N., Kouminov, P. B., Goghidze, I. G., Karasik, B. S., & Gershenzon, E. M. (1994). Nonbolometric and fast bolometric responses of YBaCuO thin films in superconducting, resistive, and normal states. In M. Nahum, & J. - C. Villegier (Eds.), Proc. SPIE (Vol. 2159, pp. 81–86). SPIE.
Abstract: The transient voltage response in both epitaxial and granular YBaCuO thin films to 20 ps pulses of YAG:Nd laser radiation with 0.63 micrometers and 1.54 micrometers was studied. In normal and resistive states both types of films demonstrate two components: nonequilibrium picosecond component and following bolometric nanosecond. The normalized amplitudes are almost the same for all films. In superconducting state we observed a kinetic inductive response and two-component shape after integration. The normalized amplitude of the response in granular films is up to several orders of magnitude larger than in epitaxial films. We interpret the nonequilibrium response in terms of a suppression of order parameter by the excess of quasiparticles followed by the change of resistance in normal and resistive states or kinetic inductance in superconducting state. The sharp rise of inductive response in granular films is explained both by a diminishing of the crossection for current percolation through the disordered network os Josephson weak links and by a decrease of condensate density in neighboring regions.
|
|
|
Verevkin, A. A., Pearlman, A., Slysz, W., Zhang, J., Sobolewski, R., Chulkova, G., et al. (2003). Ultrafast superconducting single-photon detectors for infrared wavelength quantum communications. In E. Donkor, A. R. Pirich, & H. E. Brandt (Eds.), Proc. SPIE (Vol. 5105, pp. 160–170). SPIE.
Abstract: We have developed a new class of superconducting single-photon detectors (SSPDs) for ultrafast counting of infrared (IR) photons for secure quantum communications. The devices are operated on the quantum detection mechanism, based on the photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconducting stripe. The detectors are fabricated from 3.5-nm-thick NbN films and they operate at 4.2 K inside a closed-cycle refrigerator or liquid helium cryostat. Various continuous and pulsed laser sources have been used in our experiments, enabling us to determine the detector experimental quantum efficiency (QE) in the photon-counting mode, response time, time jitter, and dark counts. Our 3.5-nm-thick SSPDs reached QE above 15% for visible light photons and 5% at 1.3 – 1.5 μm infrared range. The measured real-time counting rate was above 2 GHz and was limited by the read-out electronics (intrinsic response time is <30 ps). The measured jitter was <18 ps, and the dark counting rate was <0.01 per second. The measured noise equivalent power (NEP) is 2 x 10-18 W/Hz1/2 at λ = 1.3 μm. In near-infrared range, in terms of the counting rate, jitter, dark counts, and overall sensitivity, the NbN SSPDs significantly outperform their semiconductor counterparts. An ultrafast quantum cryptography communication technology based on SSPDs is proposed and discussed.
|
|
|
Sobolewski, R., Zhang, J., Slysz, W., Pearlman, A., Verevkin, A., Lipatov, A., et al. (2003). Ultrafast superconducting single-photon optical detectors. In J. Spigulis, J. Teteris, M. Ozolinsh, & A. Lusis (Eds.), Proc. SPIE (Vol. 5123, pp. 1–11). SPIE.
Abstract: We present a new class of single-photon devices for counting of both visible and infrared photons. Our superconducting single-photon detectors (SSPDs) are characterized by the intrinsic quantum efficiency (QE) reaching up to 100%, above 10 GHz counting rate, and negligible dark counts. The detection mechanism is based on the photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconducting stripe. The devices are fabricated from 3.5-nm-thick NbN films and operate at 4.2 K, well below the NbN superconducting transition temperature. Various continuous and pulsed laser sources in the wavelength range from 0.4 μm up to >3 μm were implemented in our experiments, enabling us to determine the detector QE in the photon-counting mode, response time, and jitter. For our best 3.5-nm-thick, 10×10 μm2-area devices, QE was found to reach almost 100% for any wavelength shorter than about 800 nm. For longer-wavelength (infrared) radiation, QE decreased exponentially with the photon wavelength increase. Time-resolved measurements of our SSPDs showed that the system-limited detector response pulse width was below 150 ps. The system jitter was measured to be 35 ps. In terms of the counting rate, jitter, and dark counts, the NbN SSPDs significantly outperform their semiconductor counterparts. Already identifeid and implemented applications of our devices range from noninvasive testing of semiconductor VLSI circuits to free-space quantum communications and quantum cryptography.
|
|
|
Slysz, W., Wegrzecki, M., Bar, J., Grabiec, P., Górska, M., Latta, C., et al. (2005). Fiber-coupled quantum-communications receiver based on two NbN superconducting single-photon detectors. In A. Rogalski, E. L. Dereniak, & F. F. Sizov (Eds.), Proc. SPIE (Vol. 5957, 59571K (1 to 10)). SPIE.
Abstract: We present the design and performance of a novel, two-channel single-photon receiver, based on two fiber-coupled NbN superconducting single-photon detectors (SSPDs). The SSPDs are nanostructured superconducting meanders covering an area of 100 μm2 and are known for ultrafast and efficient counting of single, visible-to-infrared photons. Their operation has been explained within a phenomenological hot-electron photoresponse model. Our receiver is intended for fiber-based quantum cryptography and communication systems, operational at near-infrared (NIR) telecommunication wavelengths, λ = 1.3 μm and λ = 1.55 μm. Coupling between the NbN detector and a single-mode optical fiber was achieved using a specially designed, micromechanical photoresist ring, positioned directly over the SSPD active area. The positioning accuracy of the ring was below 1 μm. The receiver with SSPDs was placed (immersed) in a standard liquid-helium transport Dewar and kept without interruption for over two months at 4.2 K. At the same time, the optical fiber inputs and electrical outputs were kept at room temperature. Our best system reached a system quantum efficiency of up to 0.3 % in the NIR radiation range, with the detector coupling efficiency of about 30 %. The response time was measured to be about 250 ps and was limited by our read-out electronics. The measured jitter was close to 35 ps. The presented performance parameters show that our NIR single photon detectors are suitable for practical quantum cryptography and for applications in quantum-correlation experiments.
|
|