Rosfjord, K. M., Yang, J. K. W., Dauler, E. A., Kerman, A. J., Vikas Anant, Voronov, B. M., et al. (2006). Nanowire Single-photon detector with an integrated optical cavity and anti-reflection coating. Opt. Express, 14(2), 527–534.
Abstract: We have fabricated and tested superconducting single-photon detectors and demonstrated detection efficiencies of 57% at 1550-nm wavelength and 67% at 1064 nm. In addition to the peak detection efficiency, a median detection efficiency of 47.7% was measured over 132 devices at 1550 nm. These measurements were made at 1.8K, with each device biased to 97.5% of its critical current. The high detection efficiencies resulted from the addition of an optical cavity and anti-reflection coating to a nanowire photodetector, creating an integrated nanoelectrophotonic device with enhanced performance relative to the original device. Here, the testing apparatus and the fabrication process are presented. The detection efficiency of devices before and after the addition of optical elements is also reported.
|
Jiang, L., Miao, W., Zhang, W., Li, N., Lin, Z. H., Yao, Q. J., et al. (2006). Characterization of quasi-optical NbN phonon-cooled superconducting HEB mixers. In Proc. 17th Int. Symp. Space Terahertz Technol. (pp. 55–58).
Abstract: In this paper, we thoroughly investigate the performance of quasi-optical NbN phonon-cooled superconducting hot-electron bolometer (HEB) mixers, cryogenically cooled by a close-cycled 4-K refrigerator at 500 GI-1z and 850 GHz. The uncorrected lowest receiver noise Abstract---In temperatures measured are 800 K at 500 CHz without anti-reflection coating, and 1000 K @ 850 GHz with a 50 11M thick Mylar anti-reflection coating. The dependence of receiver noise temperature on the critical current and bath temperature of HEB mixer is also investigated here. Lifetime of quasi-optical superconducting NbN HEB mixers of different volumes, room temperature resistances, and critical temperatures are thoroughly studied. Increased room temperature resistance with time over the initial resistance changes between 1 and 1.2, and the reduced critical current with time over the initial value fluctuates slightly around 0.7 for most HEB mixers even of different volumes, room temperature resistances, and critical temperatures. The critical current degrades sharply vvhile room temperature resistance varies over 1.25.
|
Kitaygorsky, J., Komissarov, I., Jukna, A., Sobolewski, R., Minaeva, O., Kaurova, N., et al. (2006). Nanosecond, transient resistive state in two-dimensional superconducting stripes. In Proc. APS March Meeting (H38.13).
Abstract: We have observed, nanosecond-in-duration, transient voltage pulses, generated across two-dimensional (2-D) NbN stripes (width: 100--500 nm; thickness: 3.5--10 nm) of various lengths (1--500 μm), when the wires were completely isolated from the outside world, biased at currents close to the critical current, and kept at temperatures below the mean-field critical temperature Tco. In 2-D superconducting films, at temperatures below the Kosterlitz-Thouless transition, all vortices are bound and the resistance is zero. However, these vortices can get unbound when a large enough transport current is applied. The latter results in a transient resistive state, which manifests itself as spontaneous, 2.5--8-ns-long voltage pulses with the amplitude corresponding to the unbinding potential of a vortex pair. In our 100-nm-wide stripes, we have also observed the formation of phase slip centers (PSCs) at temperatures close to Tco, and a mixture of PSCs and unbound vortex-antivortex pairs at low temperatures.
|
Gol'tsman, G. N., Vachtomin, Y. B., Antipov, S. V., Finkel, M. I., Maslennikov, S. N., Smirnov, K. V., et al. (2005). NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In Proc. SPIE (Vol. 5727, pp. 95–106).
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
Semenov, A., Richter, H., Smirnov, K., Voronov, B., Gol'tsman, G., & Hübers, H. - W. (2004). The development of terahertz superconducting hot-electron bolometric mixers. Supercond. Sci. Technol., 17(5), 436–439.
Abstract: We present recent advances in the development of NbN hot-electron bolometric (HEB) mixers for flying terahertz heterodyne receivers. Three important issues have been addressed: the quality of the source NbN films, the effect of the bolometer size on the spectral properties of different planar feed antennas, and the local oscillator (LO) power required for optimal operation of the mixer. Studies of the NbN films with an atomic force microscope indicated a surface structure that may affect the performance of the smallest mixers. Measured spectral gain and noise temperature suggest that at frequencies above 2.5 THz the spiral feed provides better overall performance than the double-slot feed. Direct measurements of the optimal LO power support earlier estimates made in the framework of the uniform mixer model.
|