Karasik, B. S., Il'in, K. S., Ptitsina, N. G., Gol'tsman, G. N., Gershenzon, E. M., Pechen', E. V., et al. (1998). Electron-phonon scattering rate in impure NbC films. In NASA/ADS (Y35.08).
Abstract: The study of the electron-phonon interaction in thin (20 nm) NbC films with electron mean free path l=2-13 nm gives an evidence that electron scattering is significantly modified due to the interference between electron-phonon and elastic electron scattering from impurities. The interference ~T^2-term, which is proportional to the residual resistivity, dominates over the Bloch-Grüneisen contribution to resistivity at low temperatures up to 60 K. The electron energy relaxation rate is directly measured via the relaxation of hot electrons heated by modulated electromagnetic radiation. In the temperature range 1.5 – 10 K the relaxation rate shows a weak dependence on the electron mean free path and strong temperature dependence T^n with the exponent n = 2.5-3. This behaviour is well explained by the theory of the electron-phonon-impurity interference taking into account the electron coupling with transverse phonons determined from the resistivity data.
|
|
|
Gousev, Y. P., Semenov, A. D., Goghidze, I. G., Pechen, E. V., Varlashkin, A. V., Gol'tsman, G. N., et al. (1997). Current dependent noise in a YBa2Cu3O7-δ hot-electron bolometer. IEEE Trans. Appl. Supercond., 7(2), 3556–3559.
Abstract: We investigated the output noise of a YBa2Cu3O7-δ (YBCO) superconducting hot-electron bolometer (HEB) in a large frequency range (10 kHz to 8 GHz); the bolometer either consisted of a structured 50 nm thick YBCO film on LaAlO/sub 3/ or a 30 nm thick film on a MgO substrate. We found that flicker noise dominated at low frequencies (below 1 MHz), while at higher frequencies Johnson noise and a current dependent noise were the main noise sources.
|
|
|
Semenov, A. D., Gousev, Y. P., Renk, K. F., Voronov, B. M., Gol'tsman, G. N., Gershenzon, E. M., et al. (1997). Noise characteristics of a NbN hot-electron mixer at 2.5 THz. IEEE Trans. Appl. Supercond., 7(2), 3572–3575.
Abstract: The noise temperature of a NbN phonon cooled hot-electron mixer has been measured at a frequency of 2.5 THz for various operating conditions. We obtained for optimal operation a double sideband mixer noise temperature of /spl ap/14000 K and a system conversion loss of /spl ap/23 dB at intermediate frequencies up to 1 GHz. The dependences of the mixer noise temperature on the bias voltage, local oscillator power, and intermediate frequency were consistent with the phenomenological description based on the effective temperature approximation.
|
|
|
Svechnikov, S. I., Okunev, O. V., Yagoubov, P. A., Gol'tsman, G. N., Voronov, B. M., Cherednichenko, S. I., et al. (1997). 2.5 THz NbN hot electron mixer with integrated tapered slot antenna. IEEE Trans. Appl. Supercond., 7(2), 3548–3551.
Abstract: A Hot Electron Bolometer (HEB) mixer for 2.5 THz utilizing a NbN thin film device, integrated with a Broken Linearly Tapered Slot Antenna (BLTSA), has been fabricated and is presently being tested. The NbN HEB device and the antenna were fabricated on a SiO2membrane. A 0.5 micrometer thick SiO2layer was grown by rf magnetron reactive sputtering on a GaAs wafer. The HEB device (phonon-cooled type) was produced as several parallel strips, 1 micrometer wide, from an ultrathin NbN film 4-7 nm thick, that was deposited onto the SiO2layer by dc magnetron reactive sputtering. The BLTSA was photoetched in a multilayer Ti-Au metallization. In order to strengthen the membrane, the front-side of the wafer was coated with a 5 micrometer thick polyimide layer just before the membrane formation. The last operation was anisotropic etching of the GaAs in a mixture of HNO3and H2O2.
|
|
|
Zorin, M., Milostnaya, I., Gol'tsman, G. N., & Gershenzon, E. M. (1997). Fast NbN superconducting switch controlled by optical radiation. IEEE Trans. Appl. Supercond., 7(2), 3734–3737.
Abstract: The switching time and the optical control power of the NbN superconducting switch have been measured. The device is based on the ultrathin film 5-8 nm thick patterned as a structure of several narrow parallel strips (/spl sim/1 /spl mu/m wide) connected to wide current leads. The current-voltage characteristic of the switch at temperature 4.2 K demonstrated a hysteresis due to DC current self-heating. We studied the superconducting-to-resistive state transition induced by both optical and bias-current excitations. The optical pulse duration was /spl sim/20 ps and the rise time of the current step was determined to be less than 50 ps. The optical pulse was delivered to the switch by the semiconductor laser through an optical fiber. We found that the measured switching time is less than the duration of the optical excitation. The threshold optical power density does not exceed 3/spl middot/10/sup 3/ W/cm/sup 2/. The proposed device can be used in the fiber input of LTS rapid single flux quantum circuits.
|
|