Danerud M, Winkler D, Zorin M, Trifonov V, Karasik B, Gershenzon EM, et al. Picosecond detection of infrared radiation with YBa2Cu3O7-δ thin films. In: Birch JR, Parker TJ, editors. Proc. SPIE. Vol 2104. Spie; 1993. p. 183–4.
Abstract: Picosecond nonequilibrium and slow bolometric responses from a patterned high-Tc superconducting (HTS) film due toinfrared radiation were investigated using both modulation and pulse techniques. Measurements at A, = 0.85 [tm andA, = 10.6 lim have shown a similar behaviour of the response vs modulation frequency f. The responsivity of the HTS filmbased detector at f ..- 0.6-1 GHz is estimated to be 10-2 – 10-1 V/W.
|
|
|
Lindgren M, Zorin MA, Trifonov V, Danerud M, Winkler D, Karasik BS, et al. Optical mixing in a patterned YBa2Cu3O7-δ thin film. Appl Phys Lett. 1994;65(26):3398–400.
Abstract: Mixing of 1.56 µm infrared radiation from two lasers in a high quality YBa2Cu3O7-δ thin film, patterned to parallel strips, was demonstrated. A mixer bandwidth of 18 GHz, limited by the measurement system, was obtained. A model based on nonequilibrium electron heating gives a good fit to the data and predicts an intrinsic mixer bandwidth in excess of 100 GHz, operating in the whole infrared spectrum. Reduction of bolometric effects and ways to decrease the conversion loss of the mixer is discussed. The minimum conversion loss is expected to be ~10 dB.
|
|
|
Cherednichenko S, Rönnung F, Gol'tsman G, Kollberg E, Winkler D. YBa2Cu3O7−δ hot-electron bolometer mixer. Phys C: Supercond. 2000;341-348:2653–4.
Abstract: We present an investigation of hot-electron bolometric mixer based on YBa2Cu3O7−δ (YBCO) superconducting thin film. Mixer conversion loss, absorbed local oscillator power and intermediate frequency bandwidth was measured at the local oscillator frequency 600 GHz. The fabrication technique for nanoscale YBCO hot-electron bolometer (HEB) mixer integrated into planar antenna structure is described.
|
|
|
Rönnung F, Cherednichenko S, Winkler D, Gol'tsman GN. A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond Sci Technol. 1999;12(11):853–5.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
Cherednichenko S, Ronnung F, Gol'tsman G, Gershenzon E, Winkler D. YBa2Cu3O7-δ hot-electron bolometer with submicron dimensions. In: Proc. 10th Int. Symp. Space Terahertz Technol.; 1999. p. 181–9.
Abstract: Photoresponse of YBa2Cu3O7-δ hot-electron bolometers to modulated near-infrared radiation was studied at a modulation .frequenc y var y ing from 0.2 MHz to 2 GHz. Bolometers were _fabricated from a 50 12 M thick film and had in-plane areas of 10x10 , um 2 . 2x0.2 s um', 1x0.2 p.m', and 0.5x0.2 jim. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
Gousev YP, Semenov AD, Goghidze IG, Pechen EV, Varlashkin AV, Gol'tsman GN, et al. Current dependent noise in a YBa2Cu3O7-δ hot-electron bolometer. IEEE Trans Appl Supercond. 1997;7(2):3556–9.
Abstract: We investigated the output noise of a YBa2Cu3O7-δ (YBCO) superconducting hot-electron bolometer (HEB) in a large frequency range (10 kHz to 8 GHz); the bolometer either consisted of a structured 50 nm thick YBCO film on LaAlO/sub 3/ or a 30 nm thick film on a MgO substrate. We found that flicker noise dominated at low frequencies (below 1 MHz), while at higher frequencies Johnson noise and a current dependent noise were the main noise sources.
|
|
|
Trifonov VA, Karasik BS, Zorin MA, Gol'tsman GN, Gershenzon EM, Lindgren M, et al. 9.6 μm wavelength mixing in a patterned YBa2Cu3O7-δ thin film. In: Proc. 7th Int. Symp. Space Terahertz Technol.; 1996. p. 337–48.
