Ryabchun SA, Tretyakov IV, Finkel MI, Maslennikov SN, Kaurova NS, Seleznev VA, et al. Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In: Proc. 19th Int. Symp. Space Terahertz Technol. Groningen, Netherlands; 2008. p. 62–7.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
|
Smirnov AV, Larionov PA, Finkel MI, Maslennikov SN, Voronov BM, Gol'tsman GN. NbZr films for THz phonon-cooled HEB mixers. In: Proc. 19th Int. Symp. Space Terahertz Technol. Groningen, Netherlands; 2008. p. 44–7.
|
|
|
|
Baselmans J, Kooi J, Baryshev A, Yang ZQ, Hajenius M, Gao JR, et al. Full characterization of small volume NbN HEB mixers for space applications. In: Proc. 16th Int. Symp. Space Terahertz Technol. Göteborg, Sweden; 2005. p. 457–62.
Abstract: NbN phonon cooled HEB’s are one of the most promising bolometer mixer technologies for (near) future (space) applications. Their performance is usually quantified by mea- suring the receiver noise temperature at a given IF frequency, usually around 1 – 2 GHz. However, for any real applications it is vital that one fully knows all the relevant properties of the mixer, including LO power, stability, direct detection, gain bandwidth and noise bandwidth, not only the noise temperature at low IF frequencies. To this aim we have measured all these parameters at the optimal operating point of one single, small volume quasioptical NbN HEB mixer. We find a minimum noise temperature of 900 K at 1.46 THz. We observe a direct detection effect indicated by a change in bias current when changing from a 300 K hot load to a 77 K cold load. Due to this effect we overestimate the noise temperature by about 22% using a 300 K hot load and a 77 K cold load. The LO power needed to reach the optimal operating point is 80 nW at the receiver lens front, 59 nW inside the NbN bridge. However, using the isothermal technique we find a power absorbed in the NbN bridge of 25 nW, a difference of about a factor 2. We obtain a gain bandwidth of 2.3 GHz and a noise bandwidth of 4 GHz. The system Allan time is about 1 sec. in a 50 MHz spectral bandwidth and a deviation from white noise integration (governed by the radiometer equation) occurs at 0.2 sec., which implies a maximum integration time of a few seconds in a 1 MHz bandwidth spectrometer.
|
|
|
|
Finkel MI, Maslennikov SN, Vachtomin YB, Svechnikov SI, Smirnov KV, Seleznev VA, et al. Hot electron bolometer mixer for 20 – 40 THz frequency range. In: Proc. 16th Int. Symp. Space Terahertz Technol. Göteborg, Sweden; 2005. p. 393–7.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
|
Maslennikov SN, Finkel MI, Antipov SV, Polyakov SL, Zhang W, Ozhegov R, et al. Spiral antenna coupled and directly coupled NbN HEB mixers in the frequency range from 1 to 70 THz. In: Proc. 17th Int. Symp. Space Terahertz Technol. Paris, France; 2006. p. 177–9.
Abstract: We investigate both antenna coupled and directly coupled HEB mixers at several LO frequencies within the range of 2.5 THz to 70 THz. H20 (2.5+10.7 THz), and CO2 (30 THz) gas discharge lasers are used as the local oscillators. The noise temperature of antenna coupled mixers is measured at LO frequencies of 2.5 THz, 3.8 THz, and 30 THz. The results for both antenna coupled and directly coupled mixer types are compared. The devices with in—plane dimensions of 5x5 ,um 2 are pumped by LO radiation at 10.7 THz. The directly coupled HEB demonstrates nearly flat dependence of responsivity on frequency in the range of 25+64 THz.
|
|
|
|
Gol'tsman G, Korneev A, Minaeva O, Antipov A, Divochiy A, Kaurova N, et al. Middle-infrared to visible-light ultrafast superconducting single-photon detector. In: Proc. ASC. Seattle; 2006.
|
|
|
|
Гершензон ЕМ. Воздействие электромагнитного излучения на сверхпроводящую плёнку ниобия в резистивном состоянии. In: Тезисы докладов 22 Всесоюзной конференции по физике низких температур.; 1982. p. 79–80.
|
|
|
|
Karasik BS, Elantiev AI. Analysis of the noise performance of a hot-electron superconducting bolometer mixer. In: Proc. 6th Int. Symp. Space Terahertz Technol. ; 1995. p. 229–46.
Abstract: A theoretical analysis for the noise temperature of hot–electron superconducting mixer has been presented. Thecontributions of both Johnson noise and electron temperature fluctuations have been evaluated. A set of criteriaensuring low noise performance of the mixer has been stated and a simple analytic expression for the noisetemperature of the mixer device has been suggested. It has been shown that an improvement of the mixer sensitivitydoes not necessarily follow by a decrease of the bandwidth. An SSB noise temperature limit due to the intrinsic noisemechanisms has been estimated to be as low as 40–90 K for a mixer device made from Nb or NbN thin film.Furthermore, the conversion gain bandwidth can be as wide as is allowed by the intrinsic electron temperaturerelaxation time if an appropriate choice of the mixer resistance has been made. The intrinsic mixer noise bandwidthis of 3 GHz for Nb device and of 5 GHz for NbN device. An additional improvement of the theory has been madewhen a distinction between the impedance measured at high intermediate frequency (larger than the mixerbandwidth) and the mixer ohmic resistance has been taken into account.Recently obtained experimental data on Nb and NbNbolometer mixer devices are viewed in connection with thetheoretical predictions.The noise temperature limit has also been specified for the mixer device where an outdiffusion coolingmechanism rather than the electron–phonon energy relaxation determines the mixer bandwidth. A consideration ofthe noise performance of a bolometer mixer made from YBaCuO film utilizing a hot–electron effect has been done.
|
|
|
|
Yagubov P, Gol'tsman G, Voronov B, Seidman L, Siomash V, Cherednichenko S, et al. The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In: Proc. 7th Int. Symp. Space Terahertz Technol. Charlottesville, Virginia, USA; 1996. p. 290–302.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|
|
|
Cherednichenko S, Yagoubov P, Il'In K, Gol'tsman G, Gershenzon E. Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In: Proc. 8th Int. Symp. Space Terahertz Technol.; 1997. p. 245–57.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|