Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Lubenchenko, A. V., Morozov, P. V., Shurkaeva, I. V., et al. (2018). Influence of sputtering parameters on the main characteristics of ultra-thin vanadium nitride films. In J. Phys.: Conf. Ser. (Vol. 1124, 051030).
Abstract: We researched the relation between deposition and ultra-thin VN films parameters. To conduct the experimental study we varied substrate temperature, Ar and N2 partial pressures and deposition rate. The study allowed us to obtain the films with close to the bulk values transition temperatures and implement such samples in order to fabricate superconducting single-photon detectors.
|
|
|
Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
|
|
Matyushkin, Y. E., Gayduchenko, I. A., Moskotin, M. V., Goltsman, G. N., Fedorov, G. E., Rybin, M. G., et al. (2018). Graphene-layer and graphene-nanoribbon FETs as THz detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051054).
Abstract: We report on detection of sub-THz radiation (129-430 GHz) using graphene based asymmetric field-effect transistor (FET) structures with different channel geometry: monolayer graphene, graphene nanoribbons. In all devices types we observed the similar trends of response on sub-THz radiation. The response fell with increasing frequency at room temperature, but increased with increasing frequency at 77 K. Our calculations show that the change in the trend of the frequency dependence at 77 K is associated with the appearance of plasma waves in the graphene channel. Unusual properties of p-n junctions in graphene are highlighted using devices of special geometry.
|
|
|
Moskotin, M. V., Gayduchenko, I. A., Goltsman, G. N., Titova, N., Voronov, B. M., Fedorov, G. F., et al. (2018). Bolometric effect for detection of sub-THz radiation with devices based on carbon nanotubes. In J. Phys.: Conf. Ser. (Vol. 1124, 051050 (1 to 5)).
Abstract: In this work we investigate the response on THz radiation of a FET device based on an individual carbon nanotube conductance channel. It was already shown, that the response of such devices can be either of diode rectification origin or of thermoelectric effect origin or of their combination. In this work we demonstrate that at 77K and 8K temperatures strong bolometric effect also makes a significant contribution to the response.
|
|
|
Gayduchenko, I., Fedorov, G., Titova, N., Moskotin, M., Obraztsova, E., Rybin, M., et al. (2018). Towards to the development of THz detectors based on carbon nanostructures. In J. Phys.: Conf. Ser. (Vol. 1092, 012039 (1 to 4)).
Abstract: Demand for efficient terahertz radiation detectors resulted in intensive study of the carbon nanostructures as possible solution for that problem. In this work we investigate the response to sub-terahertz radiation of detectors with sensor elements based on CVD graphene as well as its derivatives – carbon nanotubes (CNTs). The devices are made in configuration of field effect transistors (FET) with asymmetric source and drain (vanadium and gold) contacts and operate as lateral Schottky diodes. We show that at 300K semiconducting CNTs show better performance up to 300GHz with responsivity up to 100V/W, while quasi-metallic CNTs are shown to operate up to 2.5THz. At 300 K graphene detector exhibit the room-temperature responsivity from R = 15 V/W at f = 129 GHz to R = 3 V/W at f = 450 GHz. We find that at low temperatures (77K) the graphene lateral Schottky diodes responsivity rises with the increasing frequency of the incident sub-THz radiation. We interpret this result as a manifestation of a plasmonic effect in the devices with the relatively long plasmonic wavelengths. The obtained data allows for determination of the most promising directions of development of the technology of nanocarbon structures for the detection of THz radiation.
|
|
|
Kovalyuk, V., Ferrari, S., Kahl, O., Semenov, A., Lobanov, Y., Shcherbatenko, M., et al. (2017). Waveguide integrated superconducting single-photon detector for on-chip quantum and spectral photonic application. In J. Phys.: Conf. Ser. (Vol. 917, 062032).
