Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gogidze, I. G., Gusev, Y. P., Zorin, M. A., et al. (1992). Picosecond range detector base on superconducting niobium nitride film sensitive to radiation in spectral range from millimeter waves up to visible light. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(5), 955–960.
Abstract: Fast-operating picosecond detector of electromagnetical radiation is developed on the basis of fine superconducting film of niobium nitride with high sensitivity within spectral range from millimetric waves up to visible light. Detector sensitive element represents structure covering narrow parallel strips with micron sizes included in the rupture of microstrip line. Detecting ability of the detector and time constant measured using amplitude-simulated radiation of reverse wave tubes and pulse radiation of picosecond gas and solid-body lasers, constitute D*≅1010 W-1·cm·Hz-1/2 and τ≤5 ps respectively, at 10 K temperature. The expected value of time constant of the detector at 10 K obtained via extrapolation of directly measured dependence that is, τ ∝ τ-1, constitutes 20 ps. Experimental data demonstrate that detection mechanism is linked with electron heating effect.
|
Budyanskij, M. Y., Sejdman, L. A., Voronov, B. M., & Gubkina, T. O. (1992). Increase of reproducibility in production of superconducting thin films of niobium nitride. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(10), 1950–1954.
Abstract: Technique to control the composition of gas medium in the reactive magnetron discharge and the composition of the deposited films of niobium nitride using electrical parameters of discharge only, in particular, by δU = Up – Uar value at contant stabilized discharge current is described. Technique to select optimal condition for deposition of niobium nitride films when the films have composition meeting chemical formula, is suggested. Thin films of niobium nitride with up to 7 nm thickness and with rather high temperature of transition into superconducting state Tk > 10 K) and with low width of transition (δ < 0.6 K), are obtained. It is determined, that substrate material and dielectric sublayer do not affect. Tk value, while difference in coefficients of thermal expansion of substrate and of film affects δTk value.
|
Dzardanov, A., Ekstrom, H., Gershenzon, E., Gol'tsman, G., Jacobsson, S., Karasik, B., et al. (1994). Hot-electron superconducting mixers for 20-500 GHz operation. In Proc. Int. Conf. on Millimeter and Submillimeter Waves and Appl. (Vol. 2250, pp. 276–278).
Abstract: Bolometdcmucers based on Nb and NbN superconducting thin films in the resistive state have been prepared for 20, 100 GHz and 350-500 GHz operation. The mixing mechanism is presumably of electron heating origin. Our measurements indicate that a conversion loss of about 6-8 dB can rather easily be achieved, and that the noise is reasonably low. The requirements on the operation mode and on the film parameters in order to obtain small conversion losses or even gain are discussed. For NbN films the availability of nearly 1 GHz IF bandwidth is experimentally demonstrated. NbN hot-electron mucers combined with slot-line tapered antenna on Si membrane or with double-dipole antenna on SiO^ substrate have been fabricated. The devices we study are considered to be very promising for use in heterodyne receivers from microwaves to terahertz frequencies.
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gubkina, T. O., & Semash, V. D. (1994). Superconductive properties of ultrathin NbN films on different substrates. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 7(6), 1097–1102.
Abstract: A study was made on dependence of surface resistance, critical temperature and width of superconducting transition on application temperature and thickness of NbN films, which varied within the range of 3-10 nm. Plates of sapphire, fused and monocrystalline quartz, MgO, as well as Si and silicon oxide were used as substrates. NbN films with 160 μθ·cm specific resistance and 16.5 K (Tc) critical temperature were obtained on sapphire substrates. Intensive growth of ΔTc was noted for films, applied on fused quartz, with increase of precipitation temperature. This is explained by occurrence of high tensile stresses in NbN films, caused by sufficient difference of thermal coefficients of expansion of NbN and quartz.
|
Karasik, B. S., Gol'tsman, G. N., Voronov, B. M., Svechnikov, S. I., Gershenzon, E. M., Ekstrom, H., et al. (1995). Hot electron quasioptical NbN superconducting mixer. IEEE Trans. Appl. Supercond., 5(2), 2232–2235.
