Yang ZQ, Hajenius M, Baselmans JJA, Gao JR, Voronov B, Gol’tsman GN. Reduced noise in NbN hot-electron bolometer mixers by annealing. Supercond Sci Technol. 2006;19(4):L (9 to 12).
Abstract: We find that the sensitivity of heterodyne receivers based on superconducting hot-electron bolometers (HEBs) increases by 25–30% after annealing at 85 °C in vacuum. The devices studied are twin-slot antenna coupled mixers with a small NbN bridge of 1 × 0.15 µm2. We show that annealing changes the device properties as reflected in sharper resistive transitions of the complete device, apparently reducing the device-related noise. The lowest receiver noise temperature of 700 K is measured at a local oscillator frequency of 1.63 THz and a bath temperature of 4.3 K.
|
|
|
Hajenius M, Baselmans JJA, Gao JR, Klapwijk TM, de Korte PAJ, Voronov B, et al. Low noise NbN superconducting hot electron bolometer mixers at 1.9 and 2.5 THz. Supercond Sci Technol. 2004;17(5):S224–S228.
Abstract: NbN phonon-cooled hot electron bolometer mixers (HEBs) have been realized with negligible contact resistance between the bolometer itself and the contact structure. Using a combination of in situ cleaning of the NbN film and the use of an additional superconducting interlayer of a 10 nm NbTiN layer between the Au of the contact structure and the NbN film superior noise temperatures have been obtained as low as 950 K at 2.5 THz and 750 K at 1.9 THz. Here we address in detail the DC characterization of these devices, the interface transparencies between the bolometers and the contacts and the consequences of these factors on the mixer performance.
|
|
|
Semenov A, Richter H, Smirnov K, Voronov B, Gol'tsman G, Hübers H-W. The development of terahertz superconducting hot-electron bolometric mixers. Supercond Sci Technol. 2004;17(5):436–9.
Abstract: We present recent advances in the development of NbN hot-electron bolometric (HEB) mixers for flying terahertz heterodyne receivers. Three important issues have been addressed: the quality of the source NbN films, the effect of the bolometer size on the spectral properties of different planar feed antennas, and the local oscillator (LO) power required for optimal operation of the mixer. Studies of the NbN films with an atomic force microscope indicated a surface structure that may affect the performance of the smallest mixers. Measured spectral gain and noise temperature suggest that at frequencies above 2.5 THz the spiral feed provides better overall performance than the double-slot feed. Direct measurements of the optimal LO power support earlier estimates made in the framework of the uniform mixer model.
|
|
|
Semenov AD, Gol'tsman GN, Sobolewski R. Hot-electron effect in superconductors and its applications for radiation sensors. Supercond Sci Technol. 2002;15(4):R1–R16.
Abstract: The paper reviews the main aspects of nonequilibrium hot-electron phenomena in superconductors and various theoretical models developed to describe the hot-electron effect. We discuss implementation of the hot-electron avalanche mechanism in superconducting radiation sensors and present the most successful practical devices, such as terahertz mixers and direct intensity detectors, for far-infrared radiation. Our presentation also includes the novel approach to hot-electron quantum detection implemented in superconducting x-ray to optical photon counters.
|
|
|
Uzawa Y, Miki S, Wang Z, Kawakami A, Kroug M, Yagoubov P, et al. Performance of a quasi-optical NbN hot-electron bolometric mixer at terahertz frequencies. Supercond Sci Technol. 2002;15(1):141–5.
|
|
|
Lipatov A, Okunev O, Smirnov K, Chulkova G, Korneev A, Kouminov P, et al. An ultrafast NbN hot-electron single-photon detector for electronic applications. Supercond Sci Technol. 2002;15(12):1689–92.
Abstract: We present the latest generation of our superconducting single-photon detector (SPD), which can work from ultraviolet to mid-infrared optical radiation wavelengths. The detector combines a high speed of operation and low jitter with high quantum efficiency (QE) and very low dark count level. The technology enhancement allows us to produce ultrathin (3.5 nm thick) structures that demonstrate QE hundreds of times better, at 1.55 μm, than previous 10 nm thick SPDs. The best, 10 × 10 μm2, SPDs demonstrate QE up to 5% at 1.55 μm and up to 11% at 0.86 μm. The intrinsic detector QE, normalized to the film absorption coefficient, reaches 100% at bias currents above 0.9 Ic for photons with wavelengths shorter than 1.3 μm.
|
|
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Schubert J, Hübers H-W. NbN hot electron bolometric mixers at frequencies between 0.7 and 3.1 THz. Supercond Sci Technol. 1999;12(11):989–91.
Abstract: The performance of NbN-based phonon-cooled hot electron bolometric (HEB) quasioptical mixers is investigated in the 0.7-3.1 THz frequency range. The devices are made from a 3.5-4 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The length of the bolometer microbridge is 0.1-0.2 µm; the width is 1-2 µm. The best results of the DSB receiver noise temperature measured at 1.5 GHz intermediate frequency are: 800 K at 0.7 THz, 1100 K at 1.6 THz, 2000 K at 2.5 THz and 4200 K at 3.1 THz. The measurements were performed with a far infrared laser as the local oscillator (LO) source. The estimated LO power requirement is less than 500 nW at the receiver input. First results on spiral antenna polarization measurements are reported.
|
|
|
Il'in KS, Verevkin AA, Gol'tsman GN, Sobolewski R. Infrared hot-electron NbN superconducting photodetectors for imaging applications. Supercond Sci Technol. 1999;12(11):755–8.
Abstract: We report an effective quantum efficiency of 340, responsivity >200 A W-1 (>104 V W-1) and response time of 27±5 ps at temperatures close to the superconducting transition for NbN superconducting hot-electron photodetectors (HEPs) in the near-infrared and optical ranges. Our studies were performed on a few nm thick NbN films deposited on sapphire substrates and patterned into µm-size multibridge detector structures, incorporated into a coplanar transmission line. The time-resolved photoresponse was studied by means of subpicosecond electro-optic sampling with 100 fs wide laser pulses. The quantum efficiency and responsivity studies of our photodetectors were conducted using an amplitude-modulated infrared beam, fibre-optically coupled to the device. The observed picosecond response time and the very high efficiency and sensitivity of the NbN HEPs make them an excellent choice for infrared imaging photodetectors and input optical-to-electrical transducers for superconducting digital circuits.
|
|
|
Rönnung F, Cherednichenko S, Winkler D, Gol'tsman GN. A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond Sci Technol. 1999;12(11):853–5.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
Danerud M, Winkler D, Lindgren M, Zorin M, Trifonov V, Karasik B, et al. A fast infrared detector based on patterned YBCO thin film. Supercond Sci Technol. 1994;7(5):321–3.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
|