Gol’tsman G, Korneev A, Tarkhov M, Seleznev V, Divochiy A, Minaeva O, et al. Middle-infrared ultrafast superconducting single photon detector. In: 32nd IRMW / 15th ICTE.; 2007. p. 115–6.
Abstract: We present the results of the research on quantum efficiency of the ultrathin-film superconducting single-photon detectors (SSPD) in the wavelength rage from 1 mum to 5.7 mum. Reduction of operation temperature to 1.6 K allowed us to measure quantum efficiency of ~1 % at 5.7 mum wavelength with the SSPD made from 4-nm-thick NbN film. In a pursuit of further performance improvement we endeavored SSPD fabricating from 4-nm-thick MoRe film as an alternative material. The MoRe film exhibited transition temperature of 7.7K, critical current density at 4.2 K temperature was 1.1times10 6 A/cm 2 , and diffusivity 1.73 cmVs. The single-photon response was observed with MoRe SSPD at 1.3 mum wavelength with quantum efficiency estimated to be 0.04%.
|
|
|
|
Elvira D, Michon A, Fain B, Patriarche G, Beaudoin G, Robert-Philip I, et al. Time-resolved spectroscopy of InAsP/InP(001) quantum dots emitting near 2 μm. Appl Phys Lett. 2010;97(13):131907 (1 to 3).
Abstract: By using superconducting single photon detectors, we perform time-resolved characterization of a small ensemble of InAsP/InP quantum dots grown by metal organic vapor phase epitaxy, emitting at wavelengths between 1.6 and 2.2 μm. We demonstrate that alloying phosphorus with InAs allows to shift the emission wavelength toward higher wavelengths, while keeping the high optical quality of these quantum dots at room temperature, with no decrease in their radiative lifetime. This work was partially supported by Russian Ministry of Science and Education: Federal State Program “Scientific and Educational Cadres of Innovative” state Contract Nos. 02.740.0228, 14.740.11.0343, 14.740.11.0269, and P931, and RFBR Project No. 09-02-12364.
|
|
|
|
Korneev A, Divochiy A, Tarkhov M, Minaeva O, Seleznev V, Kaurova N, et al. New advanced generation of superconducting NbN-nanowire single-photon detectors capable of photon number resolving. In: J. Phys.: Conf. Ser. Vol 97.; 2008. 012307 (1 to 6).
Abstract: We present our latest generation of ultrafast superconducting NbN single-photon detectors (SSPD) capable of photon-number resolving (PNR). We have developed, fabricated and tested a multi-sectional design of NbN nanowire structures. The novel SSPD structures consist of several meander sections connected in parallel, each having a resistor connected in series. The novel SSPDs combine 10 μm × 10 μm active areas with a low kinetic inductance and PNR capability. That resulted in a significantly reduced photoresponse pulse duration, allowing for GHz counting rates. The detector's response magnitude is directly proportional to the number of incident photons, which makes this feature easy to use. We present experimental data on the performances of the PNR SSPDs. The PNR SSPDs are perfectly suited for fibreless free-space telecommunications, as well as for ultrafast quantum cryptography and quantum computing.
|
|
|
|
Bell M, Kaurova N, Divochiy A, Gol'tsman G, Bird J, Sergeev A, et al. On the nature of resistive transition in disordered superconducting nanowires. IEEE Trans Appl Supercond. 2007;17(2):267–70.
Abstract: Hot-electron single-photon counters based on long superconducting nanowires are starting to become popular in optical and infrared technologies due to their ultimately high sensitivity and very high response speed. We investigate intrinsic fluctuations in long NbN nanowires in the temperature range of 4.2 K-20 K, i.e. above and below the superconducting transition. These fluctuations are responsible for fluctuation resistivity and also determine the noise in practical devices. Measurements of the fluctuation resistivity were performed at low current densities and also in external magnetic fields up to 5 T. Above the BCS critical temperature T co the resistivity is well described by the Aslamazov-Larkin (AL) theory for two-dimensional samples. Below T co the measured resistivity is in excellent agreement with the Langer-Ambegaokar-McCumber-Halperin (LAMH) theory developed for one-dimensional superconductors. Despite that our nanowires of 100 nm width are two-dimensional with respect to the coherence length, our analysis shows that at relatively low current densities the one-dimensional LAMH mechanism based on thermally induced phase slip centers dominates over the two-dimensional mechanism related to unbinding of vortex-antivortex pairs below the Berezinskii-Kosterlitz-Thouless transition.
|
|
|
|
Chulkova G, Milostnaya I, Tarkhov M, Korneev A, Minaeva O, Voronov B, et al. Superconducting single-photon nanostructured detectors for advanced optical applications. In: Proc. Symposium on Photonics Technologies for 7th Framework Program. Vol 400.; 2006.
Abstract: We present superconducting single-photon detectors (SSPDs) based on NbN thin-film nanostructures and operated at liquid helium temperatures. The SSPDs are made of ultrathin NbN films (2.5-4 nm thick, Tc= 9-11K) as meander-shaped nanowires covering the area of 10× 10 µm2. Our detectors are operated at the temperature well below the critical temperature Tc and are DC biased by a current Ib close to the meander critical current Ic. The operation principle of the detector is based on the use of the resistive region in a narrow ultra-thin superconducting stripe upon the absorption of an incident photon. The developed devices demonstrate high sensitivity and response speed in a broadband range from UV to mid-IR (up to 6 µm), making them very attractive for advanced optical technologies, which require efficient detectors of single quanta and low-density optical radiation.
|
|