Meledin D, Tong CY-E, Blundell R, Kaurova N, Smirnov K, Voronov B, et al. The sensitivity and IF bandwidth of waveguide NbN hot electron bolometer mixers on MgO buffer layers over crystalline quartz. In: Harvard university, editor. Proc. 13th Int. Symp. Space Terahertz Technol. Cambridge, MA, USA; 2002. p. 65–72.
Abstract: We have developed and characterized waveguide phonon-cooled NbN Hot Electron Bolometer (FMB) mixers fabricated from a 3-4 nm thick NbN film deposited on a 200nm thick MgO buffer layer over crystalline quartz. Double side band receiver noise temperatures of 900-1050 K at 1.035 THz, and 1300-1400 K at 1.26 THz have been measured at an intermediate frequency of 1.5 GHz. The intermediate frequency bandwidth, measured at 0.8 THz LO frequency, is 3.2 GHz at the optimal bias point for low noise receiver operation.
|
Verevkin A, Zhang J, Sobolewski R, Lipatov A, Okunev O, Chulkova G, et al. Detection efficiency of large-active-area NbN single-photon superconducting detectors in the ultraviolet to near-infrared range. Appl. Phys. Lett.. 2002;80(25):4687–9.
Abstract: We report our studies on spectral sensitivity of meander-type, superconducting NbN thin-film single-photon detectors (SPDs), characterized by GHz counting rates of visible and near-infrared photons and negligible dark counts. Our SPDs exhibit experimentally determined quantum efficiencies ranging from ∼0.2% at the 1.55 μm wavelength to ∼70% at 0.4 μm. Spectral dependences of the detection efficiency (DE) at the 0.4 to 3.0-μm-wavelength range are presented. The exponential character of the DE dependence on wavelength, as well as its dependence versus bias current, is qualitatively explained in terms of superconducting fluctuations in our ultrathin, submicron-width superconducting stripes. The DE values of large-active-area NbN SPDs in the visible range are high enough for modern quantum communications.
|
Cherednichenko S, Kroug M, Khosropanah P, Adam A, Merkel H, Kolberg E, et al. A broadband terahertz heterodyne receiver with an NbN HEB mixer. In: Harward University, editor. Proc. 13th Int. Symp. Space Terahertz Technol. Cambridge, MA, USA; 2002. p. 85–95.
Abstract: We present a broadband and low noise heterodyne receiver for 1.4-1.7 THz designed for the Hershel Space Observatory. A phonon- cooled NbN HEB mixer was integrated with a normal metal double- slot antenna and an elliptical silicon lens. DSB receiver noise temperature Tr was measured from 1 GHz through 8GHz intermediate frequency band with 50 MHz instantaneous bandwidth. At 4.2 K bath temperature and at 1.6 THz LO frequency Tr is 800 K with the receiver noise bandwidth of 5 GHz. While at 2 K bath temperature Tr was as low as 700 K. At 0.6 THz and 1.1 THz a spiral antenna integrated NbN HEB mixer showed the receiver noise temperature 500 K and 800 K, though no antireflection coating was used in this case. Tr of 1100 K was achieved at 2.5 THz while the receiver noise bandwidth was 4 GHz.
|
|
Norton P. HgCdTe infrared detectors. Opto-Electron Rev. 2002;10(3):159–74.
|
Zhou YD, Becker CR, Ashokan R, Selamet Y, Chang Y, Boreiko RT, et al. Progress in far-infrared detection technology. In: Proc. SPIE. Vol 4795.; 2002. p. 121–8. (Society of Photo-Optical Instrumentation Engineers (SPIE) Conference Series).
Abstract: II-VI intrinsic very long wavelength infrared (VLWIR, λc~20 to 50 μm) materials, HgCdTe alloys as well as HgCdTe/CdTe superlattices, were grown by molecular beam epitaxy (MBE). The layers were characterized by means of X-ray diffraction, conventional Fourier transform infrared spectroscopy, Hall effect measurements and transmittance electron microscopy (TEM). Photoconductor devices were processed and their spectral response was also measured to demonstrate their applicability in the VLWIR region.
|