Yagoubov, P., Kroug, M., Merkel, H., Kollberg, E., Hübers, H. - W., Schubert, J., et al. (1999). NbN hot electron bolometric mixers at frequencies between 0.7 and 3.1 THz. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 238–246).
Abstract: The performance of NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixers is investigated in the 0.7-3.1 THz frequency range. The devices are made from a 3.5-4 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The length of the bolometer microbridge is 0.1- 0.2 gm, the width is 1-2 gm. The best results of the DSB receiver noise temperature measured at 1.5 GHz intermediate frequency are: 800 K at 0.7 THz, 1100 K at 1.6 THz, 2000 K at 2.5 THz and 4200 K at 3.1 THz. The measurements were performed with a far infrared laser as the local oscillator (LO) source. The estimated LO power required is less than 500 nW at the receiver input. First results on the spiral antenna polarization measurements are reported.
|
|
|
Il'in, K. S., Gol'tsman, G. N., Voronov, B. M., & Sobolewski, R. (1999). Characterization of the electron energy relaxation process in NbN hot-electron devices. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 390–397).
Abstract: We report on transient measurements of electron energy relaxation in NbN films with 300-fs time resolution. Using an electro-optic sampling technique, we have studied the photoresponse of 3.5-nm-thick NbN films deposited on sapphire substrates and exposed to 100-fs-wide optical pulses. Our experimental data analysis was based on the two-temperature model and has shown that in our films at the superconducting transition 10.5 K the inelastic electron-phonon scattering time was about (111}+-__.2) ps. This response time indicated that the maximum intermediate-frequency band of a NbN hot-electron phonon-cooled mixer should reach (16+41-3) GHz if one eliminates the bolometric phonon-heating effect. We have suggested several ways to increase the effectiveness of phonon cooling to achieve the above intrinsic value of the NbN mixer bandwidth.
|
|
|
Schubert, J., Semenov, A., Hübers, H. - W., Gol'tsman, G., Schwaab, G., Voronov, B., et al. (1999). Broad-band terahertz NbN hot-electron bolometric mixer. In Inst. Phys. Conf. (Vol. 167, pp. 663–666).
|
|
|
Tong, C. - Y. E., Kawamura, J., Todd, R. H., Papa, D. C., Blundell, R., Smith, M., et al. (2000). Successful operation of a 1 THz NbN hot-electron bolometer receiver. In Proc. 11th Int. Symp. Space Terahertz Technol. (pp. 49–59).
Abstract: A phonon-cooled NbN superconductive hot-electron bolometer receiver covering the frequency range 0.8-1.04 THz has successfully been used for astronomical observation at the Sub-Millimeter Telescope Observatory on Mount Graham, Arizona. This waveguide heterodyne receiver is a modified version of our fixed-tuned 800 GHz HEB receiver to allow for operation beyond 1 THz. The measured noise temperature of this receiver is about 1250 K at 0.81 THz, 560 K at 0.84 THz, and 1600 K at 1.035 THz. It has a 1 GHz wide IF bandwidth, centered at 1.8 GHz. This receiver has recently been used to detect the CO (9-8) molecular line emission at 1.037 THz in the Orion nebula. This is the first time a ground-based heterodyne receiver has been used to detect a celestial source above 1 THz.
|
|
|
Semenov, A. D., Hübers, H. –W., Schubert, J., Gol'tsman, G. N., Elantiev, A. I., Voronov, B. M., et al. (2000). Frequency dependent noise temperature of the lattice cooled hot-electron terahertz mixer. In Proc. 11th Int. Symp. Space Terahertz Technol. (pp. 39–48).
Abstract: We present the measurements and the theoretical model on the frequency dependent noise temperature of a lattice cooled hot electron bolometer (HEB) mixer in the terahertz frequency range. The experimentally observed increase of the noise temperature with frequency is a cumulative effect of the non-uniform distribution of the high frequency current in the bolometer and the charge imbalance, which occurs near the edges of the normal domain and contacts with normal metal. In addition, we present experimental results which show that the noise temperature of a HEB mixer can be reduced by about 30% due to a Parylene antireflection coating on the Silicon hyperhemispheric lens.
|
|
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Papa, D. C., Hunter, T. R., Paine, S. N., et al. (2000). Superconductive hot-electron-bolometer mixer receiver for 800-GHz operation. IEEE Trans. Microw. Theory Techn., 48(4), 683–689.
Abstract: In this paper, we describe a superconductive hot-electron-bolometer mixer receiver designed to operate in the partially transmissive 350-μm atmospheric window. The receiver employs an NbN thin-film microbridge as the mixer element, in which the main cooling mechanism of the hot electrons is through electron-phonon interaction. At a local-oscillator frequency of 808 GHz, the measured double-sideband receiver noise temperature is TRX=970 K, across a 1-GHz intermediate-frequency bandwidth centered at 1.8 GHz. We have measured the linearity of the receiver and the amount of local-oscillator power incident on the mixer for optimal operation, which is PLO≈1 μW. This receiver was used in making observations as a facility instrument at the Heinrich Hertz Telescope, Mt. Graham, AZ, during the 1998-1999 winter observing season.
|
|
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
|
|
Hübers, H. - W., Semenov, A., Schubert, J., Gol'tsman, G., Voronov, B., & Gershenzon, E. (2000). Performance of the phonon-cooled hot-electron bolometric mixer between 0.7 THz and 5.2 THz. In Proc. 8-th Int. Conf. on Terahertz Electronics (pp. 117–119).
Abstract: We report on the phonon cooled NbN hot electron bolometer as mixer in the terahertz frequency range. Its hybrid antenna consists of a hyperhemispheric silicon lens and a logarithmic-spiral feed antenna. Noise temperatures have been measured between 0.7 THz and 5.2 THz. A quarter wavelength layer of Parylene works as antireflection coating for the silicon lens and reduces the noise temperature by about 30. It was found that the antenna pattern at 2.5 THz is determined by the feed antenna and not by the diameter of the lens.
|
|
|
Huebers, H. - W., Semenov, A., Schubert, J., Gol’tsman, G. N., Voronov, B. M., Gershenzon, E. M., et al. (2000). NbN hot-electron bolometer as THz mixer for SOFIA. In R. K. Melugin, & H. - P. Roeser (Eds.), Proc. SPIE (Vol. 4014, pp. 195–202). SPIE.
Abstract: Heterodyne receivers for applications in astronomy need quantum limited sensitivity. We have investigated phonon- cooled NbN hot electron bolometric mixers in the frequency range from 0.7 THz to 5.2 THz. The devices were 3.5 nm thin films with an in-plane dimension of 1.7 X 0.2 micrometers 2 integrated in a complementary logarithmic spiral antenna. The best measured DSB receiver noise temperatures are 1300 K (0.7 THz), 2000 K (1.4 THz), 2100 K (1.6 THz), 2600 K (2.5 THz), 4000 K (3.1 THz), 5600 K (4.3 THz), and 8800 K (5.2 THz). The sensitivity fluctuation, the long term stability, and the antenna pattern were measured. The results demonstrate that this mixer is very well suited for GREAT, the German heterodyne receiver for SOFIA.
|
|
|
Cherednichenko, S., Kroug, M., Yagoubov, P., Merkel, H., Kollberg, E., Yngvesson, K. S., et al. (2000). IF bandwidth of phonon cooled HEB mixers made from NbN films on MgO substrates. In Proc. 11th Int. Symp. Space Terahertz Technol. (pp. 219–227).
Abstract: An investigation of gain and noise bandwidth of phonon-cooled hot-electron bolometric (HEB) mixers is presented. The radiation coupling to the mixers is quasioptical through either a spiral or twin-slot antenna. A maximum gain bandwidth of 4.8 GHz is obtained for mixers based on a 3.5 nm thin NbN film with Tc= 10 K. The noise bandwidth is 5.6 GHz, at the moment limited by parasitic elements in the, device mount fixture. At 0.65 THz the DSB receiver noise temperature is 700-800 К in the IF band 1-2 GHz, and 1150-2700 К in the band 3.5-7 GHz.
|
|