Danerud M, Winkler D, Lindgren M, Zorin M, Trifonov V, Karasik BS, et al. Nonequilibrium and bolometric photoresponse in patterned YBa2Cu3O7−δ thin films. J Appl Phys. 1994;76(3):1902–9.
Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.
|
|
|
|
Lindgren M, Trifonov V, Zorin M, Danerud M, Winkler D, Karasik BS, et al. Transient resistive photoresponse of YBa2Cu3O7−δ films using low power 0.8 and 10.6 μm laser radiation. Appl Phys Lett. 1994;64(22):3036–8.
Abstract: Thin YBa2Cu3O7−δ laser deposited films were patterned into devices consisting of ten parallel 1 μm wide strips. Nonequilibrium picosecond and bolometric photoresponses were studied by the use of 17 ps full width at half‐maximum laser pulses and amplitude modulated radiation from an AlGaAs laser up to 10 GHz and from a CO2 laser up to 1 GHz. The time and frequency domain measurements were in agreement. The fast response can be explained by electron heating. The use of low optical power and a sensitive measurement system excluded any nonlinear transient processes and kinetic inductance changes in the superconducting state. At 1 GHz modulation frequency, the responsivity was ∼1.2 V/W both for 0.8 and 10.6 μm wavelengths. The sensitivity of a fast and spectrally broadband infrared detector is discussed.
|
|
|
|
Ekström H, Karasik B, Kollberg E, Yngvesson KS. Investigation of a superconducting hot electron mixer. In: Proc. 5th Int. Symp. Space Terahertz Technol.; 1994. p. 169–88.
Abstract: Mixing at 20 GHz in niobium superconducting thin film strips in the resistive state is studied. Experiments give evidence that electron-heating is the main cause of the non linear phenomena. The requirements on the mode of operation and on the film parameters for small conversion loss and the possibility of conversion gain are discussed. Measurements indicate a minimum intrinsic conversion loss around 1 dB with a sharp drop for the lowest voltage bias-points, and a DSB mixer noise temperature between 100 and 450 K at 20 GHz. The device output noise temperature at the mixer operating point can be as low as 30-50 K. A simple theory is presented, which is based on the assumption that the small signal resistance is linearly dependent on power. This type of mixer is considered very promising for use in low-noise heterodyne receivers at THz frequencies.
|
|
|
|
Gol'tsman G, Jacobsson S, Ekstrom H, Karasik B, Kollberg E, Gershenzon E. Slot-line tapered antenna with NbN hot electron mixer for 300-360 GHz operation. In: Proc. 5th Int. Symp. Space Terahertz Technol.; 1994. p. 209–213a.
Abstract: NbN hot-electron mixers combined with slot-line tapered antennas on Si wdnitride membranes had been fabricated. Several strips of 1 gm wide and 5 tan long made from 100 A NbN film are inserted into the slot antenna. IV-curves under local oscillator power in 300-350 GHz frequency range and conversion gain dependencies on intermediate fre- quency in the 0.1-1 GHz range are measured and compared with that for 100 GHz frequency band. Our results show that pumped IV-curves and intermediate frequency bands are different for 100 GHz and 300 GHz frequency ranges. The interpretation exploits the fact that for the lowest radiation frequency the superconducting energy gap is larger than the radiation quantum energy while they are comparable at the higher frequency. Tha results show that such mixers have good perspectives for terahertz receiving technology.
|
|
|
|
0kunev 0., Dzardanov A, Ekstrom H, Jacobsson S, Kollberg E, Gol'tsman G, et al. NbN hot electron waveguide mixer for 100 GHz operation. In: Proc. 5th Int. Symp. Space Terahertz Technol.; 1994. p. 214–24.
Abstract: NbN is a promising superconducting material used to develope hot- electron superconducting mixers with an IF bandwidth over 1 GHz. In the 100 GHz frequency range, the following parameters were obtained for NbN films 50 A thick: the noise temperature of the receiver (DSB) 1000 K; the conversion losses 10 d13, the IF bandwidth 1 GHz; the local oscillator power 1 /LW. An increase of NbN film thickness up to 80-100 A and increase of working temperature up to 7-8 K, and a better mixer matching may allow to broader the IF band up to 3 Gllz, to reduce the conversion losses down to 3-5 dB and the noise tempera- ture down to 200-300 K.
|
|