Abstract: Hot electron superconductor mixer devices made of thin NbN films on SiO/sub 2/-Si/sub 3/N/sub 4/-Si membrane have been fabricated for 300-350 GHz operation. The device consists of 5-10 parallel strips each 5 /spl mu/m long by 1 /spl mu/m wide which are coupled to a tapered slot-line antenna. The I-V characteristics and position of optimum bias point were studied in the temperature range 4.5-8 K. The performance of the mixer at higher temperatures is closer to that predicted by theory for uniform electron heating. The intermediate frequency bandwidth versus bias has also been investigated. At the operating temperature 4.2 K a bandwidth as wide as 0.8 GHz has been measured for a mixer made of 6 nm thick film. The bandwidth tends to increase with operating temperature. The performance of the NbN mixer is expected to be better for higher frequencies where the absorption of radiation should be more uniform.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., & Voronov, B. (1995). NbN hot-electron mixer measurements at 200 GHz. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 254–261).
Abstract: We present noise and gain measurements of resistively driven NbN hot-electron mixers near 200 GHz. The device geometry is chosen so that the dominant cooling process of the hot-electrons is their interaction with the lattice. Except for a single batch, the intermediate frequency cut-off of these mixer elements is – 3 700 MHz, and has shown little variation among other batches of devices. At 100 MHz we measured intrinsic mixer losses as low as —3 dB. We measured the noise temperatures at several intermediate frequencies, and for the best de- vice at 137 MHz with 20 MHz bandwidth, we measured 2000 K; using a low-noise first- stage amplifier at 1.5 GHz with 200 MHz bandwidth, the receiver noise temperature measured 2800 K. We estimate that the noise contribution from the mixer is 500 K and the total losses are —15 dB at 137 MHz.
|
Gerecht, E., Musante, C. F., Schuch, R., Lutz, C. R., Jr., Yngvesson, K. S., et al. (1995). Hot electron detection and mixing experiments in NbN at 119 micrometer wavelength. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 284–293).
Abstract: We have performed preliminary experiments with the goal of demonstrating a Hot Electron Bolometric (HEB) mixer for a 119 micrometer wavelength (2.5 THz). We have chosen a NbN device of size 700 x 350 micrometers. This device can easily be coupled to a laser LO source, which is advantageous for performing a prototype experiment. The relatively large size of the device means that the LO power required is in the mW range; this power can be easily obtained from a THz laser source. We have measured the amount of laser power actually absorbed in the device, and from this have estimated the best optical coupling loss to be about 10 di . We are developing methods for improving the optical coupling further. Preliminary measurements of the response of the device to a chopped black-body have not yet resulted in a measured receiver noise temperature. We expect to be able to complete this measurement in the near future.
|
Yagubov, P., Gol'tsman, G., Voronov, B., Seidman, L., Siomash, V., Cherednichenko, S., et al. (1996). The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 290–302). Charlottesville, Virginia, USA.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
Ekström, H., Kroug, M., Belitsky, V., Kollberg, E., Olsson, H., Goltsman, G., et al. (1996). Hot electron mixers for THz applications. In E. J. Rolfe, & G. Pilbratt (Eds.), Proc. 30th ESLAB (pp. 207–210).
Abstract: We have measured the noise performance of 35 A thin NbN HEB devices integrated with spiral antennas on antireflection coated silicon substrate lenses at 620 GHz. From the noise measurements we have determined a total conversion gain of the receiver of—16 dB, and an intrinsic conversion of about-10 dB. The IF bandwidth of the 35 A thick NbN devices is at least 3 GHz. The DSB receiver noise temperature is less than 1450 K. Without mismatch losses, which is possible to obtain with a shorter device, and with reduced loss from the beamsplitter, we expect to achieve a DSB receiver noise temperature of less ‘than 700 K.
|
Kawamura, J., Blundell, R., Tong, C. ‐yu E., Gol’tsman, G., Gershenzon, E., & Voronov, B. (1996). Performance of NbN lattice‐cooled hot‐electron bolometric mixers. J. Appl. Phys., 80(7), 4232–4234.