Abstract: With use of the travelling-wave geometry approach, integrated superconductor- nanophotonic devices based on silicon nitride nanophotonic waveguide with a superconducting NbN-nanowire suited on top of the waveguide were fabricated. NbN-nanowire was operated as a single-photon counting detector with up to 92 % on-chip detection efficiency in the coherent mode, serving as a highly sensitive IR heterodyne mixer with spectral resolution (f/df) greater than 106 in C-band at 1550 nm wavelength
|
|
|
Zubkova, E., An, P., Kovalyuk, V., Korneev, A., Ferrari, S., Pernice, W., et al. (2017). Integrated Bragg waveguides as an efficient optical notch filter on silicon nitride platform. In J. Phys.: Conf. Ser. (Vol. 917, 062042).
Abstract: We modeled and fabricated integrated optical Bragg waveguides on a silicon nitride (Si3N4) platform. These waveguides would serve as efficient notch-filters with the desired characteristics. Transmission spectra of the fabricated integrated notch filters have been measured and attenuation at the desired wavelength of 1550 nm down to -43 dB was observed. Performance of the filters has been studied depending on different parameters, such as pitch, filling factor, and height of teeth of the Bragg grating
|
|
|
Chuprina, I. N., An, P. P., Zubkova, E. G., Kovalyuk, V. V., Kalachev, A. A., & Gol'tsman, G. N. (2017). Optimisation of spontaneous four-wave mixing in a ring microcavity. In J. Phys.: Conf. Ser. (Vol. 47, pp. 887–891).
Abstract: Abstract. A theory of spontaneous four-wave mixing in a ring microcavity is developed. The rate of emission of biphotons for pulsed and monochromatic pumping with allowance for the disper- sion of group velocities is analytically calculated. In the first case, pulses in the form of an increasing exponential are considered, which are optimal for excitation of an individual resonator mode. The behaviour of the group velocity dispersion as a function of the width and height of the waveguide is studied for a specific case of a ring microcavity made of silicon nitride. The results of the numeri- cal calculation are in good agreement with the experimental data. The ring microcavity is made of two types of waveguides: com- pletely etched and half etched. It is found that the latter allow for better control over the parameters in the manufacturing process, making them more predictable.
|
|
|
Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Morozov, P. V., Seleznev, V. A., & Smirnov, K. V. (2017). Development of high-effective superconducting single-photon detectors aimed for mid-IR spectrum range. In J. Phys.: Conf. Ser. (Vol. 917, 062037).
Abstract: We report on development of superconducting single-photon detectors (SSPD) with high intrinsic quantum efficiency in the wavelength range 1.31 – 3.3 μm. By optimization of the NbN film thickness and its compound, we managed to improve detection efficiency of the detectors in the range up to 3.3 μm. Optimized devices showed intrinsic quantum efficiencies as high as 10% at mid-IR range.
|
|
|
Seleznev, V. A., Divochiy, A. V., Vakhtomin, Y. B., Morozov, P. V., Zolotov, P. I., Vasil'ev, D. D., et al. (2016). Superconducting detector of IR single-photons based on thin WSi films. In J. Phys.: Conf. Ser. (Vol. 737, 012032).
Abstract: We have developed the deposition technology of WSi thin films 4 to 9 nm thick with high temperature values of superconducting transition (Tc~4 K). Based on deposed films there were produced nanostructures with indicative planar sizes ~100 nm, and the research revealed that even on nanoscale the films possess of high critical temperature values of the superconducting transition (Tc~3.3-3.7 K) which certifies high quality and homogeneity of the films created. The first experiments on creating superconducting single-photon detectors showed that the detectors' SDE (system detection efficiency) with increasing bias current (I b) reaches a constant value of ~30% (for X=1.55 micron) defined by infrared radiation absorption by the superconducting structure. To enhance radiation absorption by the superconductor there were created detectors with cavity structures which demonstrated a practically constant value of quantum efficiency >65% for bias currents Ib>0.6-Ic. The minimal dark counts level (DC) made 1 s-1 limited with background noise. Hence WSi is the most promising material for creating single-photon detectors with record SDE/DC ratio and noise equivalent power (NEP).
|
|