Abstract: Hot-electron bolometric (HEB) mixing of 9.6 gm infrared radiation from two lasers in high-quality YBa2Cu307_3 (YBCO) patterned thin film has been demonstrated. A heterodyne measurement showed an intermediate frequency (IF) bandwidth of 18 GHz, limited by our measurement system. An intrinsic limit of 100 GHz is predicted. Between 0.1 and 1 GHz intermediate frequency, temperature fluctuations with an equivalent output noise temperature Tfl up to -150 K, contributed to the mixer noise while Johnson noise dominated above 1 GHz. The overall conversion loss at 77 K at low intermediate frequencies was measured to be -25 dB, of which 13 dB was due to the coupling loss. The IIEB mixer is very promising for use in heterodyne receivers within the whole infrared range.
|
|
|
Zorin M, Gol'tsman GN, Karasik BS, Elantev AI, Gershenzon EM, Lindgren M, et al. Optical mixing in thin YBa2Cu3O7-x films. IEEE Trans Appl Supercond. 1995;5(2):2431–4.
Abstract: High quality, j/sub c/ (77 K)>10/sup 6/ A/cm/sup 2/, epitaxial YBa2Cu3O7-x films of 50 nm thickness were patterned into ten parallel 1 /spl mu/m wide strips. The film structure was coupled to a single-mode fiber. Mixer response was obtained at 0.78 /spl mu/m using laser frequency modulation and an optical delay line. Using two semiconductor lasers at 1.55 /spl mu/m wavelength the beating signal was used to measure the photoresponse up to 18 GHz. Nonequilibrium photoresponse in the resistive state of the superconductor was observed. Bolometric response dominates up to 3 GHz, after which the nonequilibrium response is constant up to the frequency limit of our registration system. Using an electron heating model the influence of different thermal processes on the conversion loss has been analyzed. Ways of increasing the sensitivity are also discussed.
|
|
|
Karasik BS, Milostnaya II, Zorin MA, Elantev AI, Gol'tsman GN, Gershenzon EM. High speed current switching of homogeneous YBaCuO film between superconducting and resistive states. IEEE Trans Appl Supercond. 1995;5(2):3042–5.
Abstract: Transitions of thin structured YBaCuO films from superconducting (S) to normal (N) state and back induced by a supercritical current pulse has been studied. A subnanosecond stage in the film resistance dynamic has been observed. A more gradual (nanosecond) ramp in the time dependence of the resistance follows the fast stage. The fraction of the film resistance which is attained during the fast S-N stage rises with the current amplitude. Subnanosecond N-S switching is more pronounced for smaller amplitudes of driving current and for shorter pulses. The phenomena observed are viewed within the framework of an electron heating model. The expected switching time and repetition rate of an optimized current controlling device are estimated to be 1-2 ps and 80 GHz respectively.
|
|
|
Gol'tsman G, Kouminov P, Goghidze I, Gershenzon E. Nonequilibrium kinetic inductive response of YBCO thin films to low power laser pulses. IEEE Trans Appl Supercond. 1995;5(2):2591–4.
Abstract: We have discovered a transient nonequilibrium kinetic inductive voltage response of YBCO thin films to 20 ps pulses of YAG:Nd laser radiation with 0.63 /spl mu/m and 1.54 /spl mu/m wavelength. By increasing the sensitivity of the read-out system with 100 ps resolution time and diminishing the light intensity (fluence 0.1-2 /spl mu/J/cm/sup 2/) and transport current (density /spl les/10/sup 5/ A/cm/sup 2/) we were able to observe a peculiar bipolar signal form with nearly equal amplitudes for each sign. The integration of the kinetic inductive response over time gives the result which is qualitatively, of the same form as the response in the resistive and normal states: the nonequilibrium picosecond scale component is followed by the bolometric nanosecond component. The nonequilibrium response is interpreted as suppression of the order parameter by excess quasiparticles followed by a change both in resistance (for the resistive state) and in kinetic inductance (for the superconducting state).
|
|