Abstract: Picosecond nonequilibrium and slow bolometric responses to infrared radiation from a patterned high-T c superconducting (HTS) film in resistive and normal states deposited onto LaAlO3, NdGaO3, and MgO substrates were investigated using both pulse and modulation techniques. The response time of 35 ps to a laser pulse of 17 ps FWHM has been observed. The intrinsic response time of the fast process is expected to be about a few picoseconds. The modulation technique, being free from the disadvantages of pulse methods (poor sensitivity, limited dynamic range), makes the detailed study of a number of relaxation processes possible. Besides the nonequilibrium response, two kinds of bolometric processes, namely phonon transport through the film-substrate interface and phonon thermal diffusion in a substrate, manifest themselves in certain frequency dependences.

Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.

Abstract: Nonequilibrium picosecond and bolometric responses of YBCO films 500 angstroms thick patterned into 20 X 20 micrometers ² size structure to 17 ps laser pulses and modulated radiation of GaAs and CO₂ lasers have been studied. The modulation frequencies up to 10 GHz for GaAs laser and up to 1 GHz for CO₂ were attained. The use of small radiation power (1 – 10 mW/cm² for cw radiation and 10 – 100 nJ/cm² for pulse radiation) in combination with high sensitive read-out system made possible to avoid any non-linear transient processes caused by an overheating of sample above a critical temperature or S-N switching enhanced by an intense radiation. Responses due to the change of kinetic inductance were believed to be negligible. The only signals observed were caused by a small change of the film resistance either in the resistive state created by a bias current or in the normal state. The data obtained by means of pulse and modulation techniques are in agreement. The responsivity about 1 V/W was measured at 1 GHz modulation frequency both for 0.85 micrometers and 10.6 micrometers wavelengths. The sensitivity of high-T_c fast wideband infrared detector is discussed.