Rosfjord, K. M., Yang, J. K. W., Dauler, E. A., Kerman, A. J., Vikas Anant, Voronov, B. M., et al. (2006). Nanowire Single-photon detector with an integrated optical cavity and anti-reflection coating. Opt. Express, 14(2), 527–534.
Abstract: We have fabricated and tested superconducting single-photon detectors and demonstrated detection efficiencies of 57% at 1550-nm wavelength and 67% at 1064 nm. In addition to the peak detection efficiency, a median detection efficiency of 47.7% was measured over 132 devices at 1550 nm. These measurements were made at 1.8K, with each device biased to 97.5% of its critical current. The high detection efficiencies resulted from the addition of an optical cavity and anti-reflection coating to a nanowire photodetector, creating an integrated nanoelectrophotonic device with enhanced performance relative to the original device. Here, the testing apparatus and the fabrication process are presented. The detection efficiency of devices before and after the addition of optical elements is also reported.
|
Jiang, L., Miao, W., Zhang, W., Li, N., Lin, Z. H., Yao, Q. J., et al. (2006). Characterization of quasi-optical NbN phonon-cooled superconducting HEB mixers. In Proc. 17th Int. Symp. Space Terahertz Technol. (pp. 55–58).
Abstract: In this paper, we thoroughly investigate the performance of quasi-optical NbN phonon-cooled superconducting hot-electron bolometer (HEB) mixers, cryogenically cooled by a close-cycled 4-K refrigerator at 500 GI-1z and 850 GHz. The uncorrected lowest receiver noise Abstract---In temperatures measured are 800 K at 500 CHz without anti-reflection coating, and 1000 K @ 850 GHz with a 50 11M thick Mylar anti-reflection coating. The dependence of receiver noise temperature on the critical current and bath temperature of HEB mixer is also investigated here. Lifetime of quasi-optical superconducting NbN HEB mixers of different volumes, room temperature resistances, and critical temperatures are thoroughly studied. Increased room temperature resistance with time over the initial resistance changes between 1 and 1.2, and the reduced critical current with time over the initial value fluctuates slightly around 0.7 for most HEB mixers even of different volumes, room temperature resistances, and critical temperatures. The critical current degrades sharply vvhile room temperature resistance varies over 1.25.
|
Lobanov, Y., Shcherbatenko, M., Shurakov, A., Rodin, A. V., Klimchuk, A., Nadezhdinsky, A. I., et al. (2014). Heterodyne detection at near-infrared wavelengths with a superconducting NbN hot-electron bolometer mixer. Opt. Lett., 39(6), 1429–1432.
Abstract: We report on the development of a highly sensitive optical receiver for heterodyne IR spectroscopy at the communication wavelength of 1.5 μm (200 THz) by use of a superconducting hot-electron bolometer. The results are important for the resolution of narrow spectral molecular lines in the near-IR range for the study of astronomical objects, as well as for quantum optical tomography and fiber-optic sensing. Receiver configuration as well as fiber-to-detector light coupling designs are discussed. Light absorption of the superconducting detectors was enhanced by nano-optical antennas, which were coupled to optical fibers. An intermediate frequency (IF) bandwidth of about 3 GHz was found in agreement with measurements at 300 GHz, and a noise figure of about 25 dB was obtained that was only 10 dB above the quantum limit.
|
Shcherbatenko, M., Lobanov, Y., Benderov, O., Shurakov, A., Ignatov, A., Titova, N., et al. (2015). Antenna-coupled 30 THz hot electron bolometer mixers. In Proc. 26th Int. Symp. Space Terahertz Technol. (27).
Abstract: We report on design and characterization of a superconducting Hot Electron Bolometer Mixer integrated with a logarithmic spiral antenna for mid-IR range observations. The antenna parameters have been adjusted to achieve the ultimate performance at 10 µm (30 THz) range where O3, NH3, CO2, CH4, N2O,…. lines in the Earth’s atmosphere, in planetary atmospheres and in the interstellar space can be observed. The HEB mixer is made of a thin NbN film deposited onto a GaAs substrate. To couple the radiation we rely on the quasioptical approach: the device is glued to a semi-spherical germanium lens with diameter~ 3 mm. A wet cryostat equipped with a germanium window and narrow band-pass filter is used to characterize the antenna and estimate the mixer performance.
|