Khosropanah, P., Gao, J. R., Laauwen, W. M., Hajenius, M., & Klapwijk, T. M. (2007). Low noise NbN hot electron bolometer mixer at 4.3 THz. Appl. Phys. Lett., 91, 221111 (1 to 3).
Abstract: We have studied the sensitivity of a superconducting NbN hot electron bolometer mixer integrated with a spiral antenna at 4.3 THz. Using hot/cold blackbody loads and a beam splitter all in vacuum, we measured a double sideband receiver noise temperature of 1300 K at the optimum local oscillator (LO) power of 330 nW, which is about 12 times the quantum noise (hnu/2kB). Our result indicates that there is no sign of degradation of the mixing process at the superterahertz frequencies. Moreover, a measurement method is introduced which allows us for an accurate determination of the sensitivity despite LO power fluctuations.
|
Kooi, J. W., Baselmans, J. J. A., Hajenius, M., Gao, J. R., Klapwijk, T. M., Dieleman, P., et al. (2007). IF impedance and mixer gain of NbN hot electron bolometers. J. Appl. Phys., 101(4), 044511.
|
Gao, J. R., Hajenius, M., Yang, Z. Q., Baselmans, J. J. A., Khosropanah, P., Barends, R., et al. (2007). Terahertz superconducting hot electron bolometer heterodyne receivers. IEEE Trans. Appl. Supercond., 17(2), 252–258.
Abstract: We highlight the progress on NbN hot electron bolometer (HEB) mixers achieved through fruitful collaboration between SRON Netherlands Institute for Space Research and Delft University of Technology, the Netherlands. This includes the best receiver noise temperatures of 700 K at 1.63 THz using a twin-slot antenna mixer and 1050 K at 2.84 THz using a spiral antenna coupled HEB mixer. The mixers are based on thin NbN films on Si and fabricated with a new contact-process and-structure. By reducing their areas HEB mixers have shown an LO power requirement as low as 30 nW. Those small HEB mixers have demonstrated equivalent sensitivity as those with large areas provided the direct detection effect due to broadband radiation is removed. To manifest that a HEB based heterodyne receiver can in practice be used at arbitrary frequencies above 2 THz, we demonstrate a 2.8 THz receiver using a THz quantum cascade laser (QCL) as local oscillator.
|
Hajenius, M., Yang, Z. Q., Gao, J. R., Baselmans, J. J. A., Klapwijk, T. M., Voronov, B., et al. (2007). Optimized sensitivity of NbN hot electron bolometer mixers by annealing. IEEE Trans. Appl. Supercond., 17(2), 399–402.
Abstract: We report that the heterodyne sensitivity of superconducting hot-electron bolometers (HEBs) increases by 25-30% after annealing at 85degC in high vacuum. The devices studied are twin-slot antenna coupled mixers with a small area NbN bridge of 1 mum times 0.15 mum, above which there is a SiO 2 passivation layer. The mixer noise temperature, gain, and resistance versus temperature curve of a HEB before and after annealing are compared and analysed. We show that the annealing reduces the intrinsic noise of the mixer by 37% and makes the superconducting transition of the bridge and the contacts sharper. We argue that the reduction ofthe noise is mainly due to the improvement of the transparency of the contact/film interface. The lowest receiver noise temperature of 700 K is measured at a local oscillator frequency of 1.63 THz and at a bath temperature of 4.2 K.
|
Gao, J. R., Hajenius, M., Tichelaar, F. D., Klapwijk, T. M., Voronov, B., Grishin, E., et al. (2007). Monocrystalline NbN nanofilms on a 3C-SiC∕Si substrate. Appl. Phys. Lett., 91(6), 062504 (1 to 3).
Abstract: The authors have realized NbN (100) nanofilms on a 3C-SiC (100)/Si(100) substrate by dc reactive magnetron sputtering at 800°C. High-resolution transmission electron microscopy (HRTEM) is used to characterize the films, showing a monocrystalline structure and confirming epitaxial growth on the 3C-SiC layer. A film ranging in thickness from 3.4to4.1nm shows a superconducting transition temperature of 11.8K, which is the highest reported for NbN films of comparable thickness. The NbN nano-films on 3C-SiC offer a promising alternative to improve terahertz detectors. For comparison, NbN nanofilms grown directly on Si substrates are also studied by HRTEM.
The authors acknowledge S. V. Svetchnikov at National Centre for HRTEM at Delft, who prepared the specimens for HRTEM inspections. This work was supported by the EU through RadioNet and INTAS.
|