Cherednichenko S, Yagoubov P, Il'in K, Gol'tsman G, Gershenzon E. Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers. In: Proc. 27th Eur. Microwave Conf. Vol 2. IEEE; 1997. p. 972–7.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 nm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 um wide and 2 um long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.2 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
Il'in K, Siegel M, Semenov A, Engel A, Hübers H-W, Hollmann E, et al. Thickness dependence of superconducting properties of ultrathin Nb and NbN films. In: AKF-Frühjahrstagung.; 2004.
|
|
Karasik BS, Il'in KS, Pechen EV, Krasnosvobodtsev SI. Diffusion cooling mechanism in a hot-electron NbC microbolometer mixer. Appl Phys Lett. 1996;68(16):2285–7.
|
Il'in KS, Lindgren M, Currie MA, Semenov D, Gol'tsman GN, Sobolewski R, et al. Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl Phys Lett. 2000;76(19):2752–4.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
Inderbitzin K, Engel A, Schilling A, Il'in K, Siegel M. An ultra-fast superconducting Nb nanowire single-photon detector for soft x-rays. Appl Phys Lett. 2012;101.
Abstract: Although superconducting nanowire single-photon detectors (SNSPDs) are well studied regarding the
detection of infrared/optical photons and keV-molecules, no studies on continuous x-ray photon
counting by thick-film detectors have been reported so far. We fabricated a 100 nm thick niobium
x-ray SNSPD (an X-SNSPD) and studied its detection capability of photons with keV-energies in
continuous mode. The detector is capable to detect photons even at reduced bias currents of 0.4%,
which is in sharp contrast to optical thin-film SNSPDs. No dark counts were recorded in extended
measurement periods. Strikingly, the signal amplitude distribution depends significantly on the photon
energy spectrum.VC
|