Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 23–28).
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
Ekstörm, H., Kollberg, E., Yagoubov, P., Gol'tsman, G., Gershenzon, E., & Yngvesson, S. (1997). Gain and noise bandwidth of NbN hot-electron bolometric mixers. Appl. Phys. Lett., 70(24), 3296–3298.
Abstract: We have measured the noise performance and gain bandwidth of 35 Å thin NbN hot-electron mixers integrated with spiral antennas on silicon substrate lenses at 620 GHz. The best double-sideband receiver noise temperature is less than 1300 K with a 3 dB bandwidth of ≈5 GHz. The gain bandwidth is 3.2 GHz. The mixer output noise dominated by thermal fluctuations is 50 K, and the intrinsic conversion gain is about −12 dB. Without mismatch losses and excluding the loss from the beamsplitter, we expect to achieve a receiver noise temperature of less than 700 K.
|
Cherednichenko, S., Yagoubov, P., Il'in, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers. In Proc. 27th Eur. Microwave Conf. (Vol. 2, pp. 972–977). IEEE.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 nm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 um wide and 2 um long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.2 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
Gousev, Y. P., Semenov, A. D., Goghidze, I. G., Pechen, E. V., Varlashkin, A. V., Gol'tsman, G. N., et al. (1997). Current dependent noise in a YBa2Cu3O7-δ hot-electron bolometer. IEEE Trans. Appl. Supercond., 7(2), 3556–3559.
Abstract: We investigated the output noise of a YBa2Cu3O7-δ (YBCO) superconducting hot-electron bolometer (HEB) in a large frequency range (10 kHz to 8 GHz); the bolometer either consisted of a structured 50 nm thick YBCO film on LaAlO/sub 3/ or a 30 nm thick film on a MgO substrate. We found that flicker noise dominated at low frequencies (below 1 MHz), while at higher frequencies Johnson noise and a current dependent noise were the main noise sources.
|
Semenov, A. D., Gousev, Y. P., Renk, K. F., Voronov, B. M., Gol'tsman, G. N., Gershenzon, E. M., et al. (1997). Noise characteristics of a NbN hot-electron mixer at 2.5 THz. IEEE Trans. Appl. Supercond., 7(2), 3572–3575.
Abstract: The noise temperature of a NbN phonon cooled hot-electron mixer has been measured at a frequency of 2.5 THz for various operating conditions. We obtained for optimal operation a double sideband mixer noise temperature of /spl ap/14000 K and a system conversion loss of /spl ap/23 dB at intermediate frequencies up to 1 GHz. The dependences of the mixer noise temperature on the bias voltage, local oscillator power, and intermediate frequency were consistent with the phenomenological description based on the effective temperature approximation.
|
Svechnikov, S. I., Okunev, O. V., Yagoubov, P. A., Gol'tsman, G. N., Voronov, B. M., Cherednichenko, S. I., et al. (1997). 2.5 THz NbN hot electron mixer with integrated tapered slot antenna. IEEE Trans. Appl. Supercond., 7(2), 3548–3551.
Abstract: A Hot Electron Bolometer (HEB) mixer for 2.5 THz utilizing a NbN thin film device, integrated with a Broken Linearly Tapered Slot Antenna (BLTSA), has been fabricated and is presently being tested. The NbN HEB device and the antenna were fabricated on a SiO2membrane. A 0.5 micrometer thick SiO2layer was grown by rf magnetron reactive sputtering on a GaAs wafer. The HEB device (phonon-cooled type) was produced as several parallel strips, 1 micrometer wide, from an ultrathin NbN film 4-7 nm thick, that was deposited onto the SiO2layer by dc magnetron reactive sputtering. The BLTSA was photoetched in a multilayer Ti-Au metallization. In order to strengthen the membrane, the front-side of the wafer was coated with a 5 micrometer thick polyimide layer just before the membrane formation. The last operation was anisotropic etching of the GaAs in a mixture of HNO3and H2O2.
|
Svechnikov, S., Gol'tsman, G., Voronov, B., Yagoubov, P., Cherednichenko, S., Gershenzon, E., et al. (1997). Spiral antenna NbN hot-electron bolometer mixer at submm frequencies. IEEE Trans. Appl. Supercond., 7(2), 3395–3398.
Abstract: We have studied the phonon-cooled hot-electron bolometer (HEB) as a quasioptical mixer based on a spiral antenna designed for the 0.3-1 THz frequency band and fabricated on sapphire and high resistivity silicon substrates. HEB devices were produced from superconducting 3.5-5 nm thick NbN films with a critical temperature 10-12 K and a critical current density of approximately 10/sup 7/ A/cm/sup 2/ at 4.2 K. For these devices we reached a DSB receiver noise temperature below 1500 K, a total conversion loss of L/sub t/=16 dB in the 500-700 GHz frequency range, an IF bandwidth of 3-4 GHz and an optimal LO absorbed power of /spl sime/4 /spl mu/W. We experimentally analyzed various contributions to the conversion loss and obtained an RF coupling factor of about 5 dB, internal mixer loss of 10 dB and IF mismatch of 1 dB.
|
Kawamura, J., Blundell, R., Tong, C. -yu E., Gol’tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Low noise NbN lattice-cooled superconducting hot-electron bolometric mixers at submillimeter wavelengths. Appl. Phys. Lett., 70(12), 1619–1621.
Abstract: Lattice-cooled superconducting hot-electron bolometric mixers are used in a submillimeter-wave waveguide heterodyne receiver. The mixer elements are niobium nitride film with 3.5 nm thickness and ∼10 μm2 area. The local oscillator power for optimal performance is estimated to be 0.5 μW, and the instantaneous bandwidth is 2.2 GHz. At an intermediate frequency centered at 1.4 GHz with 200 MHz bandwidth, the double sideband receiver noise temperature is 410 K at 430 GHz. The receiver has been used to detect molecular line emission in a laboratory gas cell.
|
Gerecht, E., Musante, C. F., Yngvesson, K. S., Waldman, J., Gol'tsman, G. N., Yagoubov, P. A., et al. (1997). Optical coupling and conversion gain for NbN HEB mixer at THz frequencies. In Proc. 4-th Int. Semicond. Device Research Symp. (pp. 47–50).
|