Yagubov P, Gol'tsman G, Voronov B, Seidman L, Siomash V, Cherednichenko S, et al. The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In: Proc. 7th Int. Symp. Space Terahertz Technol. Charlottesville, Virginia, USA; 1996. p. 290–302.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|
|
|
Cherednichenko S, Yagoubov P, Il'In K, Gol'tsman G, Gershenzon E. Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In: Proc. 8th Int. Symp. Space Terahertz Technol.; 1997. p. 245–57.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
|
|
Cherednichenko S, Kroug M, Merkel H, Kollberg E, Loudkov D, Smirnov K, et al. Local oscillator power requirement and saturation effects in NbN HEB mixers. In: Jet Propulsion Laboratory CIit.u.t.e of T, editor. Proc. 12th Int. Symp. Space Terahertz Technol. San Diego, CA, USA; 2001. p. 273–85.
Abstract: The local oscillator power required for NbN hot-electron bolometric mixers (P LO ) was investigated with respect to mixer size, critical temperature and ambient temperature. P LO can be decreased by a factor of 10 as the mixer size decreases from 4×0.4 µm 2 to 0.6×0.13 µm 2 . For the smallest volume mixer the optimal local oscillator power was found to be 15 nW. We found that for such mixer no signal compression was observed up to an input signal of 2 nW which corresponds to an equivalent input load of 20,000 K. For a constant mixer volume, reduction of T c can decrease optimal local oscillator power at least by a factor of 2 without a deterioration of the receiver noise temperature. Bath temperature was found to have minor effect on the receiver characteristics.
|
|
|
|
Kawamura J, Blundell R, Tong C-YE, Papa DC, Hunter TR, Paine SN, et al. Superconductive hot-electron-bolometer mixer receiver for 800-GHz operation. IEEE Trans Microw Theory Techn. 2000;48(4):683–9.
Abstract: In this paper, we describe a superconductive hot-electron-bolometer mixer receiver designed to operate in the partially transmissive 350-μm atmospheric window. The receiver employs an NbN thin-film microbridge as the mixer element, in which the main cooling mechanism of the hot electrons is through electron-phonon interaction. At a local-oscillator frequency of 808 GHz, the measured double-sideband receiver noise temperature is TRX=970 K, across a 1-GHz intermediate-frequency bandwidth centered at 1.8 GHz. We have measured the linearity of the receiver and the amount of local-oscillator power incident on the mixer for optimal operation, which is PLO≈1 μW. This receiver was used in making observations as a facility instrument at the Heinrich Hertz Telescope, Mt. Graham, AZ, during the 1998-1999 winter observing season.
|
|
|
|
Chen J, Kang L, Jin BB, Xu WW, Wu PH, Zhang W, et al. Properties of terahertz superconducting hot electron bolometer mixers. Int J Terahertz Sci Technol. 2008;1(1):37–41.
Abstract: A quasi-optical superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixer has been fabricated and measured in the terahertz (THz) frequency range of 0.5~2.52 THz. A receiver noise temperature of 2000 K at 2.52 THz has been obtained for the mixer without corrections. Also, the effect of a Parylene C anti-reflection (AR) coating on the silicon (Si) lens has been studied.
|
|
|
|
Jiang L, Antipov SV, Voronov BM, Gol'tsman GN, Zhang W, Li N, et al. Characterization of the performance of a quasi-optical NbN superconducting HEB mixer. IEEE Trans Appl Supercond. 2007;17(2):395–8.
Abstract: In this paper we focus mainly on the investigation of the performance of a quasi-optical (planar log-spiral antenna) phonon-cooled NbN superconducting hot electron bolometer (HEB) mixer, which is cryogenically cooled by a close-cycled 4-K cryocooler, at 500 and 850 GHz frequency bands. The mixer's noise performance, stability of IF output power, and local oscillator (LO) power requirement are characterized for three NbN superconducting HEB devices of different sizes. The transmission characteristics of Mylar and Zitex films with incidence waves of an elliptical polarization are also examined by measuring the mixer's noise temperature. The lowest receiver noise temperatures (with no corrections) of 750 and 1100 K are measured at 500 and 850 GHz, respectively. Experimental results also demonstrate that the bigger the HEB device is, the higher the stability of IF output power becomes.
|
|
|
|
Gol'tsman GN, Karasik BS, Svechnikov SI, Gershenzon EM, Ekström H, Kollberg E. Noise temperature of NbN hot—electron quasioptical superconducting mixer in 200-700 GHz range [abstract]. In: Proc. 6th Int. Symp. Space Terahertz Technol.; 1995. 268.
