Kroug M, Cherednichenko S, Merkel H, Kollberg E, Voronov B, Gol'tsman G, et al. NbN hot electron bolometric mixers for terahertz receivers. IEEE Trans Appl Supercond. 2001;11(1):962–5.
Abstract: Sensitivity and gain bandwidth measurements of phonon-cooled NbN superconducting hot-electron bolometer mixers are presented. The best receiver noise temperatures are: 700 K at 1.6 THz and 1100 K at 2.5 THz. Parylene as an antireflection coating on silicon has been investigated and used in the optics of the receiver. The dependence of the mixer gain bandwidth (GBW) on the bias voltage has been measured. Starting from low bias voltages, close to operating conditions yielding the lowest noise temperature, the GBW increases towards higher bias voltages, up to three times the initial value. The highest measured GBW is 9 GHz within the same bias range the noise temperature increases by a factor of two.
|
|
|
Hübers H-W, Semenov AD, Richter H, Schubert J, Hadjiloucas S, Bowen JW, et al. Antenna pattern of the quasi-optical hot-electron bolometric mixer at terahertz frequencies. In: Proc. 12th Int. Symp. Space Terahertz Technol. San Diego, CA, USA; 2001. p. 286–96.
|
|
|
Cherednichenko S, Kroug M, Khosropanah P, Adam A, Merkel H, Kolberg E, et al. A broadband terahertz heterodyne receiver with an NbN HEB mixer. In: Harward University, editor. Proc. 13th Int. Symp. Space Terahertz Technol. Cambridge, MA, USA; 2002. p. 85–95.
Abstract: We present a broadband and low noise heterodyne receiver for 1.4-1.7 THz designed for the Hershel Space Observatory. A phonon- cooled NbN HEB mixer was integrated with a normal metal double- slot antenna and an elliptical silicon lens. DSB receiver noise temperature Tr was measured from 1 GHz through 8GHz intermediate frequency band with 50 MHz instantaneous bandwidth. At 4.2 K bath temperature and at 1.6 THz LO frequency Tr is 800 K with the receiver noise bandwidth of 5 GHz. While at 2 K bath temperature Tr was as low as 700 K. At 0.6 THz and 1.1 THz a spiral antenna integrated NbN HEB mixer showed the receiver noise temperature 500 K and 800 K, though no antireflection coating was used in this case. Tr of 1100 K was achieved at 2.5 THz while the receiver noise bandwidth was 4 GHz.
|
|
|
Huebers H-W, Semenov A, Richter H, Birk M, Krocka M, Mair U, et al. Superconducting hot electron bolometer as mixer for far-infrared heterodyne receivers. In: Phillips TG, Zmuidzinas J, editors. Proc. SPIE. Vol 4855. Tucson, USA: SPIE; 2003. p. 395–401. (Presented at the Society of Photo-Optical Instrumentation Engineers (SPIE) Conference; vol 4855).
Abstract: Heterodyne receivers for applications in astronomy need quantum limited sensitivity. In instruments which are currently under development for SOFIA or Herschel superconducting hot electron bolometers (HEB) will be used to achieve this goal at frequencies above 1.4 THz. We present results of the development of a phonon-cooled NbN HEB mixer for GREAT, the German Receiver for Astronomy at Terahertz Frequencies, which will be flown aboard SOFIA. The mixer is a small superconducting bridge incorporated in a planar feed antenna and a hyperhemispherical lens. Mixers with logarithmic-spiral and double-slot feed antennas have been investigated with respect to their noise temperature, conversion loss, linearity and beam pattern. At 2.5 THz a double sideband noise temperature of 2200 K was achieved. The conversion loss was 17 dB. The response of the mixer was linear up to 400 K load temperature. The performance was verified by measuring an emission line of methanol at 2.5 THz. The measured linewidth is in good agreement with the linewidth deduced from pressure broadening measurements at millimeter wavelength. The results demonstrate that the NbN HEB is very well suited as a mixer for far-infrared heterodyne receivers.
|
|
|
Hajenius M, Baselmans JJA, Gao JR, Klapwijk TM, de Korte PAJ, Voronov B, et al. Improved NbN phonon cooled hot electron bolometer mixers. In: Proc. 14th Int. Symp. Space Terahertz Technol. Tucson, USA; 2003. p. 413–23.
Abstract: NbN phonon-cooled hot electron bolometer mixers (HEBs) have been realized with negligible contact resistance to Au pads. By adding either a 5 nm Nb or a 10 nm NbTiN layer between the Au and NbN, to preserve superconductivity in the NbN under the Au contact pad, superior noise temperatures have been obtained. Using DC I,V curves and resistive transitions in combination with process parameters we analyze the nature of these improved devices and determine interface transparencies.
|
|