Sobolewski R, Xu Y, Zheng X, Williams C, Zhang J, Verevkin A, et al. Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans Electron. 2002;E85-C(3):797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
|
|
Корнеев АА, Минаева О, Рубцова И, Милостная И, Чулкова Г, Воронов Б, et al. Сверхпроводящий однофотонный детектор на основе ультратонкой пленки NbN. Квантовая электроника. 2005;35(8):698–700.
Abstract: Представлены результаты исследований сверхпроводящих однофотонных детекторов, изготовленных из ультратонкой пленки NbN. Развитие технологического процесса изготовления детекторов, а также снижение рабочей температуры до 2 К позволили существенно увеличить квантовую эффективность: для видимого света (λ = 0.56 мкм) она составила 30%–40%, т.е. достигла предела, определяемого коэффициентом поглощения пленки. С ростом длины волны квантовая эффективность экспоненциально падает, составляя ~20% на λ=1.55 мкм и ~0.02% на λ = 5 мкм. При скорости темнового счета ~10-4s-1 экспериментально измеренная эквивалентная мощность шума составила 1.5 × 10-20 Вт/Гц-1/2; в дальнейшем она может быть уменьшена до рекордно низкого значения 5 × 10-21 Вт/Гц-1/2. Временное разрешение детектора равно 30 пс.
|
|
|
Korneev A, Minaeva O, Rubtsova I, Milostnaya I, Chulkova G, Voronov B, et al. Superconducting single-photon ultrathin NbN film detector. Quantum Electronics. 2005;35(8):698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
|
|
Maslennikov SN, Finkel MI, Antipov SV, Polyakov SL, Zhang W, Ozhegov R, et al. Spiral antenna coupled and directly coupled NbN HEB mixers in the frequency range from 1 to 70 THz. In: Proc. 17th Int. Symp. Space Terahertz Technol. Paris, France; 2006. p. 177–9.
Abstract: We investigate both antenna coupled and directly coupled HEB mixers at several LO frequencies within the range of 2.5 THz to 70 THz. H20 (2.5+10.7 THz), and CO2 (30 THz) gas discharge lasers are used as the local oscillators. The noise temperature of antenna coupled mixers is measured at LO frequencies of 2.5 THz, 3.8 THz, and 30 THz. The results for both antenna coupled and directly coupled mixer types are compared. The devices with in—plane dimensions of 5x5 ,um 2 are pumped by LO radiation at 10.7 THz. The directly coupled HEB demonstrates nearly flat dependence of responsivity on frequency in the range of 25+64 THz.
|
|
|
Gol'tsman GN, Semenov AD, Gousev YP, Zorin MA, Gogidze IG, Gershenzon EM, et al. Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond Sci Technol. 1991;4(9):453–6.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
|
|
Prober DE. Superconducting terahertz mixer using a transition-edge microbolometer. Appl Phys Lett. 1993;62(17):2119–21.
|
|
|
Gousev YP, Gol'tsman GN, Semenov AD, Gershenzon EM, Nebosis RS, Heusinger MA, et al. Broadband ultrafast superconducting NbN detector for electromagnetic radiation. J Appl Phys. 1994;75(7):3695–7.
Abstract: An ultrafast detector that is sensitive to radiation in a broad spectral range from submillimeter waves to visible light is reported. It consists of a structured NbN thin film cooled to a temperature below Tc (∼11 K). Using 20 ps pulses of a GaAs laser, we observed signal pulses with both rise and decay time of about 50 ps. From the analysis of a mixing experiment with submillimeter radiation we estimate an intrinsic response time of the detector of ∼12 ps. The sensitivity was found to be similar for the near‐infrared and submillimeter radiation. Broadband sensitivity and short response time are attributed to a quasiparticle heating effect.
|
|
|
Gol'tsman GN, Karasik BS, Okunev OV, Dzardanov AL, Gershenzon EM, Ekstrom H, et al. NbN hot electron superconducting mixers for 100 GHz operation. IEEE Trans Appl Supercond. 1995;5(2):3065–8.
Abstract: NbN is a promising superconducting material for hot-electron superconducting mixers with an IF bandwidth larger than 1 GHz. In the 1OO GHz frequency range, the following parameters were obtained for 50 /spl Aring/ thick NbN films at 4.2 K: receiver noise temperature (DSB) /spl sim/1000 K; conversion loss /spl sim/10 dB; IF bandwidth /spl sim/1 GHz; and local oscillator power /spl sim/1 /spl mu/W. An increase of the critical current of the NbN film, increased working temperature, and a better mixer matching may allow a broader IF bandwidth up to 2 GHz, reduced conversion losses down to 3-5 dB and a receiver noise temperature (DSB) down to 200-300 K.
|
|
|
Yagubov P, Gol'tsman G, Voronov B, Seidman L, Siomash V, Cherednichenko S, et al. The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In: Proc. 7th Int. Symp. Space Terahertz Technol. Charlottesville, Virginia, USA; 1996. p. 290–302.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|
|
Semenov A, Richter H, Smirnov K, Voronov B, Gol'tsman G, Hübers H-W. The development of terahertz superconducting hot-electron bolometric mixers. Supercond Sci Technol. 2004;17(5):436–9.
Abstract: We present recent advances in the development of NbN hot-electron bolometric (HEB) mixers for flying terahertz heterodyne receivers. Three important issues have been addressed: the quality of the source NbN films, the effect of the bolometer size on the spectral properties of different planar feed antennas, and the local oscillator (LO) power required for optimal operation of the mixer. Studies of the NbN films with an atomic force microscope indicated a surface structure that may affect the performance of the smallest mixers. Measured spectral gain and noise temperature suggest that at frequencies above 2.5 THz the spiral feed provides better overall performance than the double-slot feed. Direct measurements of the optimal LO power support earlier estimates made in the framework of the uniform mixer model.
|
|