Gershenzon EM, Gol’tsman GN, Dzardanov AL, Zorin MA. Ultrafast superconductive switch. IEEE Trans Magn. 1991;27(2):2844–6.
Abstract: The transition from superconductive to resistive state caused by infrared radiation and bias current pulses was investigated in order to minimize switching time tau and driving power W. Experimental results for Nb microstrips confirm the correctness of calculations based on the model of electron heating. For Nb switches, tau measured directly is 0.3-0.8 ns for radiation pulses and 1-3 ns for bias current pulses at T=4.2 K, while for YBaCuO switches at T=77 K it is expected to be several picoseconds. For an YBaCuO sample with the dimensions of 5*2*0.15 mu m/sup 2/, W was 10 mW, and it can be further reduced to the order of several microwatts by decreasing the volume of the sample.
|
Gol'tsman GN, Semenov AD, Gousev YP, Zorin MA, Gogidze IG, Gershenzon EM, et al. Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond Sci Technol. 1991;4(9):453–6.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
Voronov BM, Gershenzon EM, Gol'tsman GN, Gogidze IG, Gusev YP, Zorin MA, et al. Picosecond range detector base on superconducting niobium nitride film sensitive to radiation in spectral range from millimeter waves up to visible light. Sverkhprovodimost': Fizika, Khimiya, Tekhnika. 1992;5(5):955–60.
Abstract: Fast-operating picosecond detector of electromagnetical radiation is developed on the basis of fine superconducting film of niobium nitride with high sensitivity within spectral range from millimetric waves up to visible light. Detector sensitive element represents structure covering narrow parallel strips with micron sizes included in the rupture of microstrip line. Detecting ability of the detector and time constant measured using amplitude-simulated radiation of reverse wave tubes and pulse radiation of picosecond gas and solid-body lasers, constitute D*≅1010 W-1·cm·Hz-1/2 and τ≤5 ps respectively, at 10 K temperature. The expected value of time constant of the detector at 10 K obtained via extrapolation of directly measured dependence that is, τ ∝ τ-1, constitutes 20 ps. Experimental data demonstrate that detection mechanism is linked with electron heating effect.
|
Zorin M, Milostnaya I, Gol'tsman GN, Gershenzon EM. Fast NbN superconducting switch controlled by optical radiation. IEEE Trans Appl Supercond. 1997;7(2):3734–7.
Abstract: The switching time and the optical control power of the NbN superconducting switch have been measured. The device is based on the ultrathin film 5-8 nm thick patterned as a structure of several narrow parallel strips (/spl sim/1 /spl mu/m wide) connected to wide current leads. The current-voltage characteristic of the switch at temperature 4.2 K demonstrated a hysteresis due to DC current self-heating. We studied the superconducting-to-resistive state transition induced by both optical and bias-current excitations. The optical pulse duration was /spl sim/20 ps and the rise time of the current step was determined to be less than 50 ps. The optical pulse was delivered to the switch by the semiconductor laser through an optical fiber. We found that the measured switching time is less than the duration of the optical excitation. The threshold optical power density does not exceed 3/spl middot/10/sup 3/ W/cm/sup 2/. The proposed device can be used in the fiber input of LTS rapid single flux quantum circuits.
|
Danerud M, Winkler D, Lindgren M, Zorin M, Trifonov V, Karasik B, et al. A fast infrared detector based on patterned YBCO thin film. Supercond Sci Technol. 1994;7(5):321–3.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|