Seleznev VA, Tarkhov MA, Voronov BM, Milostnaya II, Lyakhno VY, Garbuz AS, et al. Deposition and characterization of few-nanometers-thick superconducting Mo-Re films. Supercond Sci Technol. 2008;21(11):115006 (1 to 6).
Abstract: We report on the fabrication and investigation of few-nanometers-thick superconducting molybdenum-rhenium (Mo-Re) films intended for use in nanowire single-photon superconducting detectors (SSPDs). Mo-Re films were deposited on sapphire substrates by DC magnetron sputtering of an Mo(60)-Re(40) alloy target in an atmosphere of argon. The films 2-10 nm thick had critical temperatures (Tc) from 5.6 to 9.7 K. HRTEM (high-resolution transmission electron microscopy) analysis showed that the films had a homogeneous structure. XPS (x-ray photoelectron spectroscopy) analysis showed the Mo to Re atom ratio to be 0.575/0.425, oxygen concentration to be 10%, and concentration of other elements to be 1%.
|
|
|
|
Korneeva YP, Manova NN, Florya IN, Mikhailov MY, Dobrovolskiy OV, Korneev AA, et al. Different single-photon response of wide and narrow superconducting MoxSi1−x strips. Phys Rev Applied. 2020;13(2):024011 (1 to 7).
Abstract: The photon count rate (PCR) of superconducting single-photon detectors made of MoxSi1−x films shaped as a 2-μm-wide strip and a 115-nm-wide meander strip line is studied experimentally as a function of the dc biasing current at different values of the perpendicular magnetic field. For the wide strip, a crossover current Icross is observed, below which the PCR increases with an increasing magnetic field and above which it decreases. This behavior contrasts with the narrow MoxSi1−x meander, for which no crossover current is observed, thus suggesting different photon-detection mechanisms in the wide and narrow strips. Namely, we argue that in the wide strip the absorbed photon destroys superconductivity locally via the vortex-antivortex mechanism for the emergence of resistance, while in the narrow meander superconductivity is destroyed across the whole strip line, forming a hot belt. Accordingly, the different photon-detection mechanisms associated with vortices and the hot belt determine the qualitative difference in the dependence of the PCR on the magnetic field.
|
|
|
|
Korneeva Y, Vodolazov D, Florya I, Manova N, Smirnov E, Korneev A, et al. Single photon detection in micron scale NbN and α-MoSi superconducting strips. In: EPJ Web Conf. Vol 190.; 2018. 04010 (1 to 2).
Abstract: We experimentally demonstrate the single photon detection in straight micrometer-wide NbN and α-MoSi bridges. Width of the bridges is 2 µm, while the wavelength of the photon changes from 408 to 1550 nm and critical current exceeds 50% of the depairing current. Obtained results offer the alternative route for design of detectors without resonator and meander structure and indirectly confirm vortex assisted mechanism of single photon detection.
|
|
|
|
Korneev AA, Korneeva YP, Mikhailov MY, Pershin YP, Semenov AV, Vodolazov DY, et al. Characterization of MoSi superconducting single-photon detectors in the magnetic field. IEEE Trans Appl Supercond. 2015;25(3):2200504 (1 to 4).
Abstract: We investigate the response mechanism of nanowire superconducting single-photon detectors (SSPDs) made of amorphous MoxSi1-x. We study the dependence of photon count and dark count rates on bias current in magnetic fields up to 113 mT at 1.7 K temperature. The observed behavior of photon counts is similar to the one recently observed in NbN SSPDs. Our results show that the detecting mechanism of relatively high-energy photons does not involve the vortex penetration from the edges of the film, and on the contrary, the detecting mechanism of low-energy photons probably involves the vortex penetration from the film edges.
|
|
|
|
Korneeva YP, Mikhailov MY, Pershin YP, Manova NN, Divochiy AV, Vakhtomin YB, et al. Superconducting single-photon detector made of MoSi film. Supercond Sci Technol. 2014;27(9):095012.
Abstract: We fabricated and characterized nanowire superconducting single-photon detectors made of 4 nm thick amorphous Mox Si1−x films. At 1.7 K the best devices exhibit a detection efficiency (DE) up to 18% at 1.2 $\mu {\rm m}$ wavelength of unpolarized light, a characteristic response time of about 6 ns and timing jitter of 120 ps. The DE was studied in wavelength range from 650 nm to 2500 nm. At wavelengths below 1200 nm these detectors reach their maximum DE limited by photon absorption in the thin MoSi film.
|
|