Il'in KS, Lindgren M, Currie MA, Semenov D, Gol'tsman GN, Sobolewski R, et al. Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl Phys Lett. 2000;76(19):2752–4.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
Shurakov A, Tong C-yu E, Grimes P, Blundell R, Golt'sman G. A microwave reflection readout scheme for hot electron bolometric direct detector. IEEE Trans THz Sci Technol. 2015;5:81–4.
Abstract: In this paper, we propose and present data from a fast THz detector based on the repurpose of hot electron bolometer mixers (HEB) fabricated from superconducting NbN thinfilm. This detector is essentially a traditional NbN bolometer element that operates under the influence of a microwave pump. The in-jected microwave power serves the dual purpose of enhancing the detector sensitivity and reading out the impedance changes of the device in response to incidentTHz radiation. We have measured an optical Noise Equivalent Power of 4 pW/ Hz for our detector at a bath temperature of 4.2 K. The measurement frequency was 0.83 THz and the modulation frequency was 1.48 kHz. The readout
scheme is versatile and facilitates both high-speed operation as well as multi-pixel applications.
|
Marsili F, Bitauld D, Divochiy A, Gaggero A, Leoni R, Mattioli F, et al. Superconducting nanowire photon number resolving detector at telecom wavelength. In: CLEO/QELS. Optical Society of America; 2008. Qmj1 (1 to 2).
Abstract: We demonstrate a photon-number-resolving (PNR) detector, based on parallel superconducting nanowires, capable of resolving up to 5 photons in the telecommunication wavelength range, with sensitivity and speed far exceeding existing approaches.
|
Minaeva O, Fraine A, Korneev A, Divochiy A, Goltsman G, Sergienko A. High resolution optical time-domain reflectometry using superconducting single-photon detectors. In: Frontiers in Opt. 2012/Laser Sci. XXVIII. Optical Society of America; 2012. Fw3a.39.
Abstract: We discuss the advantages and limitations of single-photon optical time-domain reflectometry with superconducting single-photon detectors. The higher two-point resolution can be achieved due to superior timing performance of SSPDs in comparison with InGaAs APDs.
|
Korneeva Y, Florya I, Vdovichev S, Moshkova M, Simonov N, Kaurova N, et al. Comparison of hot-spot formation in NbN and MoN thin superconducting films after photon absorption. In: IEEE Transactions on Applied Superconductivity. Vol 27.; 2017. 5.
Abstract: In superconducting single-photon detectors SSPD
the efficiency of local suppression of superconductivity and hotspot
formation is controlled by diffusivity and electron-phonon
interaction time. Here we selected a material, 3.6-nm-thick MoNx
film, which features diffusivity close to those of NbN traditionally
used for SSPD fabrication, but with electron-phonon interaction
time an order of magnitude larger. In MoNx detectors we study
the dependence of detection efficiency on bias current, photon
energy, and strip width and compare it with NbN SSPD. We
observe non-linear current-energy dependence in MoNx SSPD
and more pronounced plateaus in dependences of detection
efficiency on bias current which we attribute to longer electronphonon
interaction time.
|