Abstract: The electron heating effect in superconducting films is becoming very attractive for the development of THz range mixers because of the absence of frequency limitations inherent in the bolometric mechanism. However, the evidence for the spectral dependence of the position of optimal operating point has been found recently for NbN thin film devices 1.2 • The effect is presumably attributed to the variation in the absorption of radiation depending on the frequency. Since the resistive state is not spatially uniform the coupling efficiency of the mixer device with radiation can be different for frequencies larger than Zeilh and those smaller than 2Alh (d is the effective superconducting gap in the resistive state). To study the effect more thoroughly we have investigated the noise temperature of quasioptical NbN mixer device with broken hue tapered slot antenna in the frequency range 200-700 GHz. The device consists of several (5-10) parallel strips 1 jim wide and 6-7 tun thick made from NbN film on Si0 2 -Si 3 N 4 -Si membrane. The strips are connected with the gold contacts of the slot-line antenna which serves both as bias and IF leads. We used backward wave oscillators as LO sources and a standard hot/cold load technique for noise temperature measurements. The frequency dependence of noise temperature is mainly determined by two factors: frequency properties of the antenna and frequency dependence of the NbN film impedance. To separate both factors we monitored the frequency dependence of the device responsivity in the detector mode at a higher temperature within the superconducting transition where the impedance of NbN film is close to its normal resistance. In this case the impedance of the device itself is frequency independent. The experimental results will be reported at the Symposium. 1. G. Gollsman, S. Jacobsson, H. EkstrOm, B. Karasik, E. Kollberg, and E. Gershenzon, “Slot-line tapered antenna with NbN hot electron mixer for 300-360 GHz operation,” Proc of the 5th Int. Symp. on Space Terahertz Technology, pp. 209-213a, May 10-12,1994. 2. B.S. Karasik, G.N. Gol i tsman, B.M. Voronov, S.I. Svechnikov, E.M. Gershenzon, H. Ekstrom, S. Jacobsson, E. Kollberg, and K.S. Yngvesson, “Hot electron quasioptical NbN superconducting mixer,” presented at the ASC94, submitted to IEEE Trans. on Appl. Superconductivity.
|
|
|
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Gol'tsman G, Svechnikov S, et al. Noise temperature and local oscillator power requirement of NbN phonon-cooled hot electron bolometric mixers at terahertz frequencies. Appl Phys Lett. 1998;73(19):2814–6.
Abstract: In this letter, the noise performance of NbN-based phonon-cooled hot electron bolometric quasioptical mixers is investigated in the 0.55–1.1 THz frequency range. The best results of the double-sideband <cd><2018>DSB<cd><2019> noise temperature are: 500 K at 640 GHz, 600 K at 750 GHz, 850 K at 910 GHz, and 1250 K at 1.1 THz. The water vapor in the signal path causes significant contribution to the measured receiver noise temperature around 1.1 THz. The devices are made from 3-nm-thick NbN film on high-resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are typically 0.2Ï«2 um. The amount of local oscillator power absorbed in the bolometer is less than 100 nW.
|
|
|
|
Krause S, Mityashkin V, Antipov S, Gol'tsman G, Meledin D, Desmaris V, et al. Study of IF bandwidth of NbN hot electron bolometers on GaN buffer layer using a direct measurement method. In: Proc. 27th Int. Symp. Space Terahertz Technol.; 2016. p. 30–2.
Abstract: In this paper, we present a reliable measurement method to study the influence of the GaN buffer layer on phonon-escape time in comparison with commonly used Si substrates and, in consequence, on the IF bandwidth of HEBs. One of the key aspects is to operate the HEB mixer at elevated bath temperatures close to the critical temperature of the NbN ultra-thin film, where contributions from electron-phonon processes and self-heating effects are relatively small, therefore IF roll-off will be governed by the phonon-escape.Two independent experiments were performed at GARD and MSPU on a similar experimental setup at frequencies of approximately 180 and 140 GHz, respectively, and have shown reproducible and consistent results. The entire IF chain was characterized by S-parameter measurements. We compared the measurement results of epitaxial NbN grown onto GaN buffer-layer with Tc of 12.5 K (4.5nm) with high quality polycrystalline NbN films on Si substrate with Tc of 10.5K (5nm) and observed a strong indication of an enhancement of phonon escape to the substrate by a factor of two for the NbN/GaN material combination.
|
|
|
|
Semenov AD, Heusinger MA, Renk KF, Menschikov E, Sergeev AV, Elant'ev AI, et al. Influence of phonon trapping on the performance of NbN kinetic inductance detectors. IEEE Trans Appl Supercond. 1997;7(2):3083–6.
Abstract: Voltage and microwave photoresponse of NbN thin films to modulated and pulsed optical radiation reveals, far below the superconducting transition, a response time consistent with the lifetime of nonequilibrium quasiparticles. We show that even in 5 nm thick films at 4.2 K the phonon trapping is significant resulting in a quasiparticle lifetime of a few nanoseconds that is an order of magnitude larger than the recombination time. Values and temperature dependence of the quasiparticle lifetime obey the Bardeen-Cooper-Schrieffer theory and are in quantitative agreement with the electron-phonon relaxation rate determined from the resistive response near the superconducting transition. We discuss a positive effect of the phonon trapping on the performance of kinetic inductance detectors.
|
|