Sobolewski R, Zhang J, Slysz W, Pearlman A, Verevkin A, Lipatov A, et al. Ultrafast superconducting single-photon optical detectors. In: Spigulis J, Teteris J, Ozolinsh M, Lusis A, editors. Proc. SPIE. Vol 5123. SPIE; 2003. p. 1–11.
Abstract: We present a new class of single-photon devices for counting of both visible and infrared photons. Our superconducting single-photon detectors (SSPDs) are characterized by the intrinsic quantum efficiency (QE) reaching up to 100%, above 10 GHz counting rate, and negligible dark counts. The detection mechanism is based on the photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconducting stripe. The devices are fabricated from 3.5-nm-thick NbN films and operate at 4.2 K, well below the NbN superconducting transition temperature. Various continuous and pulsed laser sources in the wavelength range from 0.4 μm up to >3 μm were implemented in our experiments, enabling us to determine the detector QE in the photon-counting mode, response time, and jitter. For our best 3.5-nm-thick, 10×10 μm2-area devices, QE was found to reach almost 100% for any wavelength shorter than about 800 nm. For longer-wavelength (infrared) radiation, QE decreased exponentially with the photon wavelength increase. Time-resolved measurements of our SSPDs showed that the system-limited detector response pulse width was below 150 ps. The system jitter was measured to be 35 ps. In terms of the counting rate, jitter, and dark counts, the NbN SSPDs significantly outperform their semiconductor counterparts. Already identifeid and implemented applications of our devices range from noninvasive testing of semiconductor VLSI circuits to free-space quantum communications and quantum cryptography.
|
|
|
|
Smirnov K, Korneev A, Minaeva O, Divochiy A, Tarkhov M, Ryabchun S, et al. Ultrathin NbN film superconducting single-photon detector array. In: J. Phys.: Conf. Ser. Vol 61.; 2007. p. 1081–5.
Abstract: We report on the fabrication process of the 2 × 2 superconducting single-photon detector (SSPD) array. The SSPD array is made from ultrathin NbN film and is operated at liquid helium temperatures. Each detector is a nanowire-based structure patterned by electron beam lithography process. The advances in fabrication technology allowed us to produce highly uniform strips and preserve superconducting properties of the unpatterned film. SSPD exhibit up to 30% quantum efficiency in near infrared and up to 1% at 5-μm wavelength. Due to 120 MHz counting rate and 18 ps jitter, the time-domain multiplexing read-out is proposed for large scale SSPD arrays. Single-pixel SSPD has already found a practical application in non-invasive testing of semiconductor very-large scale integrated circuits. The SSPD significantly outperformed traditional single-photon counting avalanche diodes.
|
|
|
|
Smirnov K, Korneev A, Minaeva O, Divochij A, Rubtsova I, Antipov A, et al. Superconducting single-photon detector for near- and middle IR wavelength range. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 684–5.
Abstract: Presented in this paper are the results of research of NbN-film superconducting single-photon detector. At 2 K temperature, quantum efficiency in the visible light (0.56 mum) reaches 30-40 %. With the wavelength increase quantum efficiency decreases and comes to 20% at 1.55 mum and 0.02% at 5.6 mum. Minimum dark counts rate is 2times10-4s-1. The jitter of detector is 35 ps. The detector was successfully implemented for integrated circuits non-invasive optical testing. It is also perspective for quantum cryptography systems
|
|
|
|
Smirnov KV, Vachtomin YB, Ozhegov RV, Pentin IV, Slivinskaya EV, Korneev AA, et al. Fiber coupled single photon receivers based on superconducting detectors for quantum communications and quantum cryptography. In: Tománek P, Senderáková D, Hrabovský M, editors. Proc. SPIE. Vol 7138. Spie; 2008. 713827 (1 to 6).
Abstract: At present superconducting detectors become increasingly attractive for various practical applications. In this paper we present results on the depelopment of fiber coupled receiver systems for the registration of IR single photons, optimized for telecommunication and quantum-cryptography. These receiver systems were developed on the basis of superconducting single photon detectors (SSPD) of VIS and IR wavelength ranges. The core of the SSPD is a narrow ( 100 nm) and long ( 0,5 mm) strip in the form of a meander which is patterned from a 4-nm-thick NbN film (TC=10-11 K, jC= 5-7•106 A/cm2); the sensitive area dimensions are 10×10 μm2. The main problem to be solved while the receiver system development was optical coupling of a single-mode fiber (9 microns in diameter) with the SSPD sensitive area. Characteristics of the developed system at the optical input are as follows: quantum efficiency >10 % (at 1.3 μm), >4 % (at 1.55 μm); dark counts rate ≤1 s-1; duration of voltage pulse ≤5 ns; jitter ≤40 ps. The receiver systems have either one or two identical channels (for the case of carrying out correlation measurements) and are made as an insert in a helium storage Dewar.
|
|
|
|
Smirnov E, Golikov A, Zolotov P, Kovalyuk V, Lobino M, Voronov B, et al. Superconducting nanowire single-photon detector on lithium niobate. In: J. Phys.: Conf. Ser. Vol 1124.; 2018. 051025.
Abstract: We demonstrate superconducting niobium nitride nanowires folded on top of lithium niobate substrate. We report of 6% system detection efficiency at 20 s−1 dark count rate at telecommunication wavelength (1550 nm). Our results shown great potential for the use of NbN nanowires in the field of linear and nonlinear integrated quantum photonics.
|
|