Korneev A, Finkel M, Maslennikov S, Korneeva Y, Florya I, Tarkhov M, et al. Superconducting NbN terahertz detectors and infrared photon counters. Вестник НГУ Серия: физ. 2010;5(4):68–72.
Abstract: We present our recent achievements in the development of sensitive and ultrafast thin-film superconducting sensors: hot-electron bolometers (HEB), HEB-mixers for terahertz range and infrared single-photon counters. These sensors have already demonstrated a performance that makes them devices-of-choice for many terahertz and optical applications. Keywords: Hot electron bolometer mixers, infrared single-photon detectors, superconducting device fabrication, superconducting NbN films.
|
Kardakova A, Finkel M, Morozov D, Kovalyuk V, An P, Dunscombe C, et al. The electron-phonon relaxation time in thin superconducting titanium nitride films. Appl Phys Lett. 2013;103(25):252602 (1 to 4).
Abstract: We report on the direct measurement of the electron-phonon relaxation time, τeph, in disordered TiN films. Measured values of τeph are from 5.5 ns to 88 ns in the 4.2 to 1.7 K temperature range and consistent with a T−3 temperature dependence. The electronic density of states at the Fermi level N0 is estimated from measured material parameters. The presented results confirm that thin TiN films are promising candidate-materials for ultrasensitive superconducting detectors.
The work was supported by the Ministry of Education and Science of the Russian Federation, Contract No. 14.B25.31.0007 and by the RFBR Grant No. 13-02-91159.
|
Seleznev VA, Tarkhov MA, Voronov BM, Milostnaya II, Lyakhno VY, Garbuz AS, et al. Deposition and characterization of few-nanometers-thick superconducting Mo-Re films. Supercond Sci Technol. 2008;21(11):115006 (1 to 6).
Abstract: We report on the fabrication and investigation of few-nanometers-thick superconducting molybdenum-rhenium (Mo-Re) films intended for use in nanowire single-photon superconducting detectors (SSPDs). Mo-Re films were deposited on sapphire substrates by DC magnetron sputtering of an Mo(60)-Re(40) alloy target in an atmosphere of argon. The films 2-10 nm thick had critical temperatures (Tc) from 5.6 to 9.7 K. HRTEM (high-resolution transmission electron microscopy) analysis showed that the films had a homogeneous structure. XPS (x-ray photoelectron spectroscopy) analysis showed the Mo to Re atom ratio to be 0.575/0.425, oxygen concentration to be 10%, and concentration of other elements to be 1%.
|
Kitaygorsky J, Komissarov I, Jukna A, Minaeva O, Kaurova N, Divochiy A, et al. Fluctuations in two-dimensional superconducting NbN nanobridges and nanostructures meanders [abstract]. In: Proc. APS March Meeting. Vol 52.; 2007. L9.00013.
Abstract: We have observed fluctuations, manifested as sub-nanosecond to nanosecond transient, millivolt-amplitude voltage pulses, generated in two-dimensional NbN nanobridges, as well as in extended superconducting meander nanostructures, designed for single photon counting. Both nanobridges and nano-stripe meanders were biased at currents close to the critical current and measured in a range of temperatures from 1.5 to 8 K. During the tests, the devices were blocked from all incoming radiation by a metallic enclosure and shielded from any external magnetic fields. We attribute the observed spontaneous voltage pulses to the Kosterlitz-Thouless-type fluctuations, where the high enough applied bias current reduces the binding energy of vortex-antivortex pairs and, subsequently, thermal fluctuations break them apart causing the order parameter to momentarily reduce to zero, which in turn causes a transient voltage pulse. The duration of the voltage pulses depended on the device geometry (with the high-kinetic inductance meander structures having longer, nanosecond, pulses) while their rate was directly related to the biasing current as well as temperature.
|