Abstract: The authors have investigated the photoinduced voltage response of a current-carrying structured YBa₂Cu₃O_7-δ thin film to ultrashort far-infrared (FIR) laser pulses in the frequency range from 0.7 THz to 7 THz. The detector has shown an almost constant sensitivity of 1 mV/W and a noise equivalent power of less than 5*10/sup -7/ W/ square root Hz. The temperature dependence of the decay time of the detector signal was studied for temperatures around the transition temperature of the film ( approximately 80 K). For a detector temperature where dR/dT had its maximum, the authors observed bolometric signals with decay times of about 2 ns, and for lower temperatures they observed nonbolometric signals with decay times of approximately 120 ps; the duration of the nonbolometric signals was limited by the time resolution of the electronic registration equipment.

Abstract: We investigated the temperature dependence of the transient voltage photoresponse of a current biased structured YBa2Cu3O7−δ thin film in its transition temperature region, around 79 K. Both, picosecond nonbolometric and nanosecond bolometric response to ultrashort far-infrared laser pulses were found for frequencies between 25 cm−1 and 215 cm−1. We will discuss optimum conditions for radiation detection and present an analysis of the dynamical behaviour of excited high T c thin films.

Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.

Abstract: Thin YBa2Cu3O7−δ laser deposited films were patterned into devices consisting of ten parallel 1 μm wide strips. Nonequilibrium picosecond and bolometric photoresponses were studied by the use of 17 ps full width at half‐maximum laser pulses and amplitude modulated radiation from an AlGaAs laser up to 10 GHz and from a CO2 laser up to 1 GHz. The time and frequency domain measurements were in agreement. The fast response can be explained by electron heating. The use of low optical power and a sensitive measurement system excluded any nonlinear transient processes and kinetic inductance changes in the superconducting state. At 1 GHz modulation frequency, the responsivity was ∼1.2 V/W both for 0.8 and 10.6 μm wavelengths. The sensitivity of a fast and spectrally broadband infrared detector is discussed.