Cherednichenko S, Yagoubov P, Il'in K, Gol'tsman G, Gershenzon E. Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers. In: Proc. 27th Eur. Microwave Conf. Vol 2. IEEE; 1997. p. 972–7.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 nm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 um wide and 2 um long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.2 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
|
Merkel HF, Yagoubov PA, Kroug M, Khosropanah P, Kollberg EL, Gol’tsman GN, et al. Noise temperature and absorbed LO power measurement methods for NbN phonon-cooled hot electron bolometric mixers at terahertz frequencies. In: Proc. 28th European Microwave Conf. Vol 1.; 1998. p. 294–9.
Abstract: In this paper the absorbed LO power requirements and the noise performance of NbN based phonon-cooled hot electron bolometric (HEB) quasioptical mixers are investigated for RF frequencies in the 0.55-1.1 range The minimal measured DSB noise temperatures are about 500 K at 640 GHz, 600 K at 750 GHz, 850 K at 910 GHz and 1250 K at 1.1 THz. The increase in noise temperature at 1.1THz is attributed to water absorption. The absorbed LO power is measured using a calorimetric approach. The results are subsequently corrected for lattice heating. These values are compared to results of a novel one dimensional hot spot mixer models and to a more traditional isotherm method which tends to underestimate the absorbed LO power for small bias powers. Typically a LO power between 50nW and 100nW is needed to pump the device to the optimal operating point.
|
|
|
Kroug M, Yagoubov P, Gol'tsman G, Kollberg E. NbN quasioptical phonon cooled hot electron bolometric mixers at THz frequencies. In: Inst. Phys. Conf. Ser. Vol 1. Bristol; 1997. p. 405–8.
|
|
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Schubert J, Hubers HW, et al. Hot electron bolometric mixers based on NbN films deposited on MgO substrates. In: Inst. Phys. Conf. Ser. Vol 167. Barcelona, Spain; 1999. p. 687–90.
|
|
|
Yagoubov P, Kroug M, Merkel H, Kollberg E, Schubert J, Hubers H-W, et al. Performance of NbN phonon-cooled hot-electron bolometric mixer at Terahertz frequencies. In: Proc. 6-th Int. Conf. Terahertz Electron.; 1998. p. 149–52.
Abstract: The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The results of the DSB noire temperature are: 1300 K at 650 GHz, 4700 K at 2.5 TBz and 10000 K at 3.12 THz. The RF bandwidth of the receiver is at least 2.5 THz. The amount of LO power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain is measured to be -9 dB, the total conversion gain -14 dB.
|
|