Goltsman GN, Korneev AA, Finkel MI, Divochiy AV, Florya IN, Korneeva YP, et al. Superconducting hot-electron bolometer as THz mixer, direct detector and IR single-photon counter [abstract]. In: 35th Int. Conf. Infrared, Millimeter, and Terahertz Waves.; 2010. p. 1.
Abstract: We present a new generation of superconducting single-photon detectors (SSPDs) and hot-electron superconducting sensors with record characteristic for many terahertz and optical applications.
|
Goltsman G, Korneev A, Divochiy A, Minaeva O, Tarkhov M, Kaurova N, et al. Ultrafast superconducting single-photon detector. J Modern Opt. 2009;56(15):1670–80.
Abstract: The state-of-the-art of the NbN nanowire superconducting single-photon detector technology (SSPD) is presented. The SSPDs exhibit excellent performance at 2 K temperature: 30% quantum efficiency from visible to infrared, negligible dark count rate, single-photon sensitivity up to 5.6 µm. The recent achievements in the development of GHz counting rate devices with photon-number resolving capability is presented.
|
Gol’tsman G, Korneev A, Tarkhov M, Seleznev V, Divochiy A, Minaeva O, et al. Middle-infrared ultrafast superconducting single photon detector. In: 32nd IRMW / 15th ICTE.; 2007. p. 115–6.
Abstract: We present the results of the research on quantum efficiency of the ultrathin-film superconducting single-photon detectors (SSPD) in the wavelength rage from 1 mum to 5.7 mum. Reduction of operation temperature to 1.6 K allowed us to measure quantum efficiency of ~1 % at 5.7 mum wavelength with the SSPD made from 4-nm-thick NbN film. In a pursuit of further performance improvement we endeavored SSPD fabricating from 4-nm-thick MoRe film as an alternative material. The MoRe film exhibited transition temperature of 7.7K, critical current density at 4.2 K temperature was 1.1times10 6 A/cm 2 , and diffusivity 1.73 cmVs. The single-photon response was observed with MoRe SSPD at 1.3 mum wavelength with quantum efficiency estimated to be 0.04%.
|
Gurovich BA, Tarkhov MA, Prikhod'ko KE, Kuleshova EA, Komarov DA, Stolyarov VL, et al. Controlled modification of superconducting properties of NbN ultrathin films under composite ion beam irradiation. Nanotechnologies in Russia. 2014;9(7):386–90.
Abstract: In this work, the results of studying the microstructure and superconducting properties of ultrathin films on the basis of NbN in the initial state and after modification by being subjecting to composite ion beam irradiation with the energy ~1–3) keV are presented. HRTEM analysis showed that the initial films on the sapphire substrate in orientation “c-cut†are characterized by a grain size essentially exceeding the film thickness, while on the other substrates the size of grains corresponds to the thickness of film. Using XPS analysis, it was shown that in the initial films the atomic ratio of Nb and N is 0.51/0.49, respectively, the percentage of oxygen being lower than 5%. For ultrathin films 5 nm in thickness, the critical temperature of transit to superconducting state (T c) is found to be ~3.6 K and the density of critical current is jc ~8MA/cm2. In the work it is experimentally determined that the irradiation of NbN films by composite ion beams leads to the controlled modification of its superconducting properties due to the process of selective substitution of nitrogen atoms on the oxygen atoms.
|
Kardakova A, Finkel M, Morozov D, Kovalyuk V, An P, Dunscombe C, et al. The electron-phonon relaxation time in thin superconducting titanium nitride films. Appl Phys Lett. 2013;103(25):252602 (1 to 4).
Abstract: We report on the direct measurement of the electron-phonon relaxation time, τeph, in disordered TiN films. Measured values of τeph are from 5.5 ns to 88 ns in the 4.2 to 1.7 K temperature range and consistent with a T−3 temperature dependence. The electronic density of states at the Fermi level N0 is estimated from measured material parameters. The presented results confirm that thin TiN films are promising candidate-materials for ultrasensitive superconducting detectors.
The work was supported by the Ministry of Education and Science of the Russian Federation, Contract No. 14.B25.31.0007 and by the RFBR Grant No. 13-02-91159.
|