Abstract: The heterodyne performance of lattice‐cooled hot‐electron bolometric mixers is measured at 200 GHz. Superconducting thin‐film niobium nitride strips with ∼5 nm thickness are used as waveguide mixer elements. A double‐sideband receiver noise temperature of 750 K at 244 GHz is measured at an intermediate frequency centered at 1.5 GHz with 500 MHz bandwidth and with 4.2 K device temperature. The instantaneous bandwidth for this mixer is 1.6 GHz. The local oscillator power required by the mixer is about 0.5 μW. The mixer is linear to within 1 dB up to an input power level 6 dB below the local oscillator power. A receiver incorporating a hot‐electron bolometric mixer was used to detect molecular line emission in a laboratory gascell. This experiment unambiguously confirms that the receiver noise temperature determined from Y‐factor measurements reflects the true heterodyne sensitivity.
|
Semenov, A. D., Gousev, Y. P., Nebosis, R. S., Renk, K. F., Yagoubov, P., Voronov, B. M., et al. (1996). Heterodyne detection of THz radiation with a superconducting hot‐electron bolometer mixer. Appl. Phys. Lett., 69(2), 260–262.
Abstract: We report on the use of a superconducting hot‐electron bolometer mixer for heterodyne detection of terahertz radiation. Radiation with a wavelength of 119 μm was coupled to the mixer, a NbN microbridge, by a hybrid quasioptical antenna consisting of an extended hyperhemispherical lens and a planar logarithmic spiral antenna. We found, at an intermediate frequency of 1.5 GHz, a system double side band noise temperature of ≊40 000 K and conversion losses of 25 dB. We also discuss the possibilities of further improvement of the mixer performance.
|
Yagoubov, P., Gol'tsman, G., Voronov, B., Svechnikov, S., Cherednichenko, S., Gershenzon, E., et al. (1996). Quasioptical phonon-cooled NbN hot-electron bolometer mixer at THz frequencies. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 303–317).
Abstract: In our experiments we tested phonon-cooled hot-electron bolometer (HEB) quasioptical mixer based on spiral antenna designed for 0.5-1.2 THz frequency band and fabricated on sapphire, Si-coated sapphire and high resistivity silicon substrates. HEB devices were produced from thin superconducting NbN film 3.5-6 nm thick with the critical temperature of about 11-12 K. For these devices we achieved the receiver noise temperature T R (DSB) = 3000 K in the 500-700 GHz frequency range and an IF bandwidth of 3-4 GHz. Prelimanary measurements at frequencies 1-1.2 THz resulted the receiver noise temperature about 9000 K (DSB).
|
Gerecht, E., Musante, C. F., Wang, Z., Yngvesson, K. S., Mueller, E. R., Waldman, J., et al. (1996). Optimization of hot eleciron bolometer mixing efficiency in NbN at 119 micrometer wavelength. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 584–600).
Abstract: We describe an investigation of a NbN HEB mixer for 2.5 THz. An intrinsic conversion loss of 23 dB has been measured with a two-laser measurement technique. The conversion loss was limited by the LO power available and is expected to decrease to 10 dB or less when sufficient LO power is available. For this initial experiment we used a prototype device which is directly coupled to the laser beams. We present results for a back-short technique that improves the optical coupling to the device and describe our progress for an antenna-coupled device with a smaller dimension. Based on our measured data for conversion loss and device output noise level, we predict that NbN HEB mixers will be capable of achieving DSB receiver noise temperatures of ten times the quantum noise limit in the THz range.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 23–28).
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
Semenov, A. D., Gousev, Y. P., Renk, K. F., Voronov, B. M., Gol'tsman, G. N., Gershenzon, E. M., et al. (1997). Noise characteristics of a NbN hot-electron mixer at 2.5 THz. IEEE Trans. Appl. Supercond., 7(2), 3572–3575.
Abstract: The noise temperature of a NbN phonon cooled hot-electron mixer has been measured at a frequency of 2.5 THz for various operating conditions. We obtained for optimal operation a double sideband mixer noise temperature of /spl ap/14000 K and a system conversion loss of /spl ap/23 dB at intermediate frequencies up to 1 GHz. The dependences of the mixer noise temperature on the bias voltage, local oscillator power, and intermediate frequency were consistent with the phenomenological description based on the effective temperature approximation.
|