Abstract: The authors have investigated the photoinduced voltage response of a current-carrying structured YBa₂Cu₃O_7-δ thin film to ultrashort far-infrared (FIR) laser pulses in the frequency range from 0.7 THz to 7 THz. The detector has shown an almost constant sensitivity of 1 mV/W and a noise equivalent power of less than 5*10/sup -7/ W/ square root Hz. The temperature dependence of the decay time of the detector signal was studied for temperatures around the transition temperature of the film ( approximately 80 K). For a detector temperature where dR/dT had its maximum, the authors observed bolometric signals with decay times of about 2 ns, and for lower temperatures they observed nonbolometric signals with decay times of approximately 120 ps; the duration of the nonbolometric signals was limited by the time resolution of the electronic registration equipment.

Abstract: We present a new class of ultrafast single-photon detectors for counting both visible and infrared photons. The detection mechanism is based on photon-induced hotspot formation, which forces the supercurrent redistribution and leads to the appearance of a transient resistive barrier across an ultrathin, submicrometer-width, superconducting stripe. The devices were fabricated from 3.5-nm- and 10-nm-thick NbN films, patterned into <200-nm-wide stripes in the 4 /spl times/ 4-/spl mu/m/sup 2/ or 10 /spl times/ 10-/spl mu/m/sup 2/ meander-type geometry, and operated at 4.2 K, well below the NbN critical temperature (T/sub c/=10-11 K). Continuous-wave and pulsed-laser optical sources in the 400-nm-to 3500-nm-wavelength range were used to determine the detector performance in the photon-counting mode. Experimental quantum efficiency was found to exponentially depend on the photon wavelength, and for our best, 3.5-nm-thick, 100-/spl mu/m/sup 2/-area devices varied from >10% for 405-nm radiation to 3.5% for 1550-nm photons. The detector response time and jitter were /spl sim/100 ps and 35 ps, respectively, and were acquisition system limited. The dark counts were below 0.01 per second at optimal biasing. In terms of the counting rate, jitter, and dark counts, the NbN single-photon detectors significantly outperform their semiconductor counterparts. Already-identified applications for our devices range from noncontact testing of semiconductor CMOS VLSI circuits to free-space quantum cryptography and communications.

Abstract: Sensitivity and gain bandwidth measurements of phonon-cooled NbN superconducting hot-electron bolometer mixers are presented. The best receiver noise temperatures are: 700 K at 1.6 THz and 1100 K at 2.5 THz. Parylene as an antireflection coating on silicon has been investigated and used in the optics of the receiver. The dependence of the mixer gain bandwidth (GBW) on the bias voltage has been measured. Starting from low bias voltages, close to operating conditions yielding the lowest noise temperature, the GBW increases towards higher bias voltages, up to three times the initial value. The highest measured GBW is 9 GHz within the same bias range the noise temperature increases by a factor of two.

Abstract: We have developed a low-noise waveguide heterodyne receiver for operation near 1 THz using phonon-cooled NbN hot-electron bolometers. The mixer elements are submicron-sized microbridges of 4 nm-thick NbN film fabricated on a quartz substrate. Operating at a bath temperature of 4.2 K, the double-sideband receiver noise temperature is 760 K at 1.02 THz and 1100 K at 1.26 THz. The local oscillator is provided by solid-state sources, and power measured at the source is less than 1 /spl mu/W. The intermediate frequency bandwidth exceeds 2 GHz. The receiver was used to make the first ground-based heterodyne detection of a celestial spectroscopic line above 1 THz.