Gol'tsman GN, Vachtomin YB, Antipov SV, Finkel MI, Maslennikov SN, Smirnov KV, et al. NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In: Proc. SPIE. Vol 5727.; 2005. p. 95–106.
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
|
|
|
Goltsman GN, Vachtomin YB, Antipov SV, Finkel MI, Maslennikov SN, Polyakov SL, et al. Low-noise NbN phonon-cooled hot-electron bolometer mixers for terahertz heterodyne receivers. In: Proc. 9-th WMSCI. Vol 9. International Institute of Informatics and Systemics; 2005. p. 154–9.
|
|
|
|
Jiang L, Miao W, Zhang W, Li N, Lin ZH, Yao QJ, et al. Characterization of quasi-optical NbN phonon-cooled superconducting HEB mixers. In: Proc. 17th Int. Symp. Space Terahertz Technol.; 2006. p. 55–8.
Abstract: In this paper, we thoroughly investigate the performance of quasi-optical NbN phonon-cooled superconducting hot-electron bolometer (HEB) mixers, cryogenically cooled by a close-cycled 4-K refrigerator at 500 GI-1z and 850 GHz. The uncorrected lowest receiver noise Abstract---In temperatures measured are 800 K at 500 CHz without anti-reflection coating, and 1000 K @ 850 GHz with a 50 11M thick Mylar anti-reflection coating. The dependence of receiver noise temperature on the critical current and bath temperature of HEB mixer is also investigated here. Lifetime of quasi-optical superconducting NbN HEB mixers of different volumes, room temperature resistances, and critical temperatures are thoroughly studied. Increased room temperature resistance with time over the initial resistance changes between 1 and 1.2, and the reduced critical current with time over the initial value fluctuates slightly around 0.7 for most HEB mixers even of different volumes, room temperature resistances, and critical temperatures. The critical current degrades sharply vvhile room temperature resistance varies over 1.25.
|
|
|
|
Vahtomin YB, Finkel MI, Antipov SV, Voronov BM, Smirnov KV, Kaurova NS, et al. Gain bandwidth of phonon-cooled HEB mixer made of NbN thin film with MgO buffer layer on Si. In: Harvard university, editor. Proc. 13th Int. Symp. Space Terahertz Technol. Cambridge, MA, USA; 2002. p. 259–70.
Abstract: We present recently obtained values for gain bandwidth of NbN HEB mixers for different substrates and film thicknesses and for MgO buffer layer on Si at LO frequency of 0.85-1 THz. The maximal bandwidth, 5.2 GHz, was achieved for the device on MgO buffer layer on Si with a 2 nm thick NbN film. Functional devices based on NbN films of such thickness were fabricated for the first time due to an improvement of superconducting properties of NbN film deposited on MgO buffer layer on Si substrate.
|
|