Goltsman G, Korneev A, Minaeva O, Rubtsova I, Chulkova G, Milostnaya I, et al. Advanced nanostructured optical NbN single-photon detector operated at 2.0 K. In: Razeghi M, Brown GJ, editors. Proc. SPIE. Vol 5732. Spie; 2005. p. 520–9.
Abstract: We present our studies on quantum efficiency (QE), dark counts, and noise equivalent power (NEP) of the latest generation of nanostructured NbN superconducting single-photon detectors (SSPDs) operated at 2.0 K. Our SSPDs are based on 4 nm-thick NbN films, patterned by electron beam lithography as highly-uniform 100÷120-nm-wide meander-shaped stripes, covering the total area of 10x10 μm2 with the meander filling factor of 0.7. Advances in the fabrication process and low-temperature operation lead to QE as high as 30-40% for visible-light photons (0.56 μm wavelength)-the saturation value, limited by optical absorption of the NbN film. For 1.55 μm photons, QE was 20% and decreased exponentially with the wavelength reaching 0.02% at the 5-μm wavelength. Being operated at 2.0-K temperature the SSPDs revealed an exponential decrease of the dark count rate, what along with the high QE, resulted in the NEP as low as 5x10-21 W/Hz-1/2, the lowest value ever reported for near-infrared optical detectors. The SSPD counting rate was measured to be above 1 GHz with the pulse-to-pulse jitter below 20 ps. Our nanostructured NbN SSPDs operated at 2.0 K significantly outperform their semiconducting counterparts and find practical applications ranging from noninvasive testing of CMOS VLSI integrated circuits to ultrafast quantum communications and quantum cryptography.
|
Sobolewski R, Verevkin A, Gol’tsman GN. Superconducting optical single-photon detectors. In: CLEO/QELS. Optical Society of America; 2004. IThD1.
Abstract: We review the development of superconducting single-photon detectors. The devices are characterized by experimental quantum efficiency of ~8% for infrared photons, counting rate ~2 GHz, 18 ps jitter, and <0.01 per second dark counts.
|
Ryabchun S, Korneev A, Matvienko V, Smirnov K, Kouminov P, Seleznev V, et al. Superconducting single photon detectors array based on hot electron phenomena. In: Proc. 15th Int. Symp. Space Terahertz Technol.; 2004. p. 242–7.
Abstract: In this paper we propose to use time domain multiplexing for large format arrays of superconducting single photon detectors (SSPDs) of the terahertz, visible and infrared frequency ranges based on ultrathin superconducting NbN films. Effective realization of time domain multiplexing for SSPD arrays is possible due to a short electric pulse of the SSPD as response to radiation quantum absorption, picosecond jitter and extremely low noise equivalent power (NEP). We present experimental results of testing 2×2 arrays in the infrared waveband. The measured noise equivalent power in the infrared and expected for the terahertz waveband is 10 – 21 WHz -1/2 . The best quantum efficiency (QE) of SSPD is 50% at 1.3 µm wavelength.
|
Rubtsova I, Korneev A, Matvienko V, Chulkova G, Milostnaya I, Goltsman G, et al. Spectral sensitivity, quantum efficiency, and noise equivalent power of NbN superconducting single-photon detectors in the IR range. In: Proc. 29th IRMMW / 12th THz.; 2004. p. 461–2.
Abstract: We have developed nanostructured NbN superconducting single-photon detectors capable of GHz-rate photon counting in the 0.4 to 5 /spl mu/m wavelength range. Quantum efficiency of 30%, dark count rate 3/spl times/10/sup -4/ s/sup -1/, and NEP=10/sup -20/ W/Hz/sup -1/2/ have been measured at the 1.3-/spl mu/m wavelength for the device operating at 2.0 K.
|
Zhang J, Pearlman A, Slysz W, Verevkin A, Sobolewski R, Wilsher K, et al. A superconducting single-photon detector for CMOS IC probing. In: Proc. 16-th LEOS. Vol 2.; 2003. p. 602–3.
Abstract: In this paper, a novel, time-resolved, NbN-based, superconducting single-photon detector (SSPD) has been developed for probing CMOS integrated circuits (ICs) using photon emission timing analysis (PETA).
|