Ekstörm H, Kollberg E, Yagoubov P, Gol'tsman G, Gershenzon E, Yngvesson S. Gain and noise bandwidth of NbN hot-electron bolometric mixers. Appl Phys Lett. 1997;70(24):3296–8.
Abstract: We have measured the noise performance and gain bandwidth of 35 Å thin NbN hot-electron mixers integrated with spiral antennas on silicon substrate lenses at 620 GHz. The best double-sideband receiver noise temperature is less than 1300 K with a 3 dB bandwidth of ≈5 GHz. The gain bandwidth is 3.2 GHz. The mixer output noise dominated by thermal fluctuations is 50 K, and the intrinsic conversion gain is about −12 dB. Without mismatch losses and excluding the loss from the beamsplitter, we expect to achieve a receiver noise temperature of less than 700 K.
|
Kawamura J, Blundell R, Tong C-yu E, Gol’tsman G, Gershenzon E, Voronov B, et al. Low noise NbN lattice-cooled superconducting hot-electron bolometric mixers at submillimeter wavelengths. Appl Phys Lett. 1997;70(12):1619–21.
Abstract: Lattice-cooled superconducting hot-electron bolometric mixers are used in a submillimeter-wave waveguide heterodyne receiver. The mixer elements are niobium nitride film with 3.5 nm thickness and ∼10 μm2 area. The local oscillator power for optimal performance is estimated to be 0.5 μW, and the instantaneous bandwidth is 2.2 GHz. At an intermediate frequency centered at 1.4 GHz with 200 MHz bandwidth, the double sideband receiver noise temperature is 410 K at 430 GHz. The receiver has been used to detect molecular line emission in a laboratory gas cell.
|
Kroug M, Yagoubov P, Gol'tsman G, Kollberg E. NbN quasioptical phonon cooled hot electron bolometric mixers at THz frequencies. In: Inst. Phys. Conf. Ser. Vol 1. Bristol; 1997. p. 405–8.
|
Tong CYE, Chen L, Blundell R. Theory of distributed mixing and amplification in a superconductingquasi-particle nonlinear transmission line. IEEE Trans. Microw. Theory Techn.. 1997;45(7):1086–92.
|
Cherednichenko S, Yagoubov P, Il'In K, Gol'tsman G, Gershenzon E. Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In: Proc. 8th Int. Symp. Space Terahertz Technol.; 1997. p. 245–57.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|