Gershenzon EM, Gershenzon ME, Goltsman GN, Semenov AD, Sergeev AV. Wide-band highspeed Nb and YBaCuO detectors. IEEE Trans Magn. 1991;27(2):2836–9.
Abstract: The physical limitations on the response time and the nature of nonequilibrium detection of radiation were investigated for Nb and YBCO film in a wide spectral range from millimeter to near-infrared wavelengths. In the case of ideal heat removal from the film, the detection mechanism is connected with an electron heating effect which is not selective over a wide spectral interval. For Nb, the dependence of the response time on the electron mean free path l and temperature T is tau varies as T/sup -2/l/sup -1/. The values of detectivity D* and tau are 3*10/sup 11/ W/sup -1/ Hz/sup 1/2/ cm and 5*10/sup -9/ s at T=1.6 K, respectively. For YBCO film the tau value of 1-2 ps at T=77 K was obtained; the NEP value of 3*10/sup -11/ W-Hz/sup -1/2/ can be obtained at T=77 K in the case of the optimal film matching to the radiation.
|
|
|
Gol'tsman GN, Semenov AD, Gousev YP, Zorin MA, Gogidze IG, Gershenzon EM, et al. Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond Sci Technol. 1991;4(9):453–6.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
|
|
Verevkin A, Slysz W, Pearlman A, Zhang J, Sobolewski R, Okunev O, et al. Real-time GHz-rate counting of infrared photons using nanostructured NbN superconducting detectors. In: CLEO/QELS. Optical Society of America; 2003. CThM8.
Abstract: We demonstrate that our ultrathin, nanometer-width NbN superconducting single-photon detectors are capable of above 1-GHz-frequency, real-time counting of near-infrared photons. The measured system jitter of the detector is below 15 ps.
|
|
|
Il'in KS, Lindgren M, Currie MA, Semenov D, Gol'tsman GN, Sobolewski R, et al. Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl Phys Lett. 2000;76(19):2752–4.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
|
|
Minaeva O, Fraine A, Korneev A, Divochiy A, Goltsman G, Sergienko A. High resolution optical time-domain reflectometry using superconducting single-photon detectors. In: Frontiers in Opt. 2012/Laser Sci. XXVIII. Optical Society of America; 2012. Fw3a.39.
Abstract: We discuss the advantages and limitations of single-photon optical time-domain reflectometry with superconducting single-photon detectors. The higher two-point resolution can be achieved due to superior timing performance of SSPDs in comparison with InGaAs APDs.
|
|