Sobolewski R, Xu Y, Zheng X, Williams C, Zhang J, Verevkin A, et al. Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans Electron. 2002;E85-C(3):797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
|
|
Korneev A, Minaeva O, Rubtsova I, Milostnaya I, Chulkova G, Voronov B, et al. Superconducting single-photon ultrathin NbN film detector. Quantum Electronics. 2005;35(8):698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
|
|
Maslennikov SN, Finkel MI, Antipov SV, Polyakov SL, Zhang W, Ozhegov R, et al. Spiral antenna coupled and directly coupled NbN HEB mixers in the frequency range from 1 to 70 THz. In: Proc. 17th Int. Symp. Space Terahertz Technol. Paris, France; 2006. p. 177–9.
Abstract: We investigate both antenna coupled and directly coupled HEB mixers at several LO frequencies within the range of 2.5 THz to 70 THz. H20 (2.5+10.7 THz), and CO2 (30 THz) gas discharge lasers are used as the local oscillators. The noise temperature of antenna coupled mixers is measured at LO frequencies of 2.5 THz, 3.8 THz, and 30 THz. The results for both antenna coupled and directly coupled mixer types are compared. The devices with in—plane dimensions of 5x5 ,um 2 are pumped by LO radiation at 10.7 THz. The directly coupled HEB demonstrates nearly flat dependence of responsivity on frequency in the range of 25+64 THz.
|
|
|
Smirnov K, Korneev A, Minaeva O, Divochiy A, Tarkhov M, Ryabchun S, et al. Ultrathin NbN film superconducting single-photon detector array. In: J. Phys.: Conf. Ser. Vol 61.; 2007. p. 1081–5.
Abstract: We report on the fabrication process of the 2 × 2 superconducting single-photon detector (SSPD) array. The SSPD array is made from ultrathin NbN film and is operated at liquid helium temperatures. Each detector is a nanowire-based structure patterned by electron beam lithography process. The advances in fabrication technology allowed us to produce highly uniform strips and preserve superconducting properties of the unpatterned film. SSPD exhibit up to 30% quantum efficiency in near infrared and up to 1% at 5-μm wavelength. Due to 120 MHz counting rate and 18 ps jitter, the time-domain multiplexing read-out is proposed for large scale SSPD arrays. Single-pixel SSPD has already found a practical application in non-invasive testing of semiconductor very-large scale integrated circuits. The SSPD significantly outperformed traditional single-photon counting avalanche diodes.
|
|
|
Semenov A, Richter H, Smirnov K, Voronov B, Gol'tsman G, Hübers H-W. The development of terahertz superconducting hot-electron bolometric mixers. Supercond Sci Technol. 2004;17(5):436–9.
Abstract: We present recent advances in the development of NbN hot-electron bolometric (HEB) mixers for flying terahertz heterodyne receivers. Three important issues have been addressed: the quality of the source NbN films, the effect of the bolometer size on the spectral properties of different planar feed antennas, and the local oscillator (LO) power required for optimal operation of the mixer. Studies of the NbN films with an atomic force microscope indicated a surface structure that may affect the performance of the smallest mixers. Measured spectral gain and noise temperature suggest that at frequencies above 2.5 THz the spiral feed provides better overall performance than the double-slot feed. Direct measurements of the optimal LO power support earlier estimates made in the framework of the uniform mixer model.
|
|
|
Cherednichenko S, Kroug M, Merkel H, Kollberg E, Loudkov D, Smirnov K, et al. Local oscillator power requirement and saturation effects in NbN HEB mixers. In: Jet Propulsion Laboratory CIit.u.t.e of T, editor. Proc. 12th Int. Symp. Space Terahertz Technol. San Diego, CA, USA; 2001. p. 273–85.
Abstract: The local oscillator power required for NbN hot-electron bolometric mixers (P LO ) was investigated with respect to mixer size, critical temperature and ambient temperature. P LO can be decreased by a factor of 10 as the mixer size decreases from 4×0.4 µm 2 to 0.6×0.13 µm 2 . For the smallest volume mixer the optimal local oscillator power was found to be 15 nW. We found that for such mixer no signal compression was observed up to an input signal of 2 nW which corresponds to an equivalent input load of 20,000 K. For a constant mixer volume, reduction of T c can decrease optimal local oscillator power at least by a factor of 2 without a deterioration of the receiver noise temperature. Bath temperature was found to have minor effect on the receiver characteristics.
|
|
|
Vahtomin YB, Finkel MI, Antipov SV, Voronov BM, Smirnov KV, Kaurova NS, et al. Gain bandwidth of phonon-cooled HEB mixer made of NbN thin film with MgO buffer layer on Si. In: Harvard university, editor. Proc. 13th Int. Symp. Space Terahertz Technol. Cambridge, MA, USA; 2002. p. 259–70.
Abstract: We present recently obtained values for gain bandwidth of NbN HEB mixers for different substrates and film thicknesses and for MgO buffer layer on Si at LO frequency of 0.85-1 THz. The maximal bandwidth, 5.2 GHz, was achieved for the device on MgO buffer layer on Si with a 2 nm thick NbN film. Functional devices based on NbN films of such thickness were fabricated for the first time due to an improvement of superconducting properties of NbN film deposited on MgO buffer layer on Si substrate.
|
|
|
Meledin D, Tong CY-E, Blundell R, Kaurova N, Smirnov K, Voronov B, et al. The sensitivity and IF bandwidth of waveguide NbN hot electron bolometer mixers on MgO buffer layers over crystalline quartz. In: Harvard university, editor. Proc. 13th Int. Symp. Space Terahertz Technol. Cambridge, MA, USA; 2002. p. 65–72.
Abstract: We have developed and characterized waveguide phonon-cooled NbN Hot Electron Bolometer (FMB) mixers fabricated from a 3-4 nm thick NbN film deposited on a 200nm thick MgO buffer layer over crystalline quartz. Double side band receiver noise temperatures of 900-1050 K at 1.035 THz, and 1300-1400 K at 1.26 THz have been measured at an intermediate frequency of 1.5 GHz. The intermediate frequency bandwidth, measured at 0.8 THz LO frequency, is 3.2 GHz at the optimal bias point for low noise receiver operation.
|
|
|
Verevkin A, Zhang J, Sobolewski R, Lipatov A, Okunev O, Chulkova G, et al. Detection efficiency of large-active-area NbN single-photon superconducting detectors in the ultraviolet to near-infrared range. Appl. Phys. Lett.. 2002;80(25):4687–9.
Abstract: We report our studies on spectral sensitivity of meander-type, superconducting NbN thin-film single-photon detectors (SPDs), characterized by GHz counting rates of visible and near-infrared photons and negligible dark counts. Our SPDs exhibit experimentally determined quantum efficiencies ranging from ∼0.2% at the 1.55 μm wavelength to ∼70% at 0.4 μm. Spectral dependences of the detection efficiency (DE) at the 0.4 to 3.0-μm-wavelength range are presented. The exponential character of the DE dependence on wavelength, as well as its dependence versus bias current, is qualitatively explained in terms of superconducting fluctuations in our ultrathin, submicron-width superconducting stripes. The DE values of large-active-area NbN SPDs in the visible range are high enough for modern quantum communications.
|
|
|
Meledin D, Tong CY-E, Blundell R, Kaurova N, Smirnov K, Voronov B, et al. Study of the IF bandwidth of NbN HEB mixers based on crystalline quartz substrate with an MgO buffer layer. IEEE Trans Appl Supercond. 2003;13(2):164–7.
Abstract: In this paper, we present the results of IF bandwidth measurements on 3-4 nm thick NbN hot electron bolometer waveguide mixers, which have been fabricated on a 200-nm thick MgO buffer layer deposited on a crystalline quartz substrate. The 3-dB IF bandwidth, measured at an LO frequency of 0.81 THz, is 3.7 GHz at the optimal bias point for low noise receiver operation. We have also made measurements of the IF dynamic impedance, which allow us to evaluate the intrinsic electron temperature relaxation time and self-heating parameters at different bias conditions.
|
|