Gershenzon EM, Gol’tsman GN, Dzardanov AL, Zorin MA. Ultrafast superconductive switch. IEEE Trans Magn. 1991;27(2):2844–6.
Abstract: The transition from superconductive to resistive state caused by infrared radiation and bias current pulses was investigated in order to minimize switching time tau and driving power W. Experimental results for Nb microstrips confirm the correctness of calculations based on the model of electron heating. For Nb switches, tau measured directly is 0.3-0.8 ns for radiation pulses and 1-3 ns for bias current pulses at T=4.2 K, while for YBaCuO switches at T=77 K it is expected to be several picoseconds. For an YBaCuO sample with the dimensions of 5*2*0.15 mu m/sup 2/, W was 10 mW, and it can be further reduced to the order of several microwatts by decreasing the volume of the sample.
|
|
|
Gershenzon EM, Gol’tsman GN, Gousev YP, Elant’ev AI, Semenov AD. Electromagnetic radiation mixer based on electron heating in resistive state of superconductive Nb and YBaCuO films. IEEE Trans Magn. 1991;27(2):1317–20.
Abstract: A theory of an electron-heating mixer which makes it possible to calculate all the characteristics of the device is developed. It is shown that positive conversion gain is possible for such a mixer in the millimeter to near-infrared wavelength range. The dynamic range and the optimum heterodyne power can be selected from a very wide interval by varying the mixing element volume. Measurements made for Nb within the frequency range of 120-750 GHz confirm the theory. The conversion loss obtained at T=1.6 K and normalized to the element reaches 0.3 dB in the intermediate frequency band of 40 MHz; the possible noise temperature is 50 K. The estimation of noise temperature and output band for YBaCuO at T=77 yields 200 K and more than 10 GHz, respectively.
|
|
|
Gershenzon EM, Gol’tsman GN, Semenov AD, Sergeev AV. Mechanism of picosecond response of granular YBaCuO films to electromagnetic radiation. IEEE Trans Magn. 1991;27(2):1321–4.
Abstract: Ultrafast mechanisms of radiation detection in granular YBaCuO films are studied in the wide wavelength range from millimeter waves to near infrared. With an increase in radiation frequency, the Josephson detection at the grain-boundary weak links is replaced by electron heating into the grains. This change occurs in the submillimeter wavelength range. The electron-phonon relaxation time tau /sub eph/ is determined from direct measurements, quasi-stationary electron heating measurements, and the frequency dependence of the current at which maximum voltage shift is observed. The temperature dependence of tau /sub eph/ at T<or=40 K was found to be tau /sub eph/ approximately T/sup -1/. The results show that detectors with a response time of a few picoseconds at nitrogen temperature are attainable.
|
|
|
Gershenzon EM, Gol’tsman GN, Sergeev A, Semenov AD. Picosecond response of YBaCuO films to electromagnetic radiation. In: Gorzkowski W, Gutowski M, Reich A, Szymczak H, editors. Proc. European Conf. High-Tc Thin Films and Single Crystals.; 1990. p. 457–62.
Abstract: Radiation-induced change of the resistance was studied in the resistive state of YBaCuO films. Electron-phonon relaxation time T h was determmed from direct ep measurements and analysis of quasistationary electron heating. Temperature dependence of That TS 40 K was found to – ep be T h.. T'. The resul ts show that ep detectors with the response time of few picosecond at nitrogen temperature can be realized.
|
|
|
Gol’tsman GN. The “Millimetron” project, a future space telescope mission [abstract]. In: Proc. 18th Int. Symp. Space Terahertz Technol.; 2007. 255.
Abstract: The goal of the Millimetron project is to develop a space observatory operating in the millimeter, sub-millimeter and infrared wavelength ranges using a 12-m actively cooled telescope in a single-dish mode and as an interferometer with the space-ground and space-space baselines (the later after the launch of the second identical space telescope). The Millimetron’s main reflector and other optics will be cooled down to 4K thus enabling astronomical observations with super high sensitivity in MM and subMM (down to nanoJansky level). Heterodyne observations in an interferometer mode at frequencies 0.1-1 THz will provide super high angular resolution. The main instruments, planned to be installed are wide-range imaging arrays, radiometers with spectrometers and polarimeters, VLBI heterodyne receivers, and Mikelson type interferometer devices. Wide-range MM and subMM imaging arrays and spectrometers will be based on a superconducting hot electron direct detectors with Andreev mirrors operating at 0.1 K. Such detectors are the best candidates to reach the noise equivalent power level of 10 -19 -10 -20 W/√Hz. Heterodyne receivers will be both SIS based superconducting integrated receiver with flux-flow oscillator as LO (0.1-0.9 THz range) and HEB based receivers using multiplied Gunn oscillator as LO for 1-2 THz range and quantum cascade lasers as LO for 2-5 THz range. For observations in middle IR region there will be installed large arrays of superconducting single photon detectors, providing imaging with very high dynamic range and ultimate sensitivity.
|
|