Khosropanah P. NbN and NbTiN hot electron bolometer THz mixers [Ph.D. thesis]. Göteborg: Chalmers University of Technology; 2003.
Abstract: The thesis reports the development of Hot Electron Bolometer (HEB) mixers for radio astronomy heterodyne receivers in THz frequency range. Part of this work is the fabrication of HEB devices, which are based on NbN or NbTiN superconducting thin films (â‰<a4>5 nm). They are integrated with wideband spiral or double-slot planar antennas. The mixer chips are incorporated into a quasi-optical receiver. The experimental part of this work focuses on the characterization of the receiver as a whole, and the HEB mixers as a part. Double side band receiver noise temperature and the IF bandwidth are reported for frequencies from 0.7 THz up to 2.6 THz. The spectrum of the direct response of HEB integrated with dierent antennas are measured using Fourier Transform Spectrometer (FTS). The effect of the bolometer size on total receiver performance and the LO power requirements is also discussed. A high-yield and reliable process for fabrication of NbN HEB mixers have been achieved. Over 100 devices with different bolometer geometry, film property and also different antennas have been fabricated and measured. The measured data enables us to discuss the impact of different parameters to the receiver overall performance.
This work has provided NbN HEB mixers to the following receivers:
TREND (Terahertz REceiver with NbN HEB Device) operating at 1.25-1.5 THz, installed in AST/RO Submillimeter Wave Telescope, Amundsen/Scott South Pole Station, in 2002-2003.
Band 6-low (1.410-1.700 THz) and 6-high (1.700-1.920 THz) of the HIFI (Heterodyne Instrument for Far Infra-red) in the Herschel Space Observatory, due to launch in 2007 by ESA (European Space Agency).
Besides, there has been continuous efforts to develop better models to explain the mixer performance more accurately. They are based on two temperature model for electrons and phonons and solving one-dimensional heat balance equations along the bolometer. The principles of these models are illustrated and the calculated results are compared with measured data.
Keywords: HEB mixer, hot electron bolometer mixer, NbN, NbTiN, superconducting detector, heterodyne receiver, THz mixer, submillimeter mixer, quasioptical receiver, double slot antenna, twin slot antenna, spiral antenna, receiver noise, FTS, Fourier Transform Spectrometer
|
|
|
Смирнов КВ. Энергетическая релаксация электронов в 2D-канале гетеропереходов GAAS/ALGAAS и транспортные процессы в структурах полупроводник-сверхпроводник на их основе [Ph.D. thesis].; 2000.
Abstract: Диссертация посвящена изучению электрон-фононного взаимодействия в двумерном электронном газе, образующемся на границе раздела полупроводников AlGaAs и GaAs, а также созданию на основе гетероперехода GaAs/AlGaAs и сверхпроводника NbN гибридных структур сверхпроводник-полупроводник-сверхпроводник и изучению их электрофизических свойств.
|
|
|
Hajenius M, Baselmans JJA, Gao JR, Klapwijk TM, de Korte PAJ, Voronov B, et al. Low noise NbN superconducting hot electron bolometer mixers at 1.9 and 2.5 THz. Supercond Sci Technol. 2004;17(5):S224–S228.
Abstract: NbN phonon-cooled hot electron bolometer mixers (HEBs) have been realized with negligible contact resistance between the bolometer itself and the contact structure. Using a combination of in situ cleaning of the NbN film and the use of an additional superconducting interlayer of a 10 nm NbTiN layer between the Au of the contact structure and the NbN film superior noise temperatures have been obtained as low as 950 K at 2.5 THz and 750 K at 1.9 THz. Here we address in detail the DC characterization of these devices, the interface transparencies between the bolometers and the contacts and the consequences of these factors on the mixer performance.
|
|
|
Ryabchun SA, Tretyakov IV, Finkel MI, Maslennikov SN, Kaurova NS, Seleznev VA, et al. Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In: Proc. 19th Int. Symp. Space Terahertz Technol. Groningen, Netherlands; 2008. p. 62–7.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
Baselmans J, Kooi J, Baryshev A, Yang ZQ, Hajenius M, Gao JR, et al. Full characterization of small volume NbN HEB mixers for space applications. In: Proc. 16th Int. Symp. Space Terahertz Technol. Göteborg, Sweden; 2005. p. 457–62.
