Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B., et al. (1994). A fast infrared detector based on patterned YBCO thin film. Supercond. Sci. Technol., 7(5), 321–323.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
|
|
|
Gousev, Y. P., Gol'tsman, G. N., Semenov, A. D., Gershenzon, E. M., Nebosis, R. S., Heusinger, M. A., et al. (1994). Broadband ultrafast superconducting NbN detector for electromagnetic radiation. J. Appl. Phys., 75(7), 3695–3697.
Abstract: An ultrafast detector that is sensitive to radiation in a broad spectral range from submillimeter waves to visible light is reported. It consists of a structured NbN thin film cooled to a temperature below Tc (∼11 K). Using 20 ps pulses of a GaAs laser, we observed signal pulses with both rise and decay time of about 50 ps. From the analysis of a mixing experiment with submillimeter radiation we estimate an intrinsic response time of the detector of ∼12 ps. The sensitivity was found to be similar for the near‐infrared and submillimeter radiation. Broadband sensitivity and short response time are attributed to a quasiparticle heating effect.
|
|
|
|
Gousev, Y. P., Semenov, A. D., Gol'tsman, G. N., Sergeev, A. V., & Gershenzon, E. M. (1994). Electron-phonon interaction in disordered NbN films. Phys. B Condens. Mat., 194-196, 1355–1356.
Abstract: Electron-phonon interaction time has been investigated in disordered films of NbN. A temperatures below 5.5 K tau_eph ~ T -1"6 which is attributed to the renormalisation of phonon spectrum in thin films.
|
|
|
|
Sergeev, A., Semenov, A., Trifonov, V., Karasik, B., Gol'tsman, G., & Gershenzon, E. (1994). Heat transfer in YBaCuO thin film/sapphire substrate system. J. Supercond., 7(2), 341–344.
Abstract: The thermal boundary resistance at the YBaCuO thin film/Al2O3 substrate interface was investigated. The transparency for thermal phonons incident on the interface as well as for phonons moving from the substrate was determined. We have measured a transient voltage response of current-biased films to continuously modulated radiation. The observed knee in the modulation frequency dependence of the response reflects the crossover from the diffusion regime to the contact resistance regime of the heat transfer across the interface. The values of transparency were independently deduced both from the phonon escape time and from the time of phonon return to the film which were identified with peculiarities in the frequency dependence. The results are much more consistent with the acoustic mismatch theory than the diffuse mismatch model.
|
|
|
|
Gol'tsman, G. N., Goghidze, I. G., Kouminov, P. B., Karasik, B. S., Semenov, A. D., & Gershenzon, E. M. (1994). Influence of grain boundary weak links on the nonequilibrium response of YBaCuO thin films to short laser pulses. J. Supercond., 7(4), 751–755.
Abstract: The transient voltage response in both epitaxial and granular YBaCuO thin films to 80 ps pulses of YAG∶Nd laser radiation of wavelength 0.63 and 1.54 μm was studied. In the normal and resistive states both types of films demonstrate two components: a nonequilibrium picosecond component and a bolometric nanosecond one. The normalized amplitudes are almost the same for all films. In the superconducting state we observed a kinetic inductive response and two-component shape after integration. The normalized amplitude of the response in granular films is up to five orders of magnitude larger than in epitaxial films. We interpret the nonequilibrium response in terms of a suppression of the order parameter by the excess of quasiparticles followed by the change of resistance in the normal and resistive states or kinetic inductance in the superconducting state. The sharp rise of inductive response in granular films is explained both by a diminishing of the cross section for current percolation through the disordered network of Josephson weak links and by a decrease of condensate density in neighboring regions.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B. S., et al. (1994). Nonequilibrium and bolometric photoresponse in patterned YBa2Cu3O7−δ thin films. J. Appl. Phys., 76(3), 1902–1909.
Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.
|
|
|
|
Gol'tsman, G. N., Kouminov, P., Goghidze, I., & Gershenzon, E. M. (1994). Nonequilibrium kinetic inductive response of YBaCuO thin films to low-power laser pulses. Phys. C: Supercond., 235-240, 1979–1980.
Abstract: Transient non-equilibrium kinetic inductive voltage response of YBaCuO thin films to 20 ps pulses of YAG:Nd laser radiation with 0.63 μm and 1.5 μm wavelength has been revealed. By increasing the sensitivity of 100 ps resolution time registration system and diminishing light intensity (fluence 0.1-1 μJ2/cm2) and transport current (density j≤105 A/cm2) we observed a perculiar bipolar signal form with nearly equal amplitudes of each sign. The integration of the kinetic inductive response over time gives the result which is qualitatively of the same form as the response in the resistive and normal states: nonequilibrium picosecond scale component followed by bolometric nanosecond. Nonequilibrium response is interpreted as suppression of order parameter by excess of quasiparticles followed by a change in resistance in the resistive state and kinetic inductance in superconductive state.
|
|
|
|
Lindgren, M., Zorin, M. A., Trifonov, V., Danerud, M., Winkler, D., Karasik, B. S., et al. (1994). Optical mixing in a patterned YBa2Cu3O7-δ thin film. Appl. Phys. Lett., 65(26), 3398–3400.
Abstract: Mixing of 1.56 µm infrared radiation from two lasers in a high quality YBa2Cu3O7-δ thin film, patterned to parallel strips, was demonstrated. A mixer bandwidth of 18 GHz, limited by the measurement system, was obtained. A model based on nonequilibrium electron heating gives a good fit to the data and predicts an intrinsic mixer bandwidth in excess of 100 GHz, operating in the whole infrared spectrum. Reduction of bolometric effects and ways to decrease the conversion loss of the mixer is discussed. The minimum conversion loss is expected to be ~10 dB.
|
|
|
|
Karasik, B. S., Milostnaya, I. I., Zorin, M. A., Elantev, A. I., Gol'tsman, G. N., & Gershenzon, E. M. (1994). Subnanosecond S-N and N-S switching of YBCO film induced by current pulse. Phys. C: Supercond., 235-240, 1981–1982.
Abstract: A transition of YBCO bridge 60 nm thick from superconducting to normal state induced by an abrupt current step has been studied. A subnanosecond stage has been observed during both S-N and N-S transition. The data obtained can be explained by hot-electron phenomena. On the basis of experimental results a prediction of picosecond switch performance has been made.
|
|
|
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gubkina, T. O., & Semash, V. D. (1994). Superconductive properties of ultrathin NbN films on different substrates. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 7(6), 1097–1102.
Abstract: A study was made on dependence of surface resistance, critical temperature and width of superconducting transition on application temperature and thickness of NbN films, which varied within the range of 3-10 nm. Plates of sapphire, fused and monocrystalline quartz, MgO, as well as Si and silicon oxide were used as substrates. NbN films with 160 μθ·cm specific resistance and 16.5 K (Tc) critical temperature were obtained on sapphire substrates. Intensive growth of ΔTc was noted for films, applied on fused quartz, with increase of precipitation temperature. This is explained by occurrence of high tensile stresses in NbN films, caused by sufficient difference of thermal coefficients of expansion of NbN and quartz.
|
|