Kaurova, N. S., Finkel, M. I., Maslennikov, S. N., Vahtomin, Y. B., Antipov, S. V., Smirnov, K. V., et al. (2004). Submillimeter mixer based on YBa2Cu3O7-x thin film. In Proc. 1-st conf. Fundamental problems of high temperature superconductivity (291). Moscow-Zvenigorod.
|
|
|
Korneev, A., Kouminov, P., Matvienko, V., Chulkova, G., Smirnov, K., Voronov, B., et al. (2004). Sensitivity and gigahertz counting performance of NbN superconducting single-photon detectors. Appl. Phys. Lett., 84(26), 5338–5340.
Abstract: We have measured the quantum efficiencysQEd, GHz counting rate, jitter, and noise-equivalentpowersNEPdof nanostructured NbN superconducting single-photon detectorssSSPDsdin thevisible to infrared radiation range. Our 3.5-nm-thick and 100- to 200-nm-wide meander-typedevices(total area 10310mm2), operating at 4.2 K, exhibit an experimental QE of up to 20% inthe visible range and,10% at 1.3 to 1.55mm wavelength and are potentially sensitive up tomidinfrareds,10mmdradiation. The SSPD counting rate was measured to be above 2 GHz withjitter,18 ps, independent of the wavelength. The devices’ NEP varies from,10−17W/Hz1/2for1.55mm photons to,10−20W/Hz1/2for visible radiation. Lowering the SSPD operatingtemperature to 2.3 K significantly enhanced its performance, by increasing the QE to,20% andlowering the NEP level to,3310−22W/Hz1/2, both measured at 1.26mm wavelength.
|
|
|
Meledin, D. V., Marrone, D. P., Tong, C. - Y. E., Gibson, H., Blundell, R., Paine, S. N., et al. (2004). A 1-THz superconducting hot-electron-bolometer receiver for astronomical observations. IEEE Trans. Microwave Theory Techn., 52(10), 2338–2343.
Abstract: In this paper, we describe a superconducting hot-electron-bolometer mixer receiver developed to operate in atmospheric windows between 800-1300 GHz. The receiver uses a waveguide mixer element made of 3-4-nm-thick NbN film deposited over crystalline quartz. This mixer yields double-sideband receiver noise temperatures of 1000 K at around 1.0 THz, and 1600 K at 1.26 THz, at an IF of 3.0 GHz. The receiver was successfully tested in the laboratory using a gas cell as a spectral line test source. It is now in use on the Smithsonian Astrophysical Observatory terahertz test telescope in northern Chile.
|
|
|
Slysz, W., Wegrzecki, M., Papis, E., Gol'tsman, G. N., Verevkin, A., & Sobolewski, R. (2004). A method of optimization of the NbN superconducting single-photon detector (Vol. 36).
|
|
|
Slysz, W., Wegrzecki, M., Bar, J., Grabiec, P., Gol'tsman, G. N., Verevkin, M., et al. (2004). NbN superconducting single-photon detectors coupled with a communication fiber (Vol. 37).
|
|
|
Verevkin, A., Pearlman, A., Slysz, W., Zhang, J., Currie, M., Korneev, A., et al. (2004). Ultrafast superconducting single-photon detectors for near-infrared-wavelength quantum communications. J. Modern Opt., 51(9-10), 1447–1458.
Abstract: The paper reports progress on the design and development of niobium-nitride, superconducting single-photon detectors (SSPDs) for ultrafast counting of near-infrared photons for secure quantum communications. The SSPDs operate in the quantum detection mode, based on photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-width superconducting stripe. The devices are fabricated from 3.5 nm thick NbN films and kept at cryogenic (liquid helium) temperatures inside a cryostat. The detector experimental quantum efficiency in the photon-counting mode reaches above 20% in the visible radiation range and up to 10% at the 1.3–1.55 μn infrared range. The dark counts are below 0.01 per second. The measured real-time counting rate is above 2 GHz and is limited by readout electronics (the intrinsic response time is below 30 ps). The SSPD jitter is below 18 ps, and the best-measured value of the noise-equivalent power (NEP) is 2 × 10−18 W/Hz1/2. at 1.3 μm. In terms of photon-counting efficiency and speed, these NbN SSPDs significantly outperform semiconductor avalanche photodiodes and photomultipliers.
|
|
|
Gao, J. R., Hajenius, M., Baselmans, J. J. A., Klapwijk, T. M., de Korte, P. A. J., Voronov, B., et al. (2004). NbN hot electron bolometer mixers with superior performance for space applications. In E. Armandillo, & B. Leone (Eds.), Proc. Int. workshop on low temp. electronics (pp. 11–17). Noordwijk.
|
|
|
Il'in, K., Siegel, M., Semenov, A., Engel, A., Hübers, H. - W., Hollmann, E., et al. (2004). Thickness dependence of superconducting properties of ultrathin Nb and NbN films. In AKF-Frühjahrstagung.
|
|
|
Verevkin, A., Zhang, J., Pearlman, A., Slysz, W., Sobolewski, R., Korneev, A., et al. (2004). Ultimate sensitivity of superconducting single-photon detectors in the visible to infrared range.
Abstract: We present our quantum efficiency (QE) and noise equivalent power (NEP) measurements of the meandertype ultrathin NbN superconducting single-photon detector in the visible to infrared radiation range. The nanostructured devices with 3.5-nm film thickness demonstrate QE up to~ 10% at 1.3–1.55 µm wavelength, and up to 20% in the entire visible range. The detectors are sensitive to infrared radiation with the wavelengths down to~ 10 µm. NEP of about 2× 10-18 W/Hz1/2 was obtained at 1.3 µm wavelength. Such high sensitivity together with GHz-range counting speed, make NbN photon counters very promising for efficient, ultrafast quantum communications and another applications. We discuss the origin of dark counts in our devices and their ultimate sensitivity in terms of the resistive fluctuations in our superconducting nanostructured devices.
|
|
|
Sobolewski, R., Verevkin, A., Gol'tsman, G. N., Lipatov, A., & Wilsher, K. (2003). Ultrafast superconducting single-photon optical detectors and their applications. IEEE Trans. Appl. Supercond., 13(2), 1151–1157.
Abstract: We present a new class of ultrafast single-photon detectors for counting both visible and infrared photons. The detection mechanism is based on photon-induced hotspot formation, which forces the supercurrent redistribution and leads to the appearance of a transient resistive barrier across an ultrathin, submicrometer-width, superconducting stripe. The devices were fabricated from 3.5-nm- and 10-nm-thick NbN films, patterned into <200-nm-wide stripes in the 4 /spl times/ 4-/spl mu/m/sup 2/ or 10 /spl times/ 10-/spl mu/m/sup 2/ meander-type geometry, and operated at 4.2 K, well below the NbN critical temperature (T/sub c/=10-11 K). Continuous-wave and pulsed-laser optical sources in the 400-nm-to 3500-nm-wavelength range were used to determine the detector performance in the photon-counting mode. Experimental quantum efficiency was found to exponentially depend on the photon wavelength, and for our best, 3.5-nm-thick, 100-/spl mu/m/sup 2/-area devices varied from >10% for 405-nm radiation to 3.5% for 1550-nm photons. The detector response time and jitter were /spl sim/100 ps and 35 ps, respectively, and were acquisition system limited. The dark counts were below 0.01 per second at optimal biasing. In terms of the counting rate, jitter, and dark counts, the NbN single-photon detectors significantly outperform their semiconductor counterparts. Already-identified applications for our devices range from noncontact testing of semiconductor CMOS VLSI circuits to free-space quantum cryptography and communications.
|
|