Abstract: NbN phonon cooled HEB’s are one of the most promising bolometer mixer technologies for (near) future (space) applications. Their performance is usually quantified by mea- suring the receiver noise temperature at a given IF frequency, usually around 1 – 2 GHz. However, for any real applications it is vital that one fully knows all the relevant properties of the mixer, including LO power, stability, direct detection, gain bandwidth and noise bandwidth, not only the noise temperature at low IF frequencies. To this aim we have measured all these parameters at the optimal operating point of one single, small volume quasioptical NbN HEB mixer. We find a minimum noise temperature of 900 K at 1.46 THz. We observe a direct detection effect indicated by a change in bias current when changing from a 300 K hot load to a 77 K cold load. Due to this effect we overestimate the noise temperature by about 22% using a 300 K hot load and a 77 K cold load. The LO power needed to reach the optimal operating point is 80 nW at the receiver lens front, 59 nW inside the NbN bridge. However, using the isothermal technique we find a power absorbed in the NbN bridge of 25 nW, a difference of about a factor 2. We obtain a gain bandwidth of 2.3 GHz and a noise bandwidth of 4 GHz. The system Allan time is about 1 sec. in a 50 MHz spectral bandwidth and a deviation from white noise integration (governed by the radiometer equation) occurs at 0.2 sec., which implies a maximum integration time of a few seconds in a 1 MHz bandwidth spectrometer.
|
|
|
Finkel MI, Maslennikov SN, Vachtomin YB, Svechnikov SI, Smirnov KV, Seleznev VA, et al. Hot electron bolometer mixer for 20 – 40 THz frequency range. In: Proc. 16th Int. Symp. Space Terahertz Technol. Göteborg, Sweden; 2005. p. 393–7.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
Gol'tsman GN, Vachtomin YB, Antipov SV, Finkel MI, Maslennikov SN, Smirnov KV, et al. NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In: Proc. SPIE. Vol 5727.; 2005. p. 95–106.
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
|
|
Sobolewski R, Xu Y, Zheng X, Williams C, Zhang J, Verevkin A, et al. Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans Electron. 2002;E85-C(3):797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
|
|
Корнеев АА, Минаева О, Рубцова И, Милостная И, Чулкова Г, Воронов Б, et al. Сверхпроводящий однофотонный детектор на основе ультратонкой пленки NbN. Квантовая электроника. 2005;35(8):698–700.
Abstract: Представлены результаты исследований сверхпроводящих однофотонных детекторов, изготовленных из ультратонкой пленки NbN. Развитие технологического процесса изготовления детекторов, а также снижение рабочей температуры до 2 К позволили существенно увеличить квантовую эффективность: для видимого света (λ = 0.56 мкм) она составила 30%–40%, т.е. достигла предела, определяемого коэффициентом поглощения пленки. С ростом длины волны квантовая эффективность экспоненциально падает, составляя ~20% на λ=1.55 мкм и ~0.02% на λ = 5 мкм. При скорости темнового счета ~10-4s-1 экспериментально измеренная эквивалентная мощность шума составила 1.5 × 10-20 Вт/Гц-1/2; в дальнейшем она может быть уменьшена до рекордно низкого значения 5 × 10-21 Вт/Гц-1/2. Временное разрешение детектора равно 30 пс.
|
|
|
Korneev A, Minaeva O, Rubtsova I, Milostnaya I, Chulkova G, Voronov B, et al. Superconducting single-photon ultrathin NbN film detector. Quantum Electronics. 2005;35(8